Features & Benefits
- Product Highlights
BENEFITS
- Very fast cure response
- Water soluble
- Low formaldehyde release
APPLICATION AREAS
- Emulsion topcoat systems
- Textile coatings
- Non-woven binders
- Microencapsulation
Applications & Uses
- Applications
- Compatible Substrates & Surfaces
- Coating Type
Properties
- Physical Form
- Appearance
- Clear Liquid
- Soluble in
- Water
- Typical Properties
- Solubility & Compatibility
SOLUBILITY
Alcohol Partial Esters Insoluble Ketones Insoluble Aromatic hydrocarbons Insoluble Aliphatic hydrocarbons Insoluble Water Complete COMPATIBILITY
Water reducible polymers Very good Polymer dispersions Very good Emulsions Very good
| Value | Units | Test Method / Conditions | |
| Color | max. 70 | APHA | — |
| Non-Volatile Content | 77-81 | %wt | — |
| Free Formaldehyde Content | max. 0.4 | % | — |
| Viscosity (25°C) | 600-1000 | mPa.s | — |
Technical Details & Test Data
- Backbone Polymer Selection
CYMEL 385 resin contains a combination of methoxymethyl, methylol and imino functionalities, making it a very effective crosslinker for backbone polymer resins containing hydroxyl, amide and, to some extent, carboxyl functional groups, such as those found on alkyd, polyester or acrylic resins. Although the optimum level of CYMEL 385 resin should be determined experimentally, ratios of 20 to 30% based on resin solids are typically most effective.
- Catalysis
CYMEL 385 resin may not require the addition of an acid catalyst to the formulation to obtain effective cure. In many instances, the acidity of the backbone polymer in the formulation is sufficient to catalyze the reaction under normal baking conditions (15 minutes at 120-150°C). If catalyst addition is required, then 0.5-1.0% of CYCAT® 296-9 catalyst based on total resin solids is recommended.
- Stability
FORMULATION STABILITY
It is essential that a tertiary amine, such as dimethylethanolamine or triethylamine, be used for neutralization and pH adjustment. For optimum stability, a pH of 7.5-8.5 should be maintained.
STORAGE STABILITY
CYMEL 385 resin has a shelf life of 180 days from the date of manufacture when stored at temperatures between 5°C and 32°C. Although low temperatures are not detrimental to stability, its viscosity will increase, possibly making the resin difficult to pump or pour. The viscosity will reduce again on warming, but care should be taken to avoid excessive local heat as this can cause an irreversible increase in viscosity. Beware of freezing.
Storage & Handling
- Shelf Life
- 180 Days