Kalrez® 4079 perfluoroelastomer parts are a low compression set product for general purpose use in O-rings, diaphragms, seals and other parts used in the chemical process and aircraft industries. It is a carbon black filled product with excellent chemical resistance, good mechanical properties, and outstanding hot air aging properties. It exhibits low swell in organic acids, inorganic acids and aldehydes, and has good response to temperature cycling effects. A maximum service temperature of 316°C (600°F) is suggested, with short excursions to higher temperatures possible. Kalrez® 4079 is not recommended for use in hot water/steam applications or in contact with certain hot aliphatic amines, ethylene oxide, or propylene oxide.
Kalrez® 4079
Kalrez® 4079 perfluoroelastomer parts are a low compression set product for general purpose use in O-rings, diaphragms, seals and other parts used in the chemical process and aircraft industries. It is a carbon black filled product with excellent chemical resistance, good mechanical properties, and outstanding hot air aging properties. It exhibits low swell in organic acids, inorganic acids and aldehydes, and has good response to temperature cycling effects. A maximum service temperature of 316°C (600°F) is suggested, with short excursions to higher temperatures possible. Kalrez® 4079 is not recommended for use in hot water/steam applications or in contact with certain hot aliphatic amines, ethylene oxide, or propylene oxide.
Take Action
Knowde Enhanced TDS
Identification & Functionality
Chemical Family
Fillers Included
Parts & Shapes Type
Polymer Name
Technologies
Product Families
Features & Benefits
Product Highlights
- Good response to temperature cycling effects
- Outstanding hot air aging properties
- It exhibits low swell in organic and inorganic acids
Performance Characteristics
Figure 1 : Compression set at 204°C
Figure 2 : Sealing force retention at 204°C
Figure 3 : Performance Comparison
Applications & Uses
Plastics & Elastomers End Uses
Properties
Typical Properties
Value | Units | Test Method / Conditions | |
Compression Set (70 hr at 204°C (400 °F)) | 14 | % | ASTM D395B |
Compression Set (70 hr, 204°C, 400°F) | 14 | % | ASTM D395B |
Lowest Service Temperature | -19 (-2.2) | °C (°F) | |
Color | Black | ||
Hardness | 75 | Shore A | ASTM D2240 |
100% Modulus | 7.24 (1050) | MPa (psi) | ASTM D412 |
Hardness - Shore A | 75 | ASTM D2240 | |
Maximum Service Temperature | 316 (600) | °C (°F) | |
Elongation at Break | 150 | % | ASTM D412 |
Tensile Strength at Break | 16.88 (2450) | MPa (psi) | ASTM D412 |
Color
Black
Fillers
Carbon Black