Delrin® 911DP NC010

Sold by DuPont
Polymer Name: Polyacetal Homopolymer (POM)
Processing Methods: Extrusion, Sheet, Plaques & Profiles Extrusion, Injection Molding
Additives Included: Mold Release Agent, Lubricant (Unspecified)
Flexural Modulus: 3300.0 MPa
Start Order
Secure
Order Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
View
Similar Products from DuPont NEW

Knowde Enhanced TDS

Expand All

+

Identification & Functionality

Delrin® 911DP NC010 Features & Benefits

Applications & Uses

Properties

Color
Flame Rating
Physical Form
Part Marking Code
>POM<
Resin ID
POM
Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Modulus3400MPaISO 527
Yield Stress75MPaISO 527-1/-2
Yield Strain10%ISO 527-1/-2
Nominal Strain at Break20%ISO 527-1/-2
Flexural Modulus3300MPaASTM D 790
Flexural Stress at 3.5%90MPaISO 178
Charpy Impact Strength (23°C)160kJ/m²ISO 179/1eU
Charpy Impact Strength (-30°C)150kJ/m2ISO 179/1eU
Charpy Notched Impact Strength (23°C)6.5kJ/m2ISO 179/1eA
Charpy Notched Impact Strength (-30°C)6kJ/m2ISO 179-1/1eA
Ball Indentation Hardness (H 961/30)175DSMPaISO 2039-1
Poisson's Ratio0.37-ASTM D638
Physical Properties
ValueUnitsTest Method / Conditions
Melt Volume - Flow Rate21cm³/10minISO 1133
Melt Mass Flow Rate - MFR (190°C/2.16 kg)24g/10 minASTM D1238
Load2.16kgISO 1133
Molding Shrinkage - Parallel1.9%ISO 294-4, 2577
Molding Shrinkage - Normal1.8%ISO 294-4, 2577
Temperature190°CISO 1133
Thermal Properties
ValueUnitsTest Method / Conditions
Melting Temperature (10°C/min)178°CISO 11357-1/-3
Temperature of Deflection Under Load(1.8 MPa)108°CISO 75-1/-2
Temperature of Deflection Under Load (0.45 MPa)163°CISO 75-1/-2
Coefficient of Linear Thermal Expansion - Parallel100E-6/KISO 11359-1/-2
Coefficient of Linear Thermal Expansion - Normal100E-6/KISO 11359-1/-2
Relative Temperature Index - Electrical (0.75 mm)50°CUL 746B
Relative Temperature Index - Electrical (1.5 mm)110°CUL 746B
Relative Temperature Index - Electrical (3 mm)110°CUL 746B
Relative Temperature Index - Impact (0.75 mm)50°CUL 746B
Relative Temperature Index - Impact (1.5 mm)85°CUL 746B
Relative Temperature Index - Impact (3 mm)90°CUL 746B
Relative Temperature Index - Strength (0.75 mm)50°CUL 746B
Relative Temperature Index - Strength (1.5 mm)90°CUL 746B
Relative Temperature Index - Strength (3 mm)95°CUL 746B
Flammability
ValueUnitsTest Method / Conditions
Burning Behaviour (1.5 mm, Nominal Thickness)HBclassIEC 60695-11-10
Burning Behaviour (Thickness h)HBclassIEC 60695-11-10
FMVSS ClassB-ISO 3795 (FMVSS 302)
Burning Rate (1 mm, Thickness)25mm/minISO 3795 (FMVSS 302)
Ul RecognitionYes-UL 94
Thickness Tested1.5mmIEC 60695-11-10
Other Properties
ValueUnitsTest Method / Conditions
Humidity Absorption (2 mm)0.2%Sim. to ISO 62
Water Absorption (2 mm)0.9%Sim. to ISO 62
Density1420kg/m³ISO 1183
Processing Information (Extrusion)
ValueUnitsTest Method / Conditions
Melt Temperature Range195 - 205°C-
Processing Moisture Content≤0.2%-
Melt Temperature Optimum200°C-
Drying Time (Dehumidified Dryer)2.0 - 4.0h-
Drying Temperature75 - 85°C-
Processing Information (Injection Molding)
ValueUnitsTest Method / Conditions
Drying Temperature80°C-
Drying RecommendedYes--
Drying Time (Dehumidified Dryer)2.0 - 4.0h-
Processing Moisture Content≤0.2%-
Melt Temperature Optimum215°C-
Min. Melt Temperature210°C-
Max. Melt Temperature220°C-
Mold Temperature Optimum90°C-
Min. Mold Temperature80°C-
Max. Mold Temperature100°C-
Hold Pressure Range80 - 100MPa-
Hold Pressure Time7.5s/mm-
Annealing Time - Optional30min/mm-
Annealing Temperature160°C-
VDA Properties
ValueUnitsTest Method / Conditions
Fogging - F Value (Refraction)97%ISO 6452
Fogging, G - Value (Condensate)0.1mgISO 6452
Emissionsmax. 8mg/100g/kg/100gVDA 275

Regulatory & Compliance

Certifications & Compliance
Compliance
UL Flame Rated

Technical Details & Test Data

Stress vs Strain

DuPont Delrin 911DP NC010 Stress vs Strain