Delrin® 300TE BK602
Sold by DuPont
Delrin® 300TE is a toughened medium-high viscosity acetal homopolymer for injection molding with very low VOC emissions for applications in automotive interiors.
Polymer Name: Polyacetal Homopolymer (POM)
Processing Methods: Extrusion, Sheet, Plaques & Profiles Extrusion, Injection Molding
Additives Included: Mold Release Agent, Lubricant (Unspecified)
Flexural Modulus: 2000.0 MPa
Start Order
SecureOrder Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
Quote required
Similar Products from DuPont NEW
TypeDocument Name
Brochure
Technology Profile Laser Welding
Technology Profile Laser Welding
BrochureOther
Hot Runner Manual for Robust Molding of Semi-crystalline Resins
Hot Runner Manual for Robust Molding of Semi-crystalline Resins
OtherOther
DuPont™ Delrin® Drives Productivity and Sustainability for High Speed Filling Lines
DuPont™ Delrin® Drives Productivity and Sustainability for High Speed Filling Lines
OtherOther
Safety Restraint Systems
Safety Restraint Systems
OtherOther
DuPont SVHC Statement - Delrin®, Elvamide®, Minlon®, Rynite®, Vamac®
DuPont SVHC Statement - Delrin®, Elvamide®, Minlon®, Rynite®, Vamac®
OtherOther
Delrin® Acetal Homopolymer Resin Molding Tips
Delrin® Acetal Homopolymer Resin Molding Tips
OtherOther
Delrin® acetal resin Molding Guide
Delrin® acetal resin Molding Guide
OtherBrochure
Delrin® E-Grades for Low Emissions
Delrin® E-Grades for Low Emissions
BrochureBrochure
Electrical/Electronic Thermoplastic Encapsulation
Electrical/Electronic Thermoplastic Encapsulation
BrochureOther
General Design Principles - Module I: Chapter 8
General Design Principles - Module I: Chapter 8
OtherOther
Delrin® vs Acetal Copolymer White Paper
Delrin® vs Acetal Copolymer White Paper
OtherBrochure
DuPont Performance Polymers - Self Tapping Screws
DuPont Performance Polymers - Self Tapping Screws
BrochureKnowde Enhanced TDS
Identification & Functionality
Additives Included
Polymer Name
Plastics & Elastomers Functions
Technologies
Product Families
Delrin® 300TE BK602 Features & Benefits
Product Highlights
• Toughened, medium-high viscosity
• Very good balance of melt flow and impact properties
• Low noise properties
Applications & Uses
Markets
Applications
Plastics & Elastomers End Uses
Plastics & Elastomers Processing Methods
Properties
Mechanical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 2000 | MPa | ISO 527 |
| Hardness, Rockwell | 69 | Scale M | ISO 2039-2 |
| Hardness, Rockwell | 116 | Scale R | ISO 2039-2 |
| Yield Stress | 54 | MPa | ISO 527-1/-2 |
| Yield Strain | 20 | % | ISO 527-1/-2 |
| Strain at Break (50 mm/min) | 29 | % | ISO 527-1/-2 |
| Flexural Modulus | 2000 | MPa | ASTM D 790 |
| Flexural Stress at 3.5% | 55 | MPa | ISO 178 |
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m2 | ISO 179/1eA |
| Charpy Notched Impact Strength (-30°C) | 8 | kJ/m2 | ISO 179/1eA |
| Poisson's Ratio | 0.4 | - | ASTM E 132 |
Physical Properties
| Value | Units | Test Method / Conditions | |
| Melt Mass Flow Rate - MFR (190°C/2.16 kg) | 6 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Parallel | 1.3 | % | ISO 294-4, 2577 |
| Molding Shrinkage - Normal | 1.5 | % | ISO 294-4, 2577 |
Thermal Properties
| Value | Units | Test Method / Conditions | |
| Temperature of Deflection Under Load(1.8 MPa) | 78 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 136 | °C | ISO 75-1/-2 |
| Vicat Softening Temperature (50°C/h, 10N) | 172 | °C | ISO 306 |
| Coefficient of Linear Thermal Expansion - Parallel | 110 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion - Normal | 120 | E-6/K | ISO 11359-1/-2 |
Flammability
| Value | Units | Test Method / Conditions | |
| FMVSS Class | B | - | ISO 3795 (FMVSS 302) |
| Burning Rate (1 mm, Thickness) | max. 80 | mm/min | ISO 3795 (FMVSS 302) |
Other Properties
| Value | Units | Test Method / Conditions | |
| Density | 1370 | kg/m³ | ISO 1183 |
| Density of Melt | 1150 | kg/m³ | - |
Processing Information (Extrusion)
| Value | Units | Test Method / Conditions | |
| Melt Temperature Range | 195 - 205 | °C | - |
| Melt Temperature Optimum | 200 | °C | - |
| Drying Time (Dehumidified Dryer) | 2.0 - 4.0 | h | - |
| Drying Temperature | 75 - 85 | °C | - |
| Processing Moisture Content | ≤0.05 | % | - |
Processing Information (Injection Molding)
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 80 | °C | - |
| Drying Recommended | Yes | - | - |
| Drying Time (Dehumidified Dryer) | 4.0 - 8.0 | h | - |
| Processing Moisture Content | ≤0.05 | % | - |
| Melt Temperature Optimum | 205 | °C | - |
| Min. Melt Temperature | 200 | °C | - |
| Max. Melt Temperature | 210 | °C | - |
| Mold Temperature Optimum | 50 | °C | - |
| Min. Mold Temperature | 40 | °C | - |
| Max. Mold Temperature | 60 | °C | - |
| Hold Pressure Range | 60 - 80 | MPa | - |
| Hold Pressure Time | 7.5 | s/mm | - |
| Annealing Time - Optional | 30 | min/mm | - |
| Annealing Temperature | 160 | °C | - |
VDA Properties
| Value | Units | Test Method / Conditions | |
| Emissions | max. 2 | mg/100g/kg/100g | VDA 275 |
Technical Details & Test Data
Viscosity vs Shear Rate
Shear Stress vs Shear Rate
Specific Volume Temperature (pvT)
Packaging & Availability
Country Availability
Regional Availability
Delrin® 300TE BK602
DuPont