Crastin® ST820 NC010 is an unreinforced, Super Tough polybutylene terephthalate resin for injection molding.
Polymer Name: Polybutylene Terephthalate (PBT), Thermoplastic Polyester
Processing Methods: Coating, Injection Molding, Extrusion
Additives Included: Mold Release Agent
Flexural Modulus: 1550.0 MPa
Start Order
SecureOrder Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
Quote required
Popular DuPont Products
View all DuPont ProductsProduct NameProduct FamiliesApplications
Crastin® LW9030FR NC010 Blends & Alloys Other Devices & Assemblies, Connectors, Housings & Enclosures
Crastin® 6131 NC010 Polyesters & Copolyesters
Crastin® CE3054 BK580 Polyesters & Copolyesters
TypeDocument Name
Brochure
Technology Profile Laser Welding
Technology Profile Laser Welding
BrochureBrochure
DuPont Performance Polymers - Self Tapping Screws
DuPont Performance Polymers - Self Tapping Screws
BrochureBrochure
Electrical/Electronic Thermoplastic Encapsulation
Electrical/Electronic Thermoplastic Encapsulation
BrochureBrochure
Extrusion Applications
Extrusion Applications
BrochureOther
Design information on Crastin® PBT and Rynite® PET
Design information on Crastin® PBT and Rynite® PET
OtherOther
Hot Runner Manual
Hot Runner Manual
OtherBrochure
DuPont Performance Polymers
DuPont Performance Polymers
BrochureOther
General Design Principles - Module I: Chapter 9
General Design Principles - Module I: Chapter 9
OtherOther
Proper Use of Local Exhaust Ventilation During Processing of Plastics
Proper Use of Local Exhaust Ventilation During Processing of Plastics
OtherOther
Typical Processing Conditions for DuPont Engineering Polymers
Typical Processing Conditions for DuPont Engineering Polymers
OtherOther
DuPont Engineering Polymers General Design Principles - Module I
DuPont Engineering Polymers General Design Principles - Module I
OtherOther
General Design Principles - Module I: Chapter 7
General Design Principles - Module I: Chapter 7
OtherKnowde Enhanced TDS
Identification & Functionality
Additives Included
Chemical Family
Plastics & Elastomers Functions
Technologies
Crastin® ST820 NC010 Features & Benefits
Materials Features
Applications & Uses
Markets
Applications
Plastics & Elastomers End Uses
Plastics & Elastomers Processing Methods
Properties
Chemical Resistance
Color
Flame Rating
Part Marking Code
Mechanical Properties
Value | Units | Test Method / Conditions | |
Tensile Modulus | 1700 | MPa | ISO 527-1/-2 |
Yield Stress | 38 | MPa | ISO 527-1/-2 |
Yield Strain | 7 | % | ISO 527-1/-2 |
Flexural Modulus | 1550 | MPa | ISO 178 |
Flexural Strength | 50 | MPa | ISO 178 |
Stress (at Break, 50mm/min) | 30 | MPa | ISO 527-1/-2 |
Nominal Strain (at Break) | min. 50 | % | ISO 527-1/-2 |
Strain (at Break, 50mm/min) | 150 | % | ISO 527-1/-2 |
Charpy Impact Strength (at 23°C) | N | kJ/m² | ISO 179/1eU |
Charpy Impact Strength (at -30°C) | N | kJ/m² | ISO 179/1eU |
Poisson's Ratio | 0.42 | - | - |
Notched Charpy Impact Strength (at 23°C) | 85 | kJ/m² | ISO 179/1eA |
Notched Charpy Impact Strength (at -30°C) | 10 | kJ/m² | ISO 179/1eA |
Notched Charpy Impact Strength (at -40°C) | 10 | kJ/m² | ISO 179/1eA |
Notched Izod Impact Strength (at 23°C) | 60 | kJ/m² | ISO 180/1A |
Notched Izod Impact Strength (at -30°C) | 15 | kJ/m² | ISO 180/1A |
Notched Izod Impact Strength (at -40°C) | 10 | kJ/m² | ISO 180/1A |
Izod Impact Strength (at 23°C) | N | kJ/m² | ISO 180/1U |
Izod Impact Strength (at -30°C) | N | kJ/m² | ISO 180/1U |
Izod Impact Strength (at -40°C) | 270 | kJ/m² | ISO 180/1U |
Hardness (Rockwell Scale R) | 104 | - | ISO 2039-2 |
Typical Properties
Value | Units | Test Method / Conditions | |
Resin Identification | PBT-HI | - | ISO 1043 |
Thermal Properties
Value | Units | Test Method / Conditions | |
Specific Heat Capacity of Melt | 2100 | J/(kg K) | - |
Melt Temperature (at 10°C/min) | 225 | °C | ISO 11357-1/-3 |
Glass Transition Temperature (at 10°C/min) | 55 | °C | ISO 11357-1/-2 |
Temperature of Deflection Under Load (1.8 Mpa) | 50 | °C | ISO 75-1/-2 |
Temperature of Deflection Under Load (0.45 Mpa) | 100 | °C | ISO 75-1/-2 |
Temperature of Deflection Under Load (0.45 Mpa, Annealed) | 145 | °C | ISO 75-1/-2 |
Vicat Softening Temperature (at 50°C/H 50N) | 125 | °C | ISO 306 |
Coefficient of Linear Thermal Expansion (Parallel) | 147 | E-6/K | ISO 11359-1/-2 |
Coefficient of Linear Thermal Expansion (Normal) | 155 | E-6/K | ISO 11359-1/-2 |
Coefficient of Linear Thermal Expansion (Normal, at -40 to 23°C) | 108 | E-6/K | ISO 11359-1/-2 |
Coefficient of Linear Thermal Expansion (Normal, at 55-160°C) | 191 | E-6/K | ISO 11359-1/-2 |
Coefficient of Linear Thermal Expansion (Parallel, at -40 to 23°C) | 99 | E-6/K | ISO 11359-1/-2 |
Coefficient of Linear Thermal Expansion (Parallel, at 55-160°C) | 233 | E-6/K | ISO 11359-1/-2 |
Relative Thermal Index (Electrical, 0.75mm) | 75 | °C | UL 746B |
Relative Thermal Index (Impact, 0.75mm) | 75 | °C | UL 746B |
Relative Thermal Index (Strength, 0.75mm) | 75 | °C | UL 746B |
TGA curve | available | - | ISO 11359-1/-2 |
Thermal Conductivity of Melt | 0.2 | W/(m K) | ISO 22007-2 |
Electrical Properties
Value | Units | Test Method / Conditions | |
Surface Resistivity | 1000000000000000 | Ohm | IEC 62631-3-2 |
Electric Strength | 27 | kV/mm | IEC 60243-1 |
Relative Permittivity (at 1MHz) | 3.4 | - | IEC 62631-2-1 |
Dissipation Factor (at 100 Hz) | 200 | E-4 | IEC 62631-2-1 |
Dissipation Factor (at 1 MHz) | 190 | E-4 | IEC 62631-2-1 |
Comparative Tracking Index | 600 | - | IEC 60112 |
Volume Resistivity | min. 1E13 | Ohm.m | IEC 62631-3-1 |
Flammability
Value | Units | Test Method / Conditions | |
Oxygen Index | 19 | % | ISO 4589-1/-2 |
FMVSS Class | B | - | ISO 3795 (FMVSS 302) |
Burning Behavior (at 0.8mm Thickness) | UL94 HB | class | IEC 60695-11-10 |
Glow Wire Flammability Index (at 2mm) | 700 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index (at 3mm) | 700 | °C | IEC 60695-2-12 |
Burning Rate (at 1mm Thickness) | 38 | mm/min | ISO 3795 (FMVSS 302) |
Other Properties
Value | Units | Test Method / Conditions | |
Humidity Absorption (at 2mm) | 0.12 | % | Sim. to ISO 62 |
Water Absorption (at 2mm) | 0.31 | % | Sim. to ISO 62 |
Density of Melt | 1030 | kg/m³ | - |
Density | 1220 | kg/m³ | ISO 1183 |
Processing Information (Extrusion)
Value | Units | Test Method / Conditions | |
Drying Temperature | 110 - 130 | °C | - |
Drying Time (Dehumidified Dryer) | 2 - 4 | h | - |
Processing Moisture Content | max. 0.04 | % | - |
Melt Temperature Range | 240 - 260 | °C | - |
Processing Information (Injection Molding)
Value | Units | Test Method / Conditions | |
Drying Recommended | yes | - | - |
Drying Temperature | 120 | °C | - |
Drying Time (Dehumidified Dryer) | 2 - 4 | h | - |
Processing Moisture Content | max. 0.04 | % | - |
Hold Pressure Range | min. 60 | MPa | - |
Hold Pressure Time | 3 | s/mm | - |
Back Pressure | As low as possible | MPa | - |
Ejection Temperature | 170 | °C | - |
Melt Temperature (Optimum) | 250 | °C | - |
Melt Temperature (Minimum) | 240 | °C | - |
Melt Temperature (Maximum) | 260 | °C | - |
Mold Temperature (Optimum) | 80 | °C | - |
Mold Temperature (Minimum) | 30 | °C | - |
Mold Temperature (Maximum) | 130 | °C | - |
VDA Properties
Value | Units | Test Method / Conditions | |
Fogging (G-Value, Condensate) | 0.1 | mg | ISO 6452 |
Rheological Properties
Value | Units | Test Method / Conditions | |
Melt Mass Flow Rate (at 250°C, 5 kg) | 5 | g/10min | ISO 1133 |
Mold Shrinkage (Parallel) | 2.4 | % | ISO 294-4, 2577 |
Mold Shrinkage (Normal) | 1.9 | % | ISO 294-4, 2577 |
Mold Shrinkage (Parallel, Annealed) | 2.5 | % | ISO 294-4 |
Post Mold Shrinkage (Normal, 48h at 80°C) | 0.6 | % | ISO 294-4 |
Post Mold Shrinkage (Parallel, 48h at 80°C) | 0.8 | % | ISO 294-4 |
Chemical Resistance
Chemical Type | Chemical Name | Resistance |
Acids | Acetic Acid (5% by mass) (23°C) | Probably Resistant |
Acids | Chromic Acid solution (40% by mass) (23°C) | Not Recommended |
Acids | Citric Acid solution (10% by mass) (23°C) | Probably Resistant |
Acids | Hydrochloric Acid (36% by mass) (23°C) | Not Recommended |
Acids | Lactic Acid (10% by mass) (23°C) | Probably Resistant |
Acids | Nitric Acid (40% by mass) (23°C) | Not Recommended |
Acids | Sulfuric Acid (38% by mass) (23°C) | Not Recommended |
Acids | Sulfuric Acid (5% by mass) (23°C) | Not Recommended |
Alcohols | Ethanol (23°C) | Probably Resistant |
Alcohols | Isopropyl alcohol (23°C) | Probably Resistant |
Alcohols | Methanol (23°C) | Probably Resistant |
Bases | Ammonium Hydroxide solution (10% by mass) (23°C) | Probably Resistant |
Bases | Sodium Hydroxide solution (1% by mass) (23°C) | Probably Resistant |
Bases | Sodium Hydroxide solution (35% by mass) (23°C) | Not Recommended |
Ethers | Diethyl ether (23°C) | Probably Resistant |
Hydrocarbons | iso-Octane (23°C) | Probably Resistant |
Hydrocarbons | n-Hexane (23°C) | Probably Resistant |
Hydrocarbons | Toluene (23°C) | Probably Resistant |
Ketones | Acetone (23°C) | Probably Resistant |
Mineral oils | Insulating Oil (23°C) | Probably Resistant |
Mineral oils | SAE 10W40 multigrade motor oil (130°C) | Not Recommended |
Mineral oils | SAE 10W40 multigrade motor oil (23°C) | Probably Resistant |
Mineral oils | SAE 80/90 hypoid-gear oil (130°C) | Not Recommended |
Other | 1% nonylphenoxy-polyethyleneoxy ethanol in water (23°C) | Probably Resistant |
Other | 50% Oleic acid + 50% Olive Oil (23°C) | Probably Resistant |
Other | DOT No. 4 Brake fluid (130°C) | Not Recommended |
Other | Ethyl Acetate (23°C) | Probably Resistant |
Other | Ethylene Glycol (50% by mass) in water (108°C) | Not Recommended |
Other | Hydrogen peroxide (23°C) | Not Recommended |
Other | Phenol solution (5% by mass) (23°C) | Probably Resistant |
Other | Water (23°C) | Probably Resistant |
Other | Water (90°C) | Not Recommended |
Salt solutions | Sodium Carbonate solution (2% by mass) (23°C) | Probably Resistant |
Salt solutions | Sodium Carbonate solution (20% by mass) (23°C) | Probably Resistant |
Salt solutions | Sodium Chloride solution (10% by mass) (23°C) | Probably Resistant |
Salt solutions | Sodium Hypochlorite solution (10% by mass) (23°C) | Probably Resistant |
Salt solutions | Zinc Chloride solution (50% by mass) (23°C) | Probably Resistant |
Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (>90°C) | Not Recommended |
Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (23°C) | Probably Resistant |
Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (90°C) | Probably Resistant |
Standard Fuels | ISO 1817 Liquid 1 - E5 (60°C) | Not Recommended |
Standard Fuels | ISO 1817 Liquid 2 - M15E4 (60°C) | Not Recommended |
Standard Fuels | ISO 1817 Liquid 3 - M3E7 (60°C) | Not Recommended |
Standard Fuels | ISO 1817 Liquid 4 - M15 (60°C) | Not Recommended |
Standard Fuels | Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23°C) | Probably Resistant |
Standard Fuels | Standard fuel without alcohol (pref. ISO 1817 Liquid C) (23°C) | Probably Resistant |
Regulatory & Compliance
Certifications & Compliance
OEM Standards
Technical Details & Test Data
Viscosity vs Shear Rate
Shear Stress vs Shear Rate
Stress vs Strain
Secant Modulus vs Strain
Stress vs Strain (Isochronous, 23°C)
Creep Modulus vs Time (23°C)
Tensile Modulus vs Temperature
Packaging & Availability
Country Availability
Regional Availability
Crastin® ST820 NC010