Value | Units | Test Method / Conditions | |
Ultimate Tensile Strength (Die-C Shape, 500 mm/min) | 6.2 | MPa | ASTM D412 |
Stress at 100 % Elongation (Die-C Shape, 500 mm/min) | 4.7 | MPa | ASTM D412 |
Stress at 50 % Elongation (Die-C Shape, 500 mm/min) | 2.7 | MPa | ASTM D412 |
Tear Strength (Die-C, die cut) | 20 | kN/m | ASTM D624 |
Compression Set (23°C, 72 hrs) | 0.22 | - | ASTM D395-B |
Relative Abrasion Volume Loss | 66 | mm3 | ISO 4649 A |
Elongation at Break (Die-C Shape, 500 mm/min) | min. 130 | % | ASTM D412 |
Bayshore Rebound Resilience | 30 | % | ASTM D2632 |
Value | Units | Test Method / Conditions | |
Density | 1.027 | g/cm3 | ASTM D792 |
Value | Units | Test Method / Conditions | |
Glass Transition Temperature (DMA, tan (d)) | -9 | °C | ASTM D4065 |
Value | Units | Test Method / Conditions | |
Dissipation Factor (1 MHz) | 0.033 | - | ASTM D 150 |
Dielectric Constant (1 MHz) | 5.3 | - | ASTM D150 |