Capran® PIR-2500RT film from AdvanSix contains 100% post-industrial recycled (PIR) raw materials while providing the same top performance and processability as Capran® 2500RT, its standard, non-recycled counterpart.
Capran® PIR-2500RT is a 1.0 mil (25 micron) biaxially oriented nylon 6 film for retort applications and packaging applications that require optimum protection and performance. It features a high gas barrier, excellent toughness and puncture resistance, optical clarity, and exceptional flex crack resistance.
Ask AdvanSix Questions
Ask the Supplier
Popular AdvanSix Products
View All AdvanSix ProductsKnowde Enhanced TDS
Identification & Functionality
Capran® PIR-2500RT Features & Benefits
Capran® PIR-2500RT is a 1.0 mil (25 micron) biaxially oriented nylon 6 film. It features a superior balance of properties, including high gas barrier, excellent toughness and puncture resistance, optical clarity, and exceptional flex crack resistance.
Applications & Uses
Capran® PIR-2500RT is particularly recommended for retort applications and is well-suited for packaging applications requiring optimum protection and performance.
Properties
| Value | Units | Test Method / Conditions | |
| Average Thickness (Target, 73°F (22.7°C), 50% RH) | 25.4 | microns | AdvanSix Method |
| Average Thickness (Tolerance, 73°F (22.7°C), 50% RH) | (±) 5 | % | AdvanSix Method |
| Basis Weight (at 73°F (22.7°C), 50% RH) | 29.3 | g/sq.m | AdvanSix Method |
| Coefficient of Friction - Kinetic (Film to Film, 73°F (22.7°C), 50% RH) | 0.5 - 0.9 | - | ASTM D-1894 |
| Coefficient of Friction - Kinetic (Film to Metal, 73°F (22.7°C), 50% RH) | 0.2 - 0.3 | - | ASTM D-1894 |
| Dimensional Stability - MD (at 73°F (22.7°C), 50% RH) | max. 3.0 | % | Hot air at 320ºF (160ºC), 5 mins |
| Dimensional Stability - TD (at 73°F (22.7°C), 50% RH) | max. 2.5 | % | Hot air at 320ºF (160ºC), 5 mins |
| Elongation at Break - MD (73°F (22.7°C), 50% RH) | 80 - 110 | % | ASTM D-882 |
| Elongation at Break - TD (73°F (22.7°C), 50% RH) | 80 - 110 | % | ASTM D-882 |
| Haze (at 73°F (22.7°C), 50% RH) | max. 5.0 | % | ASTM D-1003 |
| Modulus Secant MD (at 73°F (22.7°C), 50% RH) | 1,724 - 2,413 | MPa | ASTM D-882 |
| Modulus Secant TD (at 73°F (22.7°C), 50% RH) | 1,724 - 2,413 | MPa | ASTM D-882 |
| Oxygen Transmission Rate (at 77ºF (25ºC), 0% RH) | 20 - 36 | cc/m²/day | ASTM D-3985 |
| Surface Tension Treated Side (at 73°F (22.7°C), 50% RH) | min. 56 | dynes/cm | ASTM D-2578 |
| Surface Tension Untreated Side (at 73°F (22.7°C), 50% RH) | 48 - 54 | dynes/cm | ASTM D-2578 |
| Tensile Strength at Break - MD (73°F (22.7°C), 50% RH) | 220 - 310 | MPa | ASTM D-882 |
| Tensile Strength at Break - TD (73°F (22.7°C), 50% RH) | 220 - 310 | MPa | ASTM D-882 |
| Water Vapor Transmission Rate (at 100ºF (37.7ºC), 100% RH) | 171 - 202 | gm/m²/day | ASTM F-1249 |
| Yield (at 73°F (22.7°C), 50% RH) | 34.13 | sq.m/kg | AdvanSix Method |