EBECRYL 154 is characterized by:
• Good compatibility and stability
• Low viscosity
• Light color
• Excellent reactivity
• Outstanding hardness
• Low haze development after abrasion
• No agglomeration or sedimentation
• PETA free
UV/EB cured products containing EBECRYL 154 are characterized by the following performance properties:
• High gloss
• High cross-link density
• Outstanding scratch and abrasion resistance
• Chemical resistance
• Low haze development
The actual properties of UV/EB cured products also depend on the selection of other formulation components such as reactive diluents, additives and photoinitiators.
Applications & Uses
- Applications
- Application Method
- Cure Method
- Coating Type
- Ink & Toner Type
- Suggested Applications
Formulated UV/EB curable products containing EBECRYL 154 may be applied via direct or reverse roll, offset gravure, metering rod, slot die, knife over roll, air knife, curtain, immersion, spin and spray coating methods. EBECRYL 154 is recommended for:
• Coatings requiring high scratch/abrasion resistance
• Coating requiring low haze development after abrasion
• As a modifying oligomer to increase cure speed, solvent resistance and abrasion resistance
Properties
- Physical Form
- Appearance
- Clear to slightly hazy liquid
- Typical Properties
- Cured Properties
Value | Units | Test Method / Conditions | |
Color | max. 2 | Gardner | — |
Functionalized Nanocomposite | 40-60 | % wt | — |
Particle Size Distribution | 15-40 | nm | — |
Viscosity (25°C) | 2800 | cP/mPa·s | — |
Value | Units | Test Method / Conditions | |
Elongation at Break | 1 | % | — |
Tensile Strength | 4000 (28) | psi (MPa) | — |
Young's Modulus | 64000 (441) | psi (MPa) | — |
Packaging & Availability
- Regional Availability
Storage & Handling
- Storage and Handling
Care should be taken not to expose the product to high temperature conditions, direct sunlight, ignition sources, oxidizing agents, alkalis or acids. This might cause uncontrollable polymerization of the product with the generation of heat. Storage and handling should be in stainless steel, amber glass, amber polyethylene or baked phenolic lined containers. Procedures that remove or displace oxygen from the material should be avoided. Do not store this material under an oxygen free atmosphere. Dry air is recommended to displace material removed from the container. Wash thoroughly after handling. Keep container tightly closed. Use with adequate ventilation