Packaging Coatings

VINNAPAS® B 100/20 VLE is an approximately 50% solution of a vinyl acetate/vinyl laurate copolymer in ethyl acetate. VINNAPAS® B 100/20 VLE can be diluted with esters, ketones, aromatic solvents, and chlorinated hydrocarbons. The solution's compatibility with alcohol is limited. VINNAPAS® B 100/20 VLE is not compatible with aliphatic compounds.

VINNAPAS® SAF 608 is a water-based dispersion containing a fine-particle-sized copolymer of styrene and acrylic acid ester. It has a solid content of 50%. This product is manufactured without the inclusion of coalescents, organic solvents, plasticizers, or compounds containing alkyl phenol ethoxylate (APEO). It exhibits excellent penetration into porous substrates and offers great flexibility.

VINNOL® H 15/42 is a copolymer consisting of approximately 86 wt.% vinyl chloride (VC) and 14 wt.% vinyl acetate (VAc). Its primary application is as a binder in surface coating compounds and printing inks. This thermoplastic and physically drying binder undergoes film formation as the solvent present in the formulation evaporates.

WACKER® Silicate TES 40 WN is an ethyl silicate polymer. It is a low-viscosity liquid that provides approximately 41% of silicon dioxide (silica) upon complete hydrolysis. WACKER® Silicate TES 40 WN is used for the precipitation of polymeric SiO2 structures (silica) upon complete hydrolysis, with ethanol being produced as a by-product.

VINNOL® H 40/43 is a copolymer composed of approximately 66 wt.% vinyl chloride (VC) and approximately 34 wt.% vinyl acetate (VAc). Its primary application is as a binder for surface coating compounds and printing inks. This thermoplastic binder undergoes physical drying, resulting in the formation of a film once the solvent in the formulation has evaporated.

VINNOL® H 40/60 is a copolymer composed of approximately 61 wt.% vinyl chloride (VC) and approximately 39 wt.% vinyl acetate (VAc). Primarily, it serves as a binder for surface coating compounds and printing inks. As a thermoplastic binder, VINNOL® H 40/60 undergoes physical drying, resulting in the formation of a film as the solvent in the formulation evaporates.

VINNOL® H 40/50 is a copolymer composed of approximately 63 wt.% vinyl chloride (VC) and approximately 37 wt.% vinyl acetate (VAc). Its primary application is as a binder for surface coating compounds and printing inks. This thermoplastic binder undergoes physical drying, resulting in the formation of a film as the solvent within the formulation evaporates.

VINNOL® H 40/55 is a copolymer comprising approximately 62 wt.% vinyl chloride (VC) and approximately 38 wt.% vinyl acetate (VAc). Its primary application lies in serving as a binder for surface coating compounds and printing inks. Functioning as a thermoplastic, physically drying binder, VINNOL® H 40/55 undergoes film formation once the solvent present in the formulation has evaporated.

HDK® H15 is a synthetic, hydrophobic, amorphous silica produced via flame hydrolysis. It is a white colloidal powder of high purity. HDK® H15 is commonly utilized as a thickening and thixotropic agent in coatings, printing inks, adhesives, cosmetics, and other applications. Additionally, it serves as a reinforcing filler in elastomers, particularly silicone elastomers. Moreover, HDK® H15 functions as a free flow additive in the production of technical powders.

HDK® N20 is a synthetic, hydrophilic, amorphous silica produced through flame hydrolysis. It is a standard product widely used in various industrial applications. This white colloidal powder offers high purity and serves multiple purposes. One of the primary applications of HDK® N20 is as a thickening and thixotropic agent in organic systems such as unsaturated polyesters, coatings, printing inks, adhesives, and cosmetics. Additionally, it functions as a reinforcing filler in elastomers, particularly silicone elastomers.

HDK® H13L is a synthetic, hydrophobic, amorphous silica produced via flame hydrolysis. It is a white colloidal powder of high purity. HDK® H13L is primarily used as a thickening, thixotropic, and anti-sedimentation agent in various applications such as coatings, printing inks, adhesives, and others. It finds its main application in polar systems. The strong hydrophobicity of HDK® H13L makes it particularly suitable for solvent-free systems, high solids formulations, and waterborne coatings.

DIACRON™ FC-3294 is a polyester resin with excellent solvent solubility and is optimal as a binder for paints and inks. It exhibits excellent adhesion to plastic films, moldings and metals such as aluminum, copper, and iron. It improves hardness, heat resistance, toughness, and solvent resistance by using curing agents such as isocyanates and epoxy resins.   Features: Excellent pigment dispersion. Can be used with cross-linking agents. Excellent chemical and weather resistance   Benefits: Solvent solubility High solid differentiation Durability   Applications: For various types of inks (Screen printing and inkjet, etc. )               PCM coatings      Solventless & High Solids Coating     *DIACRON™ is provided by Mitsubishi Chemical Corporation, a member of the Mitsubishi Chemical Group.