Aegis® PIR-H100MP resin from AdvanSix contains 100% post-industrial recycled (PIR) raw materials while providing the same top performance and processability as Aegis® H100MP, its standard, non-recycled counterpart.
Aegis® PIR-H100MP resin is a lubricated, nucleated, medium-viscosity nylon 6 extrusion grade homopolymer for cast or blown film applications. It features a combination of strength, toughness, and thermoforming properties along with excellent heat, chemical and abrasion resistance.
Ask AdvanSix Questions
Ask the Supplier
Popular AdvanSix Products
View All AdvanSix ProductsKnowde Enhanced TDS
Identification & Functionality
Aegis® PIR-H100MP Features & Benefits
Applications & Uses
Aegis® PIR-H100MP is a lubricated and nucleated medium viscosity nylon 6 extrusion grade homopolymer for cast or blown film applications
Properties
| Value | Units | Test Method / Conditions | |
| Melting Point | 220 (428) | °C (°F) | ASTM D-3418 |
| Value | Units | Test Method / Conditions | |
| Density | 1.13 | g/cm³ | ASTM D-792 |
| Extractable Content | max. 0.8 | % | SOP-702-307 |
| Melt Flow Rate (at 235°C/1.0 kg or 455°F/1.0 kg) | 2.6 | g/10 min | ASTM D-1238 |
| RV (at 96% Sulfuric Acid) | 3.35 | - | - |
| Viscosity (FAV) | 100 | - | ASTM D-789 |
| Value | Units | Test Method / Conditions | |
| Flexural Modulus - MD* (at 73°F (22.7°C) | 2650 | MPa | ASTM D-790 |
| Flexural Modulus - MD* (at 73°F (22.7°C) | 110 | MPa | ASTM D-790 |
| Heat Deflection Temperature - MD* (at 73°F ( 23°C)) | 61 (142) | ºC (ºF) | ASTM D-648 |
| Notched Izod - MD* (at 73°F (23°C)) | 60 | J/m | ASTM D-256 |
| Tensile Modulus - MD* (at 73°F (23°C)) | 3240 | MPa | ASTM D-882 |
| Tensile Strength - MD* (at 73°F (23°C)) | 80 | MPa | ASTM D-882 |
| Yield Elongation - MD* (at 73°F (23°C), 0% RH) | 3.8 | % | ASTM D-882 |
| Value | Units | Test Method / Conditions | |
| Elmendorf Tear Strength - MD* (at 23°C (73°F)) | 880 | N | ASTM D-1922 |
| Elmendorf Tear Strength - TD* (at 23°C (73°F)) | 950 | N | ASTM D-1004 |
| Elongation - MD* (at 23°C (73°F)) | 340 | % | ASTM D-882 |
| Elongation - TD* (at 23°C (73°F)) | 340 | % | ASTM D-882 |
| Graves Tear - MD* (at 73°F (23°C)) | 2140 | N | ASTM D-1004 |
| Graves Tear - TD* (at 73°F (23°C)) | 2070 | N | ASTM D-882 |
| Puncture Index - MD*(at 73°F (23°C)) | 470 | gm/mil | ASTM D-5478 |
| Puncture Strength - MD* (at 73°F (23°C)) | 960 | grams | ASTM D-5478 |
| Tensile Modulus - MD* (at 73°F (23°C)) | 700 | MPa | ASTM D-882 |
| Tensile Modulus - TD* (at 73°F (23°C)) | 590 | MPa | ASTM D-5478 |
| Tensile Strength - MD* (at 73°F (23°C)) | 90 | MPa | ASTM D-882 |
| Tensile Strength - TD* (at 73°F (23°C)) | 80 | MPa | ASTM D-882 |
| Tensile Yield - MD* (at 73°F (22.7°C), 50% RH) | 30 | MPa | ASTM D-882 |
| Tensile Yield (at 73°F (22.7°C), 50% RH) | 30 | MPa | ASTM D-882 |
| Value | Units | Test Method / Conditions | |
| Carbon Dioxide Permeability (at 23°C (73°F), 0% RH) | 72.8 | cc/m²/day | - |
| Nitrogen Permeability (at 73°F (23°C), 0% RH) | 14 | cc/m²/day | - |
| Oxygen Permeability (at 73°F (23°C), 0% RH) | 40.3 | cc/m²/day | D-3958 |
| Water Vapor Permeability (at 100°F (38°C), 100% RH ) | 992 | gm-mil/m²/day | F-1249 |
| Value | Units | Test Method / Conditions | |
| Moisture (24 Hour) | 1.6 | % | ASTM D-570 |
| Moisture (50% RH) | 2.7 | % | ASTM D-570 |
| Moisture (Saturation) | 9.5 | % | ASTM D-570 |
| Moisture Content | max. 0.08 | % | ASTM D-6869 |
Aegis® PIR-H100MP conforms to FDA requirements of 21 CFR 177.1500 as well as EU Directive 2011/10/EC. Aegis® PIR-H100MP homopolymer possesses the combination of strength, toughness and thermoforming properties associated with nylon 6 as well as excellent heat, chemical and abrasion resistance.
*Note: MD = Machine Direction and TD = Traverse Direction. Test samples obtained from 2-mil thick unoriented cast film.
Processing conditions for test specimens: melt temperature = 240ºC (464ºF); mold temperature = 80ºC (176ºF).
Regulatory & Compliance
Technical Details & Test Data
Melt Viscosity vs. Temperature
Melt Temperature: 220°C (428°F)
Melt Temperature Range: 232°C (450°F) to 271°C (520°F).
Two key factors affect the melt viscosity (stiffness or fluidity of the melt) :
1. The molecular weight (Mw) of the resin: Higher Mw resins will have a higher melt viscosity than lower Mw resins.
2. Temperature of the melt for any given Mw resin: Higher process temperatures will provide a more fluid melt viscosity
than lower process temperatures.
Typical Barrel Profile for Cast Films
Barrel: 230-260°C (446-500°F)
Adapter: 260-266°C (500-510°F)
Die: 260°C (500°F)
Process Melt Temperature: 260-270°C (500-518°F)
Typical Barrel Profile for Tubular (Blown) Films
Barrel: 246-254°C (474-490°F)
Adapter: 260°C (500°F)
Die: 254°C (490°F)
Process Melt Temperature: 254-260°C (490-500°F)
Screw Parameters
Metering Section: 40%
Transition Section: 3 to 4 flights
Feed Section: Balance of screw length
Compression Ratio: 3.5:1 to 4.0:1
L/D Ratio: 24:1
Metering Section Flight Depth
| Screw Diameter | Recommended Depth |
| 1" | 0.055" |
| 1.5" | 0.060" |
| 2" | 0.070" |
| 2.5" | 0.080" |
| 3.5" | 0.100" |
| 4.5" | 0.115" |
| 6" | 0.135" |
Storage & Handling
Material Handling
Aegis® PIR-H100MP is supplied in sealed containers and drying prior to processing is not required. However, higher moisture is the primary cause of processing issues. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80°C (176°F) is recommended. Drying time is dependent on moisture level. More information about safe handling procedures can be obtained by requesting the Safety Data Sheet.