Delrin® 100 is a high viscosity acetal homopolymer for use in easy-to-fill molds. Delrin® 100 provides optimum mechanical performance with its excellent combination of toughness and strength.
Polymer Name: Polyacetal Homopolymer (POM)
Processing Methods: Injection Molding, Extrusion
Additives Included: Mold Release Agent
Flexural Modulus: 2800.0 MPa
Start Order
SecureOrder Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
View
Popular DuPont Products
View All DuPont Products Delrin® 300TE BK602
Delrin® 500AL NC010
Delrin® 570 NC000
TypeDocument Name
Brochure
Technology Profile Laser Welding
Technology Profile Laser Welding
BrochureTechnical Data Sheet
Delrin® 100 NC010 Technical Data Sheet
Delrin® 100 NC010 Technical Data Sheet
Technical Data SheetOther
Hot Runner Manual for Robust Molding of Semi-crystalline Resins
Hot Runner Manual for Robust Molding of Semi-crystalline Resins
OtherBrochure
DuPont Performance Polymers - Self Tapping Screws
DuPont Performance Polymers - Self Tapping Screws
BrochureOther
Delrin® acetal resin Molding Guide
Delrin® acetal resin Molding Guide
OtherOther
Safety Restraint Systems
Safety Restraint Systems
OtherBrochure
Electrical/Electronic Thermoplastic Encapsulation
Electrical/Electronic Thermoplastic Encapsulation
BrochureBrochure
Delrin® E-Grades for Low Emissions
Delrin® E-Grades for Low Emissions
BrochureOther
Delrin® Acetal Homopolymer Resin Molding Tips
Delrin® Acetal Homopolymer Resin Molding Tips
OtherOther
Delrin® Design Guide-Module III
Delrin® Design Guide-Module III
OtherOther
Delrin® vs Acetal Copolymer White Paper
Delrin® vs Acetal Copolymer White Paper
OtherOther
General Design Principles - Module I: Chapter 8
General Design Principles - Module I: Chapter 8
OtherKnowde Enhanced TDS
Identification & Functionality
Additives Included
Polymer Name
Plastics & Elastomers Functions
Technologies
Product Families
Delrin® 100 NC010 Features & Benefits
Applications & Uses
Markets
Applications
Plastics & Elastomers End Uses
Plastics & Elastomers Processing Methods
Properties
Chemical Resistance
Color
Flame Rating
Part Marking Code
Mechanical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 2900 | MPa | ISO 527-1/-2 |
| Yield Stress | 71 | MPa | ISO 527-1/-2 |
| Yield Strain | 26 | % | ISO 527-1/-2 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Flexural Strength | 93 | MPa | ISO 178 |
| Compressive Strength | 110 | MPa | ISO 604 |
| Nominal Strain (at Break) | 45 | % | ISO 527-1/-2 |
| Ball Indentation Hardness (H 358/30) | 173 | MPa | ISO 2039-1 |
| Flexural Stress (at 3.5%) | 77 | MPa | ISO 178 |
| Poisson's Ratio | 0.37 | - | - |
| Tensile Creep Modulus (1h) | 2900 | MPa | ISO 899-1 |
| Tensile Creep Modulus (1000h) | 1600 | MPa | ISO 899-1 |
| Charpy Impact Strength (at 23°C) | N | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (at -30°C) | 425 | kJ/m² | ISO 179/1eU |
| Notched Charpy Impact Strength (at 23°C) | 15 | kJ/m² | ISO 179/1eA |
| Notched Charpy Impact Strength (at -30°C) | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (at 23°C) | 14 | kJ/m² | ISO 180/1A |
| Notched Izod Impact Strength (at -40°C) | 13 | kJ/m² | ISO 180/1A |
| Hardness (Rockwell Scale M) | 90 | - | ISO 2039-2 |
| Hardness (Rockwell Scale R) | 121 | - | ISO 2039-2 |
| Abrasion Resistance ᴰˢ | 4 | mm³ | ISO 4649 |
Typical Properties
| Value | Units | Test Method / Conditions | |
| Resin Identification | POM | - | ISO 1043 |
Thermal Properties
| Value | Units | Test Method / Conditions | |
| Specific Heat Capacity of Melt | 3000 | J/(kg K) | - |
| Temperature Index (Tensile Strength, 5000h) | 125 | °C | IEC 60216-1 |
| Melt Temperature (at 10°C/min) | 178 | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.8 Mpa) | 95 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (1.8 Mpa, Annealed) | 115 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 Mpa) | 160 | °C | ISO 75-1/-2 |
| Vicat Softening Temperature (at 50°C/H 50N) | 160 | °C | ISO 306 |
| Vicat Softening Temperature (at 50°C/H 10N) | 175 | °C | ISO 306 |
| Coefficient of Linear Thermal Expansion (Parallel) | 110 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (Normal) | 110 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (Normal, at -40 to 23°C) | 100 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (Parallel, at -40 to 23°C) | 100 | E-6/K | ISO 11359-1/-2 |
| Relative Thermal Index (Electrical, 0.75mm) | 50 | °C | UL 746B |
| Relative Thermal Index (Electrical, 1.5mm) | 105 | °C | UL 746B |
| Relative Thermal Index (Electrical, 3mm) | 105 | °C | UL 746B |
| Relative Thermal Index (Electrical, 6mm) | 105 | °C | UL 746B |
| Relative Thermal Index (Impact, 0.75mm) | 50 | °C | UL 746B |
| Relative Thermal Index (Impact, 1.5mm) | 85 | °C | UL 746B |
| Relative Thermal Index (Impact, 3mm) | 85 | °C | UL 746B |
| Relative Thermal Index (Impact, 6mm) | 85 | °C | UL 746B |
| Relative Thermal Index (Strength, 0.75mm) | 50 | °C | UL 746B |
| Relative Thermal Index (Strength, 1.5mm) | 90 | °C | UL 746B |
| Relative Thermal Index (Strength, 3mm) | 90 | °C | UL 746B |
| Relative Thermal Index (Strength, 6mm) | 90 | °C | UL 746B |
| Temperature Index (Tensile Strength, 20000h) | 110 | °C | IEC 60216-1 |
| Effective Thermal Diffusivity | 1.0e-07 | m²/s | - |
Electrical Properties
| Value | Units | Test Method / Conditions | |
| Surface Resistivity | 30000000000000 | Ohm | IEC 62631-3-2 |
| Electric Strength | 41 | kV/mm | IEC 60243-1 |
| Relative Permittivity (at 100Hz) | 3.9 | - | IEC 62631-2-1 |
| Relative Permittivity (at 1MHz) | 3.8 | - | IEC 62631-2-1 |
| Dissipation Factor (at 100 Hz) | 10 | E-4 | IEC 62631-2-1 |
| Dissipation Factor (at 1 MHz) | 55 | E-4 | IEC 62631-2-1 |
| Comparative Tracking Index | 600 | - | IEC 60112 |
| Volume Resistivity | min. 1E13 | Ohm.m | IEC 62631-3-1 |
Flammability
| Value | Units | Test Method / Conditions | |
| FMVSS Class | B | - | ISO 3795 (FMVSS 302) |
| Burning Behavior (at 1.5mm Nominal Thickness) | UL94 HB | class | IEC 60695-11-10 |
| Burning Behavior (at 0.8mm Thickness) | UL94 HB | class | IEC 60695-11-10 |
| Glow Wire Flammability Index (at 1mm) | 550 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2mm) | 550 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 3mm) | 550 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (at 0.75mm) | 550 | °C | IEC 60695-2-13 |
| Glow Wire Ignition Temperature (at 0.4mm) | 550 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (at 1mm) | 550 | °C | IEC 60695-2-13 |
| Glow Wire Ignition Temperature (at 1.5mm) | 550 | °C | IEC 60695-2-13 |
| Glow Wire Ignition Temperature (at 2mm) | 550 | °C | IEC 60695-2-13 |
| Glow Wire Ignition Temperature (at 3mm) | 550 | °C | IEC 60695-2-13 |
| Burning Rate (at 1mm Thickness) | 40 | mm/min | ISO 3795 (FMVSS 302) |
Other Properties
| Value | Units | Test Method / Conditions | |
| Humidity Absorption (at 2mm) | 0.2 | % | Sim. to ISO 62 |
| Water Absorption (at 2mm) | 0.9 | % | Sim. to ISO 62 |
| Water Absorption (Immersion 24h) | 0.27 | % | Sim. to ISO 62 |
| Density of Melt | 1190 | kg/m³ | - |
| Density | 1420 | kg/m³ | ISO 1183 |
Processing Information (Extrusion)
| Value | Units | Test Method / Conditions | |
| Melt Temperature Range | 195 - 205 | °C | - |
| Melt Temperature (Optimum) | 200 | °C | - |
| Drying Temperature | 80 | °C | - |
| Drying Time (Dehumidified Dryer) | 2 - 4 | h | - |
| Processing Moisture Content | max. 0.2 | % | - |
Processing Information (Injection Molding)
| Value | Units | Test Method / Conditions | |
| Drying Recommended | yes | - | - |
| Drying Temperature | 80 | °C | - |
| Drying Time (Dehumidified Dryer) | 2 - 4 | h | - |
| Processing Moisture Content | max. 0.2 | % | - |
| Hold Pressure Range | 90 - 110 | MPa | - |
| Hold Pressure Time | 8 | s/mm | - |
| Annealing Temperature | 160 | °C | - |
| Melt Temperature (Optimum) | 215 | °C | - |
| Melt Temperature (Minimum) | 210 | °C | - |
| Melt Temperature (Maximum) | 220 | °C | - |
| Maximum Screw Tangential Speed | 0.2 | m/s | - |
| Mold Temperature (Optimum) | 90 | °C | - |
| Mold Temperature (Minimum) | 80 | °C | - |
| Mold Temperature (Maximum) | 100 | °C | - |
| Annealing Time (Optional) | 30 | min/mm | - |
VDA Properties
| Value | Units | Test Method / Conditions | |
| Fogging (G-Value, Condensate) | 0.1 | mg | ISO 6452 |
Rheological Properties
| Value | Units | Test Method / Conditions | |
| Melt Volume-Flow Rate (at 190°C, 2.16 kg) | 1.9 | cm³/10min | ISO 1133 |
| Melt Mass Flow Rate (at 190°C, 2.16 kg) | 2.2 | g/10min | ISO 1133 |
| Mold Shrinkage (Parallel) | 2.2 | % | ISO 294-4, 2577 |
| Mold Shrinkage (Normal) | 1.9 | % | ISO 294-4, 2577 |
| Mold Shrinkage (Parallel, Annealed) | 3 | % | ISO 294-4 |
| Mold Shrinkage (Normal, Annealed) | 2.4 | % | ISO 294-4 |
Note
- [DS]: Derived from similar grade
Chemical Resistance
| Chemical Type | Chemical Name | Resistance |
| Acids | Acetic Acid (5% by mass) (23°C) | Probably Resistant |
| Acids | Chromic Acid solution (40% by mass) (23°C) | Not Recommended |
| Acids | Citric Acid solution (10% by mass) (23°C) | Not Recommended |
| Acids | Hydrochloric Acid (36% by mass) (23°C) | Not Recommended |
| Acids | Lactic Acid (10% by mass) (23°C) | Not Recommended |
| Acids | Nitric Acid (40% by mass) (23°C) | Not Recommended |
| Acids | Sulfuric Acid (38% by mass) (23°C) | Not Recommended |
| Acids | Sulfuric Acid (5% by mass) (23°C) | Not Recommended |
| Alcohols | Ethanol (23°C) | Probably Resistant |
| Alcohols | Isopropyl alcohol (23°C) | Probably Resistant |
| Alcohols | Methanol (23°C) | Probably Resistant |
| Bases | Ammonium Hydroxide solution (10% by mass) (23°C) | Not Recommended |
| Bases | Sodium Hydroxide solution (1% by mass) (23°C) | Not Recommended |
| Bases | Sodium Hydroxide solution (35% by mass) (23°C) | Not Recommended |
| Ethers | Diethyl ether (23°C) | Probably Resistant |
| Hydrocarbons | iso-Octane (23°C) | Probably Resistant |
| Hydrocarbons | n-Hexane (23°C) | Probably Resistant |
| Hydrocarbons | Toluene (23°C) | Probably Resistant |
| Ketones | Acetone (23°C) | Probably Resistant |
| Mineral oils | Automatic hypoid-gear oil Shell Donax TX (135°C) | Not Recommended |
| Mineral oils | Hydraulic oil Pentosin CHF 202 (125°C) | Not Recommended |
| Mineral oils | Insulating Oil (23°C) | Probably Resistant |
| Mineral oils | Motor oil OS206 304 Ref.Eng.Oil, ISP (135°C) | Not Recommended |
| Mineral oils | SAE 10W40 multigrade motor oil (130°C) | Not Recommended |
| Mineral oils | SAE 10W40 multigrade motor oil (23°C) | Probably Resistant |
| Mineral oils | SAE 80/90 hypoid-gear oil (130°C) | Not Recommended |
| Other | 1% nonylphenoxy-polyethyleneoxy ethanol in water (23°C) | Probably Resistant |
| Other | 50% Oleic acid + 50% Olive Oil (23°C) | Probably Resistant |
| Other | DOT No. 4 Brake fluid (120°C) | Not Recommended |
| Other | DOT No. 4 Brake fluid (130°C) | Not Recommended |
| Other | Ethyl Acetate (23°C) | Probably Resistant |
| Other | Ethylene Glycol (50% by mass) in water (108°C) | Not Recommended |
| Other | Hydrogen peroxide (23°C) | Not Recommended |
| Other | Phenol solution (5% by mass) (23°C) | Probably Resistant |
| Other | Water (23°C) | Probably Resistant |
| Other | Water (90°C) | Not Recommended |
| Salt solutions | Sodium Carbonate solution (2% by mass) (23°C) | Not Recommended |
| Salt solutions | Sodium Carbonate solution (20% by mass) (23°C) | Not Recommended |
| Salt solutions | Sodium Chloride solution (10% by mass) (23°C) | Probably Resistant |
| Salt solutions | Sodium Hypochlorite solution (10% by mass) (23°C) | Not Recommended |
| Salt solutions | Zinc Chloride solution (50% by mass) (23°C) | Not Recommended |
| Standard Fuels | Diesel EN 590 (100°C) | Not Recommended |
| Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (>90°C) | Not Recommended |
| Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (23°C) | Probably Resistant |
| Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (90°C) | Not Recommended |
| Standard Fuels | ISO 1817 Liquid 1 - E5 (60°C) | Probably Resistant |
| Standard Fuels | ISO 1817 Liquid 2 - M15E4 (60°C) | Probably Resistant |
| Standard Fuels | ISO 1817 Liquid 3 - M3E7 (60°C) | Probably Resistant |
| Standard Fuels | ISO 1817 Liquid 4 - M15 (60°C) | Probably Resistant |
| Standard Fuels | Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23°C) | Probably Resistant |
| Standard Fuels | Standard fuel without alcohol (pref. ISO 1817 Liquid C) (23°C) | Probably Resistant |
| Sterilization methods | Ethylene Oxide | Probably Resistant |
Regulatory & Compliance
Certifications & Compliance
OEM Specifications
Technical Details & Test Data
Viscosity vs Shear Rate
Shear Stress vs Shear Rate
Dynamic Shear Modulus vs Temperature
Stress vs Strain
Secant Modulus vs Strain
Specific Volume Temperature (pvT)
Packaging & Availability
Country Availability
Regional Availability
Delrin® 100 NC010
DuPont