35N is a pure polyimide laminate and prepreg system for applications requiring high temperature performance. High Tg (250°C) results in low Z-direction expansion for resistance to PTH failure during PWB processing, and minimizes risk of latent PTH defects in-service. Reduced temperature and time to cure offers improved throughput compared to traditional polyimide cycles.

85N is the ultimate polyimide and laminate prepreg system fo PWB's requiring resistance to high temperature, both in process and in end-use applications. Bromine-free chemistry provides Bestin-Class thermal stability for applications with sustained high in-use temperatures as well as for use in lead-free soldering applications.

Greene, Tweed's Arlon® 1000, a tough, hig temperature, semi-crystalline thermoplastic, offers a unique combination of mechanical, thermal and chemical propertier. Arlon 1000 features superior compressive strength and minimum creep, as well as broad chemical resistance. Arlon is an excellent choice for applications such as valve seats and bushings greater abrasion resistance and lower wear and better fatigue properties than other thermoplastics.

Arlon 85HP’s unique blend of pure polyimide resin and micro-fi ne proprietary fi llers results in superior performance for demanding applications. Compared to conventional polyimide systems, 85HP has a lower Z-axis expansion and twice the thermal conductivity. 85HP reduces resin cracking and wicking in designs with high density plated through holes and vias. 85HP prepreg has resin fl ow characteristics and pressed thickness matching standard polyimides.

55NT is an epoxy laminate and prepreg system, reinforced with a non-woven aramid substrate. This system combines compatibility with lead-free processing, using a hightemperature epoxy resin, with the low in-plane (x,y) expansion and outstanding dimensional stability of non-woven aramid reinforcement.

33N is a flame retardant (UL94 V-O) polyimide laminate and prepreg system where the excellent high performance properties of polyimide need to be combined with flame retardance. High Tg (250°C) results in low overall z-axis expansion, and minimizes risk of latent PTH defects in-service.

37N is a polyimide low-flow prepreg suitable for bonding multilayer polyimide rigid-flex, attaching heat sinks to polyimide MLBs, or other applications where minimal and uniform resin flow is required.

Arlon 45N is a tough, high Tg (175°C by DSC) multifunctional epoxy laminate and prepreg system designed for use in a variety of higher layer count MLB's. Processeable using conventional FR-4 conditions, 45N is supplied to meet the requirements of IPC-4101/24.

47N is a low-flow epoxy prepreg engineered for binding multilayer epoxy rigid-flex or attaching heatsinks to multilayer PCBs. An optional low lamination temperature protects components already mounted on the PCB.

Arlon 44N is a high resin content multifunctional (175°C) epoxy prepreg system with a proprietary micordisperse ceramic filler system. 44N is engineered for the filling of clearance holes in thin Metal cores such as 0.006" Copperinvar- Copper or via holes in sequentially laminated MLB designs. Based on Arlon's 45N, the 44N system is compatible with conventional epoxy lamination and fabrication.

84N is a high performance ceramic-filled polyimide prepreg based on Arlon’s 85N pure polyimide system, designed for use in filling etched areas in polyimide multilayers that contain thick copper layers and for filling clearance holes in metal cores. The ceramic filler in the resin serves to reduce shrinkage and inhibit crack formulation during through-hole drilling in filled clearance areas.

55LM is an epoxy laminate and prepreg system, reinforced with non-woven aramid fiber, with substantially lower moisture absorption compared with conventional epoxy/aramid products, even in high-humidity environments.

35NQ is a pure polyimide laminate and prepreg system. Reinforced with woven Quartz fabric, combining the advantages of a reduced cure cycle, high temperature polyimide system (Tg >/=250°C), with low dielectric constant and loss tangent (DK = 3.5, loss 0.009 at 1 MHz) for applications requiring operation at RF/Microwave frequencies. Polyimide Quartz materials also exhibit reduced in-plane CTE for expansion matched SMT applications.