Identification & Functionality
- Chemical Family
- Technologies
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
Applications & Uses
- Application Method
- Cure Method
- Surface Preparation
Steel surfaces are to be abrasive blasted with chloride free abrasive. Exterior applications to SSPC SP-10 Near White metal finish. Immersion applications to SSPC SP-5 White metal 3 to 5 mil profile. Grind flat all burrs, weld seams, radius sharp edges. Fresh blasted ferrous surfaces to be should be coated immediately with ARCOR™ 1321K to prevent oxidation of surface. For very large areas ARCOR™ EE-80 can be used as a pre-prime to help hold the blast.
Concrete surfaces should be degreased if oil and grease contamination is present. Degreased surface shall be high pressure washed, acid etched and high pressure washed again so surface is clean and free of all grease, oils and surface laitance. Existing coatings should be abrasive blasted to clean concrete. Prime with ARCOR™ 1321K.
- Mixing
Thoroughly mix Activator into Base with mixing stick or drill with low speed mixing blade scraping sides and bottom of container or mixing board. Mix by Volume 2 parts Base to 1 part Activator. Or by weight 100 grams base to 36 grams activator. Mix thoroughly to produce an even colored and streak-free material.
- Thinning
- Not Advised; but if necessary add 5% by volume(6oz/gal.) Acetone or MEK to extend pot-life and/or thin for cold weather application.
- Application
Brush: medium to stiff bristle of sufficient quality that bristles do not pull out and stick in coating. Trim or tape to <1” nap.
Ideal for exterior applications to resist exposure to Salt Water; Caustics, Alcohols, Acids. Also suitable for immersion service in water (brakish, salt) and Caustics. Excellent for Secondary Containment’s.
Roller: good quality 3/8” nap.
Plural Spray: 0.031-0.035 tip, 2,200-3,500 PSI, Heat to 130ºF Base, 100ºF Activator. 30 mesh screens. Heated hose @ 140ºF
Airless Spray: 0.031-0.039 tip, 4,000-4,500 PSI(45:1). Add 6-oz/gal of MEK or Acetone.(Caution: Short Pot-Life)
Conventional Spray: Not Recommended.
All spray equipment should employ traps to prevent water and oil from contaminating coating and screens to prevent particulate contamination.- Application Temperature
- Keep between 55 to 95ºF(17 to 35ºC). Substrate: Keep between 45 to 105ºF(7 to 40ºC). The difference in temperature of the substrate and the material should never exceed 10ºF(5ºC). Substrate shall be a minimum of 5ºF(3ºC) above dew point. Do not apply if relative humidity exceeds 90%. If necessary heat metal prior to surface preparation using electric heater or heat lamp. Never use gas, oil or kerosene heaters as they will leave a greasy residue on metal surface. For best results keep all material in warm area overnight(75ºF+, 24ºC) for ease of mixing. If necessary Base component of material can be heated by microwave for 30 seconds for a 1 MK Base unit or by warm water bath. Heat activator by warm water bath only. If necessary let material cool before application.
- Overcoat / Cure Time
By brush, roller or squeegee recoat while material is still soft, but tack-free, between 1-12 hours at 77ºF(25ºC). If overcoat window is exceeded abrade surface with course sandpaper, grinder or brush blast. By spray application a single coat to 20 milsis recommended. For multiple coats, recoat between 1-12 hours at 72ºF. Full cure before chemical immersion 72 hours at 72ºF. Add 12 hours additional cure time for each 10ºF below 72ºF. Subtract 12 hours of cure time for each 10ºF above 72ºF. Force Cure with heat for best performance for 4 hours at 150ºF(66ºC), 12 hours at 100ºF( 38ºC).
- Clean Up
Clean tools immediately after use with M.E.K. or similar. Isopropyl Alcohol can be used in solvent restricted areas.
Properties
- Temperature Properties
- Specifications
- Chemical Resistance
Water Excellent Alkalis Excellent Inorganic Acids Good Organic Acids Good Organic Solvents Good - Film Thickness
Can be applied up to 20 mils in a single coat. Single coat spray application. Hand application may require a 2nd coat.
- Flexibility
Very Good Excellent with Polyester Cloth; 1.5 oz/ft2 (.5 KG/M2)
- Mix Ratio
2:1 by Volume (Base:Activator) 100 gm: 36 gm by weight
| Value | Units | Test Method / Conditions | |
| Maximum Temperature for Immersion Service | 63.0 | °C | - |
| Temperature Spike Tolerance for Immersion Service (3hrs) | 93.0 | °C | - |
| Maximum Temperature for Dry Heat | 163.0 | °C | - |
| Value | Units | Test Method / Conditions | |
| Solid Content | 100.0 | % Volume | - |
| Viscosity | 10,000-18,000 | cps | - |
| Pot Life (at 72°F) | 35.0 | min/kg | - |
| Coverage (at 20 mils) | 80.0 | ft² / gal / coat | - |
Packaging & Availability
- Weight per Gallon
11.6 lbs (5.27 KG), 231 cu.in.)
Storage & Handling
- Shelf Life
- 5 Years (at 13-35ºC)