Delrin® 510GR is a 10% glass-reinforced acetal homopolymer for injection molding. It has high strength, stiffness, and high deflection temperature and excellent creep resistance.
Polymer Name: Polyacetal Homopolymer (POM)
Processing Methods: Injection Molding
Fillers Included: Glass Fiber
Additives Included: Mold Release Agent
Flexural Modulus: 5250.0 MPa
Start Order
SecureOrder Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
Quote required
Popular DuPont Products
View All DuPont Products Delrin® 300TE BK602
Delrin® 500AL NC010
Delrin® 570 NC000
Knowde Enhanced TDS
Identification & Functionality
Additives Included
Fillers Included
Polymer Name
Plastics & Elastomers Functions
Technologies
Product Families
Delrin® 510GR NC000 Features & Benefits
Applications & Uses
Markets
Applications
Plastics & Elastomers End Uses
Plastics & Elastomers Processing Methods
Properties
Mechanical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 5500 | MPa | ISO 527-1/-2 |
| Flexural Modulus | 5250 | MPa | ISO 178 |
| Flexural Strength | 175 | MPa | ISO 178 |
| Stress (at Break) | 105 | MPa | ISO 527-1/-2 |
| Strain (at Break) | 3.7 | % | ISO 527-1/-2 |
| Flexural Stress (at 3.5%) | 160 | MPa | ISO 178 |
| Tensile Creep Modulus (1h) | 4800 | MPa | ISO 899-1 |
| Tensile Creep Modulus (1000h) | 3500 | MPa | ISO 899-1 |
| Poisson's Ratio | 0.35 | - | - |
| Charpy Impact Strength (at 23°C) | 50 | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (at -30°C) | 50 | kJ/m² | ISO 179/1eU |
| Notched Charpy Impact Strength (at 23°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Notched Charpy Impact Strength (at -30°C) | 5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (at 23°C) | 5 | kJ/m² | ISO 180/1A |
| Hardness (Rockwell Scale M) | 100 | - | ISO 2039-2 |
| Hardness (Rockwell Scale R) | 122 | - | ISO 2039-2 |
Typical Properties
| Value | Units | Test Method / Conditions | |
| Resin Identification | POM-GF10 | - | ISO 1043 |
Thermal Properties
| Value | Units | Test Method / Conditions | |
| Melt Temperature (at 10°C/min) | 178 | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.8 Mpa) | 164 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 Mpa) | 174 | °C | ISO 75-1/-2 |
| Vicat Softening Temperature (at 50°C/H 50N) | 160 | °C | ISO 306 |
| Coefficient of Linear Thermal Expansion (Parallel) | 70 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (Normal) | 100 | E-6/K | ISO 11359-1/-2 |
| Relative Thermal Index (Electrical, 0.75mm) | 50 | °C | UL 746B |
| Relative Thermal Index (Impact, 0.75mm) | 50 | °C | UL 746B |
| Relative Thermal Index (Strength, 0.75mm) | 50 | °C | UL 746B |
Electrical Properties
| Value | Units | Test Method / Conditions | |
| Relative Permittivity (at 100Hz) | 3.7 | - | IEC 62631-2-1 |
| Relative Permittivity (at 1MHz) | 3.9 | - | IEC 62631-2-1 |
| Comparative Tracking Index | 600 | - | IEC 60112 |
| Volume Resistivity | 100000000000 | Ohm.m | IEC 62631-3-1 |
Flammability
| Value | Units | Test Method / Conditions | |
| FMVSS Class | B | - | ISO 3795 (FMVSS 302) |
| Burning Behavior (at 0.75mm Thickness) | UL94 HB | class | IEC 60695-11-10 |
| Burning Rate (at 1mm Thickness) | 46 | mm/min | ISO 3795 (FMVSS 302) |
Other Properties
| Value | Units | Test Method / Conditions | |
| Humidity Absorption (at 2mm) | 0.16 | % | Sim. to ISO 62 |
| Water Absorption (at 2mm) | 1.1 | % | Sim. to ISO 62 |
| Density | 1490 | kg/m³ | ISO 1183 |
Processing Information (Injection Molding)
| Value | Units | Test Method / Conditions | |
| Drying Recommended | yes | - | - |
| Drying Temperature | 80 | °C | - |
| Drying Time (Dehumidified Dryer) | 2 - 4 | h | - |
| Processing Moisture Content | max. 0.2 | % | - |
| Hold Pressure Range | 80 - 100 | MPa | - |
| Hold Pressure Time | 8 | s/mm | - |
| Annealing Temperature | 160 | °C | - |
| Melt Temperature (Optimum) | 215 | °C | - |
| Melt Temperature (Minimum) | 210 | °C | - |
| Melt Temperature (Maximum) | 220 | °C | - |
| Maximum Screw Tangential Speed | 0.3 | m/s | - |
| Mold Temperature (Optimum) | 90 | °C | - |
| Mold Temperature (Minimum) | 80 | °C | - |
| Mold Temperature (Maximum) | 100 | °C | - |
| Annealing Time (Optional) | 30 | min/mm | - |
VDA Properties
| Value | Units | Test Method / Conditions | |
| Fogging (G-Value, Condensate) | 0.65 | mg | ISO 6452 |
Rheological Properties
| Value | Units | Test Method / Conditions | |
| Melt Volume-Flow Rate (at 190°C, 2.16 kg) | 12 | cm³/10min | ISO 1133 |
| Mold Shrinkage (Parallel) | 1 | % | ISO 294-4, 2577 |
| Mold Shrinkage (Normal) | 1.4 | % | ISO 294-4, 2577 |
Regulatory & Compliance
Certifications & Compliance
Technical Details & Test Data
Stress vs Strain
Secant Modulus vs Strain
Packaging & Availability
Country Availability
Regional Availability
Delrin® 510GR NC000
DuPont