Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Reinforcement Material
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Physical Form
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
| Value | Units | Test Method / Conditions | |
| Tensile Strength | 5 (35) | kpsi (MPa) | IPC TM-650 2.4.18.3 |
| Flexural Strength | 38 (262) | kpsi (MPa) | IPC TM-650 2.4.4 |
| Peel Strength to Copper (1 oz/35 micron) After Thermal Stress | 3.6 (0.6) | lb/in (N/mm) | IPC TM-650 2.4.8 |
| Peel Strength to Copper (1 oz/35 micron) at Elevated Temperatures | 3.6 (0.6) | lb/in (N/mm) | IPC TM-650 2.4.8.2 |
| Peel Strength to Copper (1 oz/35 micron) After Process Solutions | 3.6 (0.6) | lb/in (N/mm) | IPC TM-650 2.4.8 |
| Young's Modulus | 2.0 (13.8) | Mpsi (GPa) | IPC TM-650 2.4.18.3 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity | 1.38 | - | ASTM D 792 |
| Water Absorption (0.062) | 0.3 | % | IPC TM-650 2.6.2.1 |
| Value | Units | Test Method / Conditions | |
| Glass Transition Temperature (Tg) - DSC | 170 | °C | IPC TM-650 2.4.25 |
| Coefficient of Thermal Expansion (X,Y) | 6.0 - 9.0 | ppm/°C | IPC TM-650 2.4.41 |
| Coefficient of Thermal Expansion (Z) - Below Tg | 99 | ppm/°C | IPC TM-650 2.4.24 |
| Coefficient of Thermal Expansion (Z) - Above Tg | 259 | ppm/°C | IPC TM-650 2.4.24 |
| z-axis Expansion (50-260oC) | 3.5 | % | IPC TM-650 2.4.24 |
| Decomposition Temperature (Td, 5%) | 368 | °C | IPC TM-650 2.3.41 |
| Decomposition Temperature (Td) - Initial | 351 | °C | IPC TM-650 2.3.41 |
| T300 | 28 | min | IPC TM-650 2.4.24.1 |
| T260 | min. 60 | min | IPC TM-650 2.4.24.1 |
| T288 | min. 60 | min | IPC TM-650 2.4.24.1 |
| Thermal Conductivity | 0.2 | W/(m K) | DIN 52616 |
| Value | Units | Test Method / Conditions | |
| Electrical Strength | 1240 (48.8) | Volts/mil (kV/mm) | IPC TM-650 2.5.6.2 |
| Dielectric Constant (1 MHz) | 3.8 | - | ASTM D 150 |
| Dissipation Factor (1 MHz) | 0.015 | - | ASTM D 150 |
| Volume Resistivity (C96/35/90) | 2.3 x 10^7 | MΩ-cm | IPC TM-650 2.5.17.1 |
| Volume Resistivity (E24/125) | 6.6 x 10^7 | MΩ-cm | IPC TM-650 2.5.17.1 |
| Surface Resistivity (C96/35/90) | 1.8 x 10^8 | MΩ | IPC TM-650 2.5.17.1 |
| Surface Resistivity (E24/125) | 1.6 x 10^8 | MΩ | IPC TM-650 2.5.17.1 |
| Arc Resistance | 165 | sec | IPC TM-650 2.5.1 |
| Value | Units | Test Method / Conditions | |
| Flammability | V-0 | class | UL-94 |