Delrin® 100T is a toughened, high viscosity acetal homopolymer with superior impact resistance. It is designed for highly stressed parts where outstanding toughness is required.
Polymer Name: Polyacetal Homopolymer (POM)
Processing Methods: Injection Molding, Extrusion
Additives Included: Mold Release Agent, Lubricant (Unspecified)
Flexural Modulus: 1700.0 MPa
Start Order
SecureOrder Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
View
Popular DuPont Products
View All DuPont Products Delrin® 300TE BK602
Delrin® 500AL NC010
Delrin® 570 NC000
Knowde Enhanced TDS
Identification & Functionality
Additives Included
Polymer Name
Plastics & Elastomers Functions
Technologies
Product Families
Delrin® 100T NC010 Features & Benefits
Applications & Uses
Markets
Applications
Plastics & Elastomers End Uses
Plastics & Elastomers Processing Methods
Properties
Mechanical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 1900 | MPa | ISO 527-1/-2 |
| Yield Stress | 55 | MPa | ISO 527-1/-2 |
| Yield Strain | 25 | % | ISO 527-1/-2 |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Poisson's Ratio | 0.41 | - | - |
| Nominal Strain (at Break) | min. 50 | % | ISO 527-1/-2 |
| Flexural Stress (at 3.5%) | 52 | MPa | ISO 178 |
| Charpy Impact Strength (at 23°C) | N | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (at -30°C) | N | kJ/m² | ISO 179/1eU |
| Notched Charpy Impact Strength (at 23°C) | 26 | kJ/m² | ISO 179/1eA |
| Notched Charpy Impact Strength (at -30°C) | 14 | kJ/m² | ISO 179/1eA |
| Hardness (Rockwell Scale M) | 59 | - | ISO 2039-2 |
| Hardness (Rockwell Scale R) | 113 | - | ISO 2039-2 |
Typical Properties
| Value | Units | Test Method / Conditions | |
| Resin Identification | POM-I | - | ISO 1043 |
Thermal Properties
| Value | Units | Test Method / Conditions | |
| Melt Temperature (at 10°C/min) | 178 | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.8 Mpa) | 72 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 Mpa) | 130 | °C | ISO 75-1/-2 |
| Vicat Softening Temperature (at 50°C/H 10N) | 173 | °C | ISO 306 |
| Coefficient of Linear Thermal Expansion (Parallel) | 120 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (Normal) | 120 | E-6/K | ISO 11359-1/-2 |
| Relative Thermal Index (Electrical, 1.5mm) | 100 | °C | UL 746B |
| Relative Thermal Index (Electrical, 3mm) | 100 | °C | UL 746B |
| Relative Thermal Index (Impact, 1.5mm) | 85 | °C | UL 746B |
| Relative Thermal Index (Impact, 3mm) | 85 | °C | UL 746B |
| Relative Thermal Index (Strength, 1.5mm) | 85 | °C | UL 746B |
| Relative Thermal Index (Strength, 3mm) | 85 | °C | UL 746B |
| TGA curve | available | - | ISO 11359-1/-2 |
| Effective Thermal Diffusivity | 7.0e-08 | m²/s | - |
Electrical Properties
| Value | Units | Test Method / Conditions | |
| Dissipation Factor (at 1 MHz) | 90 | E-4 | IEC 62631-2-1 |
| Volume Resistivity | 6000000000000 | Ohm.m | IEC 62631-3-1 |
| Comparative Tracking Index | 600 | - | IEC 60112 |
Flammability
| Value | Units | Test Method / Conditions | |
| FMVSS Class | B | - | ISO 3795 (FMVSS 302) |
| Burning Behavior (at 1.5mm Nominal Thickness) | UL94 HB | class | IEC 60695-11-10 |
| Glow Wire Flammability Index (at 1mm) | 550 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2mm) | 550 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 3mm) | 550 | °C | IEC 60695-2-12 |
| Burning Rate (at 1mm Thickness) | 42 | mm/min | ISO 3795 (FMVSS 302) |
Other Properties
| Value | Units | Test Method / Conditions | |
| Humidity Absorption (at 2mm) | 0.3 | % | Sim. to ISO 62 |
| Water Absorption (at 2mm) | 0.9 | % | Sim. to ISO 62 |
| Density | 1370 | kg/m³ | ISO 1183 |
Processing Information (Extrusion)
| Value | Units | Test Method / Conditions | |
| Melt Temperature Range | 195 - 205 | °C | - |
| Melt Temperature (Optimum) | 200 | °C | - |
| Drying Temperature | 80 | °C | - |
| Processing Moisture Content | max. 0.05 | % | - |
| Drying Time (Dehumidified Dryer) | 4 - 8 | h | - |
Processing Information (Injection Molding)
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 80 | °C | - |
| Drying Recommended | yes | - | - |
| Drying Time (Dehumidified Dryer) | 4 - 8 | h | - |
| Processing Moisture Content | max. 0.05 | % | - |
| Hold Pressure Range | 60 - 80 | MPa | - |
| Hold Pressure Time | 7.5 | s/mm | - |
| Annealing Temperature | 160 | °C | - |
| Melt Temperature (Optimum) | 205 | °C | - |
| Melt Temperature (Minimum) | 200 | °C | - |
| Melt Temperature (Maximum) | 210 | °C | - |
| Maximum Screw Tangential Speed | 0.2 | m/s | - |
| Mold Temperature (Optimum) | 50 | °C | - |
| Mold Temperature (Minimum) | 40 | °C | - |
| Mold Temperature (Maximum) | 60 | °C | - |
| Annealing Time (Optional) | 30 | min/mm | - |
VDA Properties
| Value | Units | Test Method / Conditions | |
| Emissions | max. 8 | mg/kg | VDA 275 |
Rheological Properties
| Value | Units | Test Method / Conditions | |
| Melt Volume-Flow Rate (at 190°C, 2.16 kg) | 1.9 | cm³/10min | ISO 1133 |
| Melt Mass Flow Rate (at 190°C, 2.16 kg) | 2.1 | g/10min | ISO 1133 |
| Mold Shrinkage (Parallel) | 1.3 | % | ISO 294-4, 2577 |
| Mold Shrinkage (Normal) | 1.5 | % | ISO 294-4, 2577 |
Regulatory & Compliance
Certifications & Compliance
Technical Details & Test Data
Viscosity vs Shear Rate
Shear Stress vs Shear Rate
Dynamic Shear Modulus vs Temperature
Stress vs Strain
Secant Modulus vs Strain
Specific Volume Temperature (pvT)
Packaging & Availability
Country Availability
Regional Availability
Delrin® 100T NC010
DuPont