Delrin® 100TE is a toughened, high viscosity acetal homopolymer with very low VOC emissions for applications in automotive interiors. Processing methods include injection molding.
Polymer Name: Polyacetal Homopolymer (POM)
Processing Methods: Injection Molding, Extrusion
Additives Included: Mold Release Agent, Lubricant (Unspecified)
Flexural Modulus: 1850.0 MPa
Start Order
SecureOrder Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
View
Popular DuPont Products
View All DuPont Products Delrin® 300TE BK602
Delrin® 500AL NC010
Delrin® 570 NC000
Knowde Enhanced TDS
Identification & Functionality
Additives Included
Polymer Name
Plastics & Elastomers Functions
Technologies
Product Families
Delrin® 100TE NC010 Features & Benefits
Product Highlights
• Toughened, high viscosity resin
• Outstanding impact resistance and good moldability
• Good friction partner in gear applications
• Designed for highly stressed parts where outstanding toughness is required
Applications & Uses
Markets
Applications
Plastics & Elastomers End Uses
Plastics & Elastomers Processing Methods
Properties
Mechanical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 1850 | MPa | ISO 527-1/-2 |
| Yield Stress | 54 | MPa | ISO 527-1/-2 |
| Yield Strain | 26 | % | ISO 527-1/-2 |
| Nominal Strain (at Break) | min. 50 | % | ISO 527-1/-2 |
| Poisson's Ratio | 0.41 | - | - |
| Flexural Stress (at 3.5%) | 51 | MPa | ISO 178 |
| Charpy Impact Strength (at 23°C) | N | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (at -30°C) | N | kJ/m² | ISO 179/1eU |
| Notched Charpy Impact Strength (at 23°C) | 24 | kJ/m² | ISO 179/1eA |
| Notched Charpy Impact Strength (at -30°C) | 13 | kJ/m² | ISO 179/1eA |
| Hardness (Rockwell Scale M) | 64.6 | - | ISO 2039-2 |
| Hardness (Rockwell Scale R) | 113 | - | ISO 2039-2 |
Thermal Properties
| Value | Units | Test Method / Conditions | |
| Melt Temperature (at 10°C/min) | 178 | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.8 Mpa) | 71 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 Mpa) | 126 | °C | ISO 75-1/-2 |
| Vicat Softening Temperature (at 50°C/H 10N) | 173 | °C | ISO 306 |
| Coefficient of Linear Thermal Expansion (Parallel) | 120 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (Normal) | 120 | E-6/K | ISO 11359-1/-2 |
Flammability
| Value | Units | Test Method / Conditions | |
| FMVSS Class | B | - | ISO 3795 (FMVSS 302) |
| Burning Rate (at 1mm Thickness) | 42 | mm/min | ISO 3795 (FMVSS 302) |
Other Properties
| Value | Units | Test Method / Conditions | |
| Humidity Absorption (at 2mm) | 0.3 | % | Sim. to ISO 62 |
| Water Absorption (at 2mm) | 0.8 | % | Sim. to ISO 62 |
| Density | 1370 | kg/m³ | ISO 1183 |
| Density of Melt | 1160 | kg/m³ | - |
Processing Information (Extrusion)
| Value | Units | Test Method / Conditions | |
| Melt Temperature Range | 195 - 205 | °C | - |
| Melt Temperature (Optimum) | 200 | °C | - |
| Drying Time (Dehumidified Dryer) | 2 - 4 | h | - |
| Drying Temperature | 75 - 85 | °C | - |
| Processing Moisture Content | max. 0.05 | % | - |
Processing Information (Injection Molding)
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 80 | °C | - |
| Drying Recommended | yes | - | - |
| Drying Time (Dehumidified Dryer) | 4 - 8 | h | - |
| Processing Moisture Content | max. 0.05 | % | - |
| Hold Pressure Range | 60 - 80 | MPa | - |
| Hold Pressure Time | 7.5 | s/mm | - |
| Annealing Temperature | 160 | °C | - |
| Melt Temperature (Optimum) | 205 | °C | - |
| Melt Temperature (Minimum) | 200 | °C | - |
| Melt Temperature (Maximum) | 210 | °C | - |
| Maximum Screw Tangential Speed | 0.2 | m/s | - |
| Mold Temperature (Optimum) | 50 | °C | - |
| Mold Temperature (Minimum) | 40 | °C | - |
| Mold Temperature (Maximum) | 60 | °C | - |
| Annealing Time (Optional) | 30 | min/mm | - |
VDA Properties
| Value | Units | Test Method / Conditions | |
| Emissions | max. 2 | mg/kg | VDA 275 |
Rheological Properties
| Value | Units | Test Method / Conditions | |
| Melt Volume-Flow Rate (at 190°C, 2.16 kg) | 2 | cm³/10min | ISO 1133 |
| Melt Mass Flow Rate (at 190°C, 2.16 kg) | 2.2 | g/10min | ISO 1133 |
| Mold Shrinkage (Parallel) | 1.3 | % | ISO 294-4, 2577 |
| Mold Shrinkage (Normal) | 1.5 | % | ISO 294-4, 2577 |
Regulatory & Compliance
Technical Details & Test Data
Viscosity vs Shear Rate
Shear Stress vs Shear Rate