Braskem 2000 Series TI-2150C
Search in

Highly Crystalline Homopolymer phase, very high molecular weight EPR phase, very high flexural modulus, reduced emissions and reduced gels.

Braskem 2000 Series TI-2150C

Highly Crystalline Homopolymer phase, very high molecular weight EPR phase, very high flexural modulus, reduced emissions and reduced gels.
Take Action

Knowde Enhanced TDS

Expand All

+

Identification & Functionality

+

Features & Benefits

+
Performance Highlights
  • 100% ductility at -30 C
  • Demonstrated up to 30% reduction in external elastomer loading levels in TPO compounds
  • Potential impact modifier for compounding, automotive and packaging applications.
  • High stiffness and flow performance
  • Reduced emissions
  • Low gels
  • Suppressed tiger marking
  • Highly crystalline homopolymer phase
  • Very high molecular weight EPR phase
  • Very high flexural modulus

Applications & Uses

+
Plastics & Elastomers Processing Methods

Properties

+
Typical Properties
ValueUnitsTest Method / Conditions
Elongation at Yield (2 in/min, 50 mm/min)7%ASTM D-638
Flexural Modulus (0.05 in/min, 1.3 mm/min, 1% secant)235,000(1,620)psi(MPa)ASTM D-790A
Notched Izod Impact Strength (at 23°C)1.5(80)ft-lbs/in(J/m)ASTM D-256A
Tensile Strength at Yield (2 in/min, 50 mm/min)4,600(32)psi(MPa)ASTM D-638
Control Properties
ValueUnitsTest Method / Conditions
Nominal Melt Flow (230°C/2.16kg)15g/10 minASTM D-1238

Documents (4)

Name
Type
Polypropylene for Automotive and Compounding
Brochure
Polypropylene Products Overview
Brochure
Braskem TI2150C Safety Data Sheet
Safety Data Sheet
Braskem TI2150C Technical Data Sheet
Technical Data Sheet