Aegis® PIR-H135MP resin from AdvanSix contains 100% post-industrial recycled (PIR) raw materials while providing the same top performance and processability as Aegis® H135MP, its standard, non-recycled counterpart.
Aegis® PIR-H135MP is a lubricated and nucleated high viscosity, nylon 6 extrusion grade homopolymer for cast or blown film. It combines strength, toughness and exceptional thermoforming properties with excellent heat, chemical and abrasion resistance.
Ask AdvanSix Questions
Ask the Supplier
Popular AdvanSix Products
View All AdvanSix ProductsKnowde Enhanced TDS
Identification & Functionality
Aegis® PIR-H135MP Features & Benefits
Applications & Uses
Properties
| Value | Units | Test Method / Conditions | |
| Melting Point | 220 (428) | °C (°F) | ASTM D-3418 |
| Value | Units | Test Method / Conditions | |
| Density | 1.13 | g/cmᵌ | ASTM D-792 |
| Extractable Content | max. 0.8 | % | SOP-702-307 |
| Melt Flow Rate (at 235°C/1.0 kg or 455°F/1.0 kg) | 1.2 | g/10 min | ASTM D-1238 |
| RV (at 96% Sulfuric Acid) | 3.75 | - | - |
| Viscosity FAV | 135 | - | ASTM D-789 |
| Value | Units | Test Method / Conditions | |
| Flexural Modulus - MD (at 73°F (23°C) | 2690 | MPa | ASTM D-790 |
| Flexural Strength - MD (at 73°F (23°C) | 100 | MPa | ASTM D-790 |
| Heat Deflection Temperature - MD (at 73°F ( 23°C)) | 57 (135) | ºC (ºF) | ASTM D-648 |
| Notched Izod Impact (at 73°F (23°C)) | 60 | J/m | ASTM D-256 |
| Tensile Modulus - MD (at 73°F (23°C)) | 3130 | MPa | ASTM D-882 |
| Tensile Strength - MD (at 73°F (23°C)) | 80 | MPa | ASTM D-882 |
| Yield Elongation - MD (at 73°F (23°C), 0% RH) | 3.7 | % | ASTM D-882 |
| Value | Units | Test Method / Conditions | |
| Elmendorf Tear Strength - MD (at 23°C (73°F)) | 840 | N | ASTM D-1922 |
| Elmendorf Tear Strength - TD (at 23°C (73°F)) | 1140 | N | ASTM D-1922 |
| Elongation - MD (at 23°C (73°F)) | 350 | % | ASTM D-882 |
| Elongation - TD (at 23°C (73°F)) | 360 | % | ASTM D-882 |
| Graves Tear - MD (at 73°F (23°C)) | 2540 | N | ASTM D-1004 |
| Graves Tear - TD (at 73°F (23°C)) | 2230 | N | ASTM D-1004 |
| Puncture Index - MD (at 73°F (23°C)) | 480 | gm/mil | ASTM D-5478 |
| Puncture Strength - MD (at 73°F (23°C)) | 940 | grams | ASTM D-5478 |
| Tensile Modulus - MD (at 73°F (23°C)) | 640 | MPa | ASTM D-882 |
| Tensile Modulus - TD (at 73°F (23°C)) | 610 | MPa | ASTM D-882 |
| Tensile Strength - MD (at 73°F (23°C)) | 100 | MPa | ASTM D-882 |
| Tensile Strength - TD (at 73°F (23°C)) | 100 | MPa | ASTM D-882 |
| Tensile Yield - MD (at 73°F (23°C)) | 30 | MPa | ASTM D-882 |
| Tensile Yield - TD (at 73°F (23°C)) | 30 | MPa | ASTM D-882 |
| Value | Units | Test Method / Conditions | |
| Carbon Dioxide Permeability (at 23°C (73°F), 0% RH) | 72.8 | cc/m²/day | - |
| Nitrogen Permeability (at 73°F (23°C), 0% RH) | 14 | cc/m²/day | - |
| Oxygen Permeability (at 73°F (23°C), 0% RH) | 40.3 | cc/m²/day | D-3958 |
| Water Vapor Permeability (at 100°F (38°C), 100% RH ) | 992 | gm-mil/m²/day | F-1249 |
| Value | Units | Test Method / Conditions | |
| Moisture (24 Hour) | 1.6 | % | ASTM D-570 |
| Moisture (50% RH) | 2.7 | % | ASTM D-570 |
| Moisture (Saturation) | 9.5 | % | ASTM D-570 |
| Moisture Content | max. 0.08 | % | ASTM D-6869 |
MD = Machine Direction and TD = Traverse Direction
Regulatory & Compliance
Technical Details & Test Data
Melt Viscosity vs. Temperature
Melt Temperature: 220°C (428°F)
Melt Temperature Range: 232°C (450°F) to 271°C (520°F).
Two key factors affect the melt viscosity (stiffness or fluidity of the melt):
1. The molecular weight (Mw) of the resin: Higher Mw resins will have a higher melt viscosity than lower Mw resins.
2. Temperature of the melt for any given Mw resin: Higher process temperatures will provide a more fluid melt viscosity than lower process temperatures.
Typical Barrel Profile for Cast Films
Barrel: 230-260°C (446-500°F)
Adapter: 260-266°C (500-510°F)
Die: 260°C (500°F)
Process Melt Temperature: 260-270°C (500-518°F)
Typical Barrel Profile for Tubular (Blown) Films
Barrel: 246-254°C (474-490°F)
Adapter: 260°C (500°F)
Die: 254°C (490°F)
Process Melt Temperature: 254-260°C (490-500°F)
Screw Parameters
Metering Section: 40%
Transition Section: 3 to 4 flights
Feed Section: Balance of screw length
Compression Ratio: 3.5:1 to 4.0:1
L/D Ratio: 24:1
Metering Section Flight Depth
| Screw Diameter | Recommended Depth |
| 1" | 0.055" |
| 1.5" | 0.060" |
| 2" | 0.070" |
| 2.5" | 0.080" |
| 3.5" | 0.100" |
| 4.5" | 0.115" |
| 6" | 0.135" |
Note: The values in this data sheet are for natural color resins only. Colorants or other additives may alter some or all of these properties. The data listed here fall within the normal range of product properties, but should not be used to establish specification limits nor used alone as the basis of design.
Storage & Handling
Material Handling
Aegis® PIR-H120ZP is supplied in sealed containers and drying prior to processing is not required. However, higher moisture is the primary cause of processing issues. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80°C (176°F) is recommended. Drying time is dependent on moisture level. More information about safe handling procedures can be obtained by requesting the Safety Data Sheet.