Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Physico-Chemical Properties
- Fire Resistance
| Value | Units | Test Method / Conditions | |
| Tensile Strength | 15 | MPa | ASTM D3182 |
| Charpy Notched Impact Strength (at 23°C) | 20 | kJ/m2 | ISO 179-1/1eA |
| Hardness | 71 | Shore D | ISO 7619-1 |
| Hardness | 71 | Shore D | ISO 868 |
| Charpy Unnotched Impact Strength (at 23°C) | NB | kJ/m2 | ISO 179-1/1eU |
| Yield stress | 21 | MPa | ISO 527 |
| Strain at break | 25 | % | ISO 527 |
| Elongation at Break | 25 | % | ISO 527-2/1A |
| Flexural modulus, 23° | 2700 | MPa | ISO 178 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Izod Notched Impact Strength | 16 | kJ/m2 | ISO 180/1A |
| Charpy impact strength (+23°) | N | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (+23°) | 20 | kJ/m2 | ISO 179/1eA |
| Stress at Break | 15 | MPa | ISO 527-2/1A |
| Stress at Yield Point | 21 | MPa | ISO 527-2/1A |
| Value | Units | Test Method / Conditions | |
| Melt Volume Flow Rate - MVR (230°C/2.16 kg) | 10 | cm3/10 min | ISO 1133 |
| Density | 1100 | kg/m3 | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Temperature of deflection under load (1.80 Mpa) | 70 | °C | ISO 75-1/-2 |
| Melting temperature (10°C/min) | 167 | °C | ISO 11357-1/-3 |
| Heat Deflection Temperature | 70 | °C | ISO 75-2/Af |
| Melting Point | 165/168 | °C | ISO 11357-3 |
| Vicat softening temperature | 150 | °C | ISO 306 |
| Vicat Softening Point | 150 | °C | ISO 306/A50 |
| Value | Units | Test Method / Conditions | |
| CTI | min. 600 | V | CEI 60112 |
| Value | Units | Test Method / Conditions | |
| Density | 1.1 | g/cm3 | ISO 1183-1 |
| MVI (at 230°C-2.16Kg) | 10 | cm3/10min | ISO 1133-1 |
| Value | Units | Test Method / Conditions | |
| Falling Ball Test | 126 | °C | CEI 60695-10-2 |
Technical Details & Test Data
- Note
- The LOI measures are obtained through standard specimens of type I, with ignition of type A.
- The values indicated above have been realized with standard specimens which are conditionned according to ISO 291. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties.