Delrin® FG900P is a general purpose low viscosity acetal homopolymer for multicavity and thin wall molding with improved processing thermal stability. It has been developed for applications in contact with food. This product is manufactured according to Good Manufacturing Practice (GMP) principles and generally accepted in food contact applications in Europe and the USA when meeting applicable use conditions.
Polymer Name: Polyacetal Homopolymer (POM)
Processing Methods: Injection Molding
Additives Included: Mold Release Agent, Lubricant (Unspecified)
Flexural Modulus: 3000.0 MPa
Start Order
SecureOrder Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
View
Popular DuPont Products
View All DuPont Products Delrin® 111PA NC010
Delrin® SC698 NC010
Delrin® FG511DP NC010
Knowde Enhanced TDS
Identification & Functionality
Additives Included
Polymer Name
Plastics & Elastomers Functions
Technologies
Product Families
Delrin® FG900P NC010 Features & Benefits
Labeling Claims
Materials Features
Applications & Uses
Markets
Plastics & Elastomers End Uses
Plastics & Elastomers Processing Methods
Properties
Chemical Resistance
Color
Flame Rating
Part Marking Code
Mechanical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 3300 | MPa | ISO 527-1/-2 |
| Yield Stress | 71 | MPa | ISO 527-1/-2 |
| Yield Strain | 12 | % | ISO 527-1/-2 |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Nominal Strain (at Break) | 23 | % | ISO 527-1/-2 |
| Poisson's Ratio | 0.37 | - | - |
| Tensile Creep Modulus (1h) | 2800 | MPa | ISO 899-1 |
| Tensile Creep Modulus (1000h) | 1500 | MPa | ISO 899-1 |
| Charpy Impact Strength (at 23°C) | 200 | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (at -30°C) | 200 | kJ/m² | ISO 179/1eU |
| Notched Charpy Impact Strength (at 23°C) | 8 | kJ/m² | ISO 179/1eA |
| Notched Charpy Impact Strength (at -30°C) | 7 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (at 23°C) | 7 | kJ/m² | ISO 180/1A |
| Notched Izod Impact Strength (at -40°C) | 8 | kJ/m² | ISO 180/1A |
| Hardness (Rockwell Scale M) | 92 | - | ISO 2039-2 |
| Hardness (Rockwell Scale R) | 120 | - | ISO 2039-2 |
Typical Properties
| Value | Units | Test Method / Conditions | |
| Resin Identification | POM | - | ISO 1043 |
Thermal Properties
| Value | Units | Test Method / Conditions | |
| Melt Temperature (at 10°C/min) | 178 | °C | ISO 11357-1/-3 |
| Temperature of Deflection Under Load (1.8 Mpa) | 94 | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 Mpa) | 162 | °C | ISO 75-1/-2 |
| Vicat Softening Temperature (at 50°C/H 50N) | 160 | °C | ISO 306 |
| Coefficient of Linear Thermal Expansion (Parallel) | 120 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (Normal) | 120 | E-6/K | ISO 11359-1/-2 |
| Relative Thermal Index (Electrical, 0.75mm) | 50 | °C | UL 746B |
| Relative Thermal Index (Electrical, 1.5mm) | 110 | °C | UL 746B |
| Relative Thermal Index (Electrical, 3mm) | 110 | °C | UL 746B |
| Relative Thermal Index (Impact, 0.75mm) | 50 | °C | UL 746B |
| Relative Thermal Index (Impact, 1.5mm) | 85 | °C | UL 746B |
| Relative Thermal Index (Impact, 3mm) | 90 | °C | UL 746B |
| Relative Thermal Index (Strength, 0.75mm) | 50 | °C | UL 746B |
| Relative Thermal Index (Strength, 1.5mm) | 90 | °C | UL 746B |
| Relative Thermal Index (Strength, 3mm) | 95 | °C | UL 746B |
Flammability
| Value | Units | Test Method / Conditions | |
| Burning Behavior (at 1.5mm Nominal Thickness) | UL94 HB | class | IEC 60695-11-10 |
| Burning Behavior (at 0.8mm Thickness h) | UL94 HB | class | IEC 60695-11-10 |
| Hot Wire Ignition (at 0.75mm) | 8 | s | UL 746A |
Other Properties
| Value | Units | Test Method / Conditions | |
| Humidity Absorption (at 2mm) | 0.4 | % | Sim. to ISO 62 |
| Water Absorption (at 2mm) | 1.4 | % | Sim. to ISO 62 |
| Density | 1420 | kg/m³ | ISO 1183 |
Processing Information (Injection Molding)
| Value | Units | Test Method / Conditions | |
| Drying Recommended | yes | - | - |
| Drying Temperature | 80 | °C | - |
| Drying Time (Dehumidified Dryer) | 2 - 4 | h | - |
| Processing Moisture Content | max. 0.2 | % | - |
| Hold Pressure Range | 80 - 100 | MPa | - |
| Hold Pressure Time | 8 | s/mm | - |
| Annealing Temperature | 160 | °C | - |
| Melt Temperature (Optimum) | 215 | °C | - |
| Melt Temperature (Minimum) | 210 | °C | - |
| Melt Temperature (Maximum) | 220 | °C | - |
| Maximum Screw Tangential Speed | 0.3 | m/s | - |
| Mold Temperature (Optimum) | 90 | °C | - |
| Mold Temperature (Minimum) | 80 | °C | - |
| Mold Temperature (Maximum) | 100 | °C | - |
| Annealing Time (Optional) | 30 | min/mm | - |
VDA Properties
| Value | Units | Test Method / Conditions | |
| Fogging (F-Value, Refraction) | 95 | % | ISO 6452 |
| Fogging (G-Value, Condensate) | 0.2 | mg | ISO 6452 |
| Emissions | max. 8 | mg/kg | VDA 275 |
Rheological Properties
| Value | Units | Test Method / Conditions | |
| Melt Volume-Flow Rate (at 190°C, 2.16 kg) | 21 | cm³/10min | ISO 1133 |
| Melt Mass Flow Rate (at 190°C, 2.16 kg) | 25 | g/10min | ISO 1133 |
| Mold Shrinkage (Parallel) | 1.9 | % | ISO 294-4, 2577 |
| Mold Shrinkage (Normal) | 1.9 | % | ISO 294-4, 2577 |
Chemical Resistance
| Chemical Type | Chemical Name | Resistance |
| Acids | Acetic Acid (5% by mass) (23°C) | Probably Resistant |
| Acids | Chromic Acid solution (40% by mass) (23°C) | Not Recommended |
| Acids | Citric Acid solution (10% by mass) (23°C) | Not Recommended |
| Acids | Hydrochloric Acid (36% by mass) (23°C) | Not Recommended |
| Acids | Lactic Acid (10% by mass) (23°C) | Not Recommended |
| Acids | Nitric Acid (40% by mass) (23°C) | Not Recommended |
| Acids | Sulfuric Acid (38% by mass) (23°C) | Not Recommended |
| Acids | Sulfuric Acid (5% by mass) (23°C) | Not Recommended |
| Alcohols | Ethanol (23°C) | Probably Resistant |
| Alcohols | Isopropyl alcohol (23°C) | Probably Resistant |
| Alcohols | Methanol (23°C) | Probably Resistant |
| Bases | Ammonium Hydroxide solution (10% by mass) (23°C) | Not Recommended |
| Bases | Sodium Hydroxide solution (1% by mass) (23°C) | Not Recommended |
| Bases | Sodium Hydroxide solution (35% by mass) (23°C) | Not Recommended |
| Ethers | Diethyl ether (23°C) | Probably Resistant |
| Hydrocarbons | iso-Octane (23°C) | Probably Resistant |
| Hydrocarbons | n-Hexane (23°C) | Probably Resistant |
| Hydrocarbons | Toluene (23°C) | Probably Resistant |
| Ketones | Acetone (23°C) | Probably Resistant |
| Mineral oils | Insulating Oil (23°C) | Probably Resistant |
| Mineral oils | SAE 10W40 multigrade motor oil (130°C) | Not Recommended |
| Mineral oils | SAE 10W40 multigrade motor oil (23°C) | Probably Resistant |
| Mineral oils | SAE 80/90 hypoid-gear oil (130°C) | Not Recommended |
| Other | 1% nonylphenoxy-polyethyleneoxy ethanol in water (23°C) | Probably Resistant |
| Other | 50% Oleic acid + 50% Olive Oil (23°C) | Probably Resistant |
| Other | DOT No. 4 Brake fluid (130°C) | Not Recommended |
| Other | Ethyl Acetate (23°C) | Probably Resistant |
| Other | Ethylene Glycol (50% by mass) in water (108°C) | Not Recommended |
| Other | Hydrogen peroxide (23°C) | Not Recommended |
| Other | Phenol solution (5% by mass) (23°C) | Not Recommended |
| Other | Water (23°C) | Probably Resistant |
| Other | Water (90°C) | Not Recommended |
| Salt solutions | Sodium Carbonate solution (2% by mass) (23°C) | Not Recommended |
| Salt solutions | Sodium Carbonate solution (20% by mass) (23°C) | Not Recommended |
| Salt solutions | Sodium Chloride solution (10% by mass) (23°C) | Probably Resistant |
| Salt solutions | Sodium Hypochlorite solution (10% by mass) (23°C) | Not Recommended |
| Salt solutions | Zinc Chloride solution (50% by mass) (23°C) | Not Recommended |
| Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (>90°C) | Not Recommended |
| Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (23°C) | Probably Resistant |
| Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (90°C) | Not Recommended |
| Standard Fuels | ISO 1817 Liquid 1 - E5 (60°C) | Probably Resistant |
| Standard Fuels | ISO 1817 Liquid 2 - M15E4 (60°C) | Probably Resistant |
| Standard Fuels | ISO 1817 Liquid 3 - M3E7 (60°C) | Probably Resistant |
| Standard Fuels | ISO 1817 Liquid 4 - M15 (60°C) | Probably Resistant |
| Standard Fuels | Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23°C) | Probably Resistant |
| Standard Fuels | Standard fuel without alcohol (pref. ISO 1817 Liquid C) (23°C) | Probably Resistant |
Regulatory & Compliance
Certifications & Compliance
Technical Details & Test Data
Viscosity vs Shear Rate
Shear Stress vs Shear Rate
Dynamic Shear Modulus vs Temperature
Stress vs Strain
Secant Modulus vs Strain
Packaging & Availability
Country Availability
Regional Availability
Delrin® FG900P NC010
DuPont