Capran® MT1200 Film
Sold by AdvanSix
Capran® MT1200 film is a 0.47 mil (12 micron) biaxially oriented Nylon 6 film with a metallized barrier coating by controlled vacuum deposition of high-purity aluminum. The metallized film has corona treatment on the reverse side. Capran® MT1200 film not only maintains its physical properties, but also offers exceptional gas barrier and a pure glossy metallic appearance, making it especially well-suited for packaging and balloon applications.
Polymer Name: BOPA (Nylon) Film, Polyamide 6 (PA 6)
Processing Methods: Film Extrusion, Extrusion
Physical Form: Film
Start Order
SecureOrder Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
Quote required
Ask AdvanSix Questions
Ask the Supplier
Popular AdvanSix Products
View all AdvanSix ProductsProduct NameProduct FamiliesApplications
TypeDocument Name
Technical Data Sheet
Capran® MT1200 Film Technical Data Sheet
Capran® MT1200 Film Technical Data Sheet
Technical Data SheetBrochure
AdvanSix Resins & Films for Packaging
AdvanSix Resins & Films for Packaging
BrochureKnowde Enhanced TDS
Identification & Functionality
Chemical Family
Polymer Name
Technologies
Capran® MT1200 Film Features & Benefits
Applications & Uses
Markets
Applications
Plastics & Elastomers Processing Methods
Properties
Physical Form
Typical Properties
| Value | Units | Test Method / Conditions | |
| Average Thickness (Target, 73°F (22.7°C), 50% RH) | 12 | microns | AdvanSix Method |
| Average Thickness (Tolerance, 73°F (22.7°C), 50% RH) | ± 5 | % | AdvanSix Method |
| Basis Weight (at 73°F (22.7°C), 50% RH) | 13.94 | g/sq.m | AdvanSix Method |
| Coefficient of Friction - Kinetic (Film to Film, 73°F (22.7°C), 50% RH) | 0.6 - 0.8 | - | ASTM D-1894 |
| Coefficient of Friction - Kinetic (Film to Metal, 73°F (22.7°C), 50% RH) | 0.2 - 0.3 | - | ASTM D-1894 |
| Dimensional Stability - MD (at 73°F (22.7°C), 50% RH) | max. 3.0 | % | Hot air at 320ºF (160ºC), 5 mins |
| Dimensional Stability - TD (at 73°F (22.7°C), 50% RH) | max. 2.5 | % | Hot air at 320ºF (160ºC), 5 mins |
| Elongation at Break - MD (73°F (22.7°C), 50% RH) | 70 - 105 | % | ASTM D-882 |
| Elongation at Break - TD (73°F (22.7°C), 50% RH) | 70 - 105 | % | ASTM D-882 |
| Modulus Secant MD (at 73°F (22.7°C), 50% RH) | 1,724 - 2,413 | MPa | ASTM D-882 |
| Modulus Secant TD (at 73°F (22.7°C), 50% RH) | 1,724 - 2,413 | MPa | ASTM D-882 |
| Optical Density | min. 2.2 | - | Macbeth |
| Oxygen Transmission Rate (at 73ºF (23ºC), 0% RH) | 0.47 - 1.09 | cc/m²/day | ASTM D-3985 |
| Surface Tension Non-Metallized Side (at 73°F (22.7°C), 50% RH) | min. 50 | dynes/cm | ASTM D-2578 |
| Tear Strength - Graves (at 73°F (22.7°C), 50% RH) | 600 - 1,000 | - | ASTM D-1004 |
| Tensile Strength - MD (at 73°F (23°C), 50% RH) | 234 - 310 | MPa | ASTM D-882 |
| Tensile Strength - TD (at 73°F (23°C), 50% RH) | 234 - 310 | MPa | ASTM D-882 |
| Water Vapor Transmission Rate (at 100ºF (37.7ºC), 100% RH) | 2.64 | gm/m²/day | ASTM F-1249 |
| Yield (at 73°F (22.7°C), 50% RH) | 71.76 | sq.m/kg | AdvanSix Method |