Company logo

Zytel® 101 NC010

Sold by DuPont
Polymer Name: Polyamide 66 (PA 66)
Processing Methods: Injection Molding, Extrusion
Flexural Modulus: 2800.0 MPa
Start Order
Secure
Order Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
View

Knowde Enhanced TDS

Expand All

+

Identification & Functionality

Chemical Family
Plastics & Elastomers Functions
Technologies

Zytel® 101 NC010 Features & Benefits

Materials Features
General Purpose

Applications & Uses

Properties

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Modulus3100/1400MPaISO 527-1/-2
Abrasion Resistance6/*mm³ISO 4649
Yield Stress82/55MPaISO 527-1/-2
Yield Strain4.5/25%ISO 527-1/-2
Flexural Modulus2800/1200MPaISO 178
Flexural Strength90/54MPaISO 178
Nominal Strain (at Break)25/min. 50%ISO 527-1/-2
Strain (at Break, 50mm/min)45/-%ISO 527-1/-2
Tensile Creep Modulus (1h)*/1200MPaISO 899-1
Tensile Creep Modulus (1000h)*/700MPaISO 899-1
Charpy Impact Strength (at 23°C)N/NkJ/m²ISO 179/1eU
Charpy Impact Strength (at -30°C)400/NkJ/m²ISO 179/1eU
Ball Indentation Hardness (H 358/30)180/85MPaISO 2039-1
Notched Charpy Impact Strength (at 23°C)5.5/15kJ/m²ISO 179/1eA
Notched Charpy Impact Strength (at -30°C)4.5/3kJ/m²ISO 179/1eA
Ball Indentation Hardness (H 961/30)160/*MPaISO 2039-1
Notched Izod Impact Strength (at 23°C)5.5/12kJ/m²ISO 180/1A
Poisson's Ratio0.37/0.43--
Notched Izod Impact Strength (at -30°C)5.5/-kJ/m²ISO 180/1A
Notched Izod Impact Strength (at -40°C)5.5/-kJ/m²ISO 180/1A
Izod Impact Strength (at 23°C)N/NkJ/m²ISO 180/1U
Izod Impact Strength (at -30°C)300/-kJ/m²ISO 180/1U
Hardness (Rockwell Scale M)79/59-ISO 2039-2
Hardness (Rockwell Scale R)121/108-ISO 2039-2
Typical Properties
ValueUnitsTest Method / Conditions
Resin IdentificationPA66-ISO 1043
ISO DesignationISO 16396-PA66,,M1G1N,S14-030--
Thermal Properties
ValueUnitsTest Method / Conditions
Specific Heat Capacity of Melt2790J/(kg K)-
Melt Temperature (at 10°C/min)262/*°CISO 11357-1/-3
Glass Transition Temperature (at 10°C/min)65/40°CISO 11357-1/-2
Temperature of Deflection Under Load (1.8 Mpa)70/*°CISO 75-1/-2
Temperature of Deflection Under Load (0.45 Mpa)190/*°CISO 75-1/-2
Vicat Softening Temperature (at 50°C/H 50N)240/*°CISO 306
Coefficient of Linear Thermal Expansion (Parallel)100/*E-6/KISO 11359-1/-2
Coefficient of Linear Thermal Expansion (Normal)110/*E-6/KISO 11359-1/-2
Thermal Conductivity0.24W/(m K)ISO 22007-2
Specific Heat Capacity (Solid)1680J/(kg K)-
Relative Thermal Index (Electrical, 0.75mm)130°CUL 746B
Relative Thermal Index (Electrical, 1.5mm)130°CUL 746B
Relative Thermal Index (Electrical, 3mm)130°CUL 746B
Relative Thermal Index (Electrical, 6mm)130°CUL 746B
Relative Thermal Index (Impact, 0.75mm)75°CUL 746B
Relative Thermal Index (Impact, 1.5mm)75°CUL 746B
Relative Thermal Index (Impact, 3mm)75°CUL 746B
Relative Thermal Index (Impact, 6mm)75°CUL 746B
Relative Thermal Index (Strength, 0.75mm)85°CUL 746B
Relative Thermal Index (Strength, 1.5mm)85/*°CUL 746B
Relative Thermal Index (Strength, 3mm)85°CUL 746B
Relative Thermal Index (Strength, 6mm)85°CUL 746B
Thermal Conductivity of Melt0.16W/(m K)ISO 22007-2
Effective Thermal Diffusivity9.0e-08m²/s-
Film Properties
ValueUnitsTest Method / Conditions
Thickness of Specimen0.1/*mm-
Maximum Stress (Parallel)80/*MPaISO 527-3
Maximum Stress (Normal)75/*MPaISO 527-3
Maximum Strain (Parallel)300/*%ISO 527-3
Maximum Strain (Normal)250/*%ISO 527-3
Water Vapor Transmission Rate (at 23°C/85%R.H.)8/*g/(m²*d)DIS 15106-1/-2
Oxygen Transmission Rate (at 23°C/0%R.H.)12/*cm³/(m²*d*bar)DIS 15105-1/-2
Carbon Dioxide Transmission Rate (at 23°C/0%R.H.)45/*cm³/(m²*d*bar)DIS 15105-1/-2
Gloss (60°)90/*-ISO 2813
Haze0.02/*-ISO 14782
Electrical Properties
ValueUnitsTest Method / Conditions
Surface Resistivity*/1E12OhmIEC 62631-3-2
Electric Strength32/28kV/mmIEC 60243-1
Relative Permittivity (at 100Hz)3.8/6-IEC 62631-2-1
Relative Permittivity (at 1MHz)3.5/4-IEC 62631-2-1
Dissipation Factor (at 100 Hz)80/2100E-4IEC 62631-2-1
Dissipation Factor (at 1 MHz)180/750E-4IEC 62631-2-1
Comparative Tracking Index600/--IEC 60112
Comparative Tracking Index475/--IEC 60112
Dielectric Constant (at 1 GHz)3.1/--ASTM D 2520 B
Dielectric Constant (at 10 GHz)3/--ASTM D 2520 B
Volume Resistivity1E13/1E11Ohm.mIEC 62631-3-1
Flammability
ValueUnitsTest Method / Conditions
Oxygen Index28/*%ISO 4589-1/-2
FMVSS ClassDNI-ISO 3795 (FMVSS 302)
Burning Behavior (at 1.5mm/* Nominal Thickness)UL94 V-2/*classIEC 60695-11-10
Burning Behavior (at 0.71mm/* Thickness h)UL94 V-2/*classIEC 60695-11-10
Glow Wire Flammability Index (at 0.75mm)960/-°CIEC 60695-2-12
Glow Wire Flammability Index (at 1.5mm)960/-°CIEC 60695-2-12
Glow Wire Flammability Index (at 3mm)960/-°CIEC 60695-2-12
Glow Wire Ignition Temperature (at 0.75mm)725/-°CIEC 60695-2-13
Glow Wire Ignition Temperature (at 1.5mm)750/-°CIEC 60695-2-13
Glow Wire Ignition Temperature (at 3mm)800/-°CIEC 60695-2-13
Glow Wire Temperature (at 1mm, No Flame)805/-°CIEC 60335-1
Glow Wire Temperature (at 1.5mm, No Flame)775/-°CIEC 60335-1
Glow Wire Temperature (at 2mm, No Flame)700/-°CIEC 60335-1
Other Properties
ValueUnitsTest Method / Conditions
Humidity Absorption (at 2mm)2.6/*%Sim. to ISO 62
Water Absorption (at 2mm)8.5/*%Sim. to ISO 62
Water Absorption (Immersion 24h)1.2/*%Sim. to ISO 62
Density of Melt980kg/m³-
Density1140/-kg/m³ISO 1183
Processing Information (Extrusion)
ValueUnitsTest Method / Conditions
Melt Temperature Range275 - 290°C-
Processing Moisture Contentmax. 0.06%-
Melt Temperature (Optimum)285°C-
Drying Temperature80°C-
Drying Time (Dehumidified Dryer)4 - 6h-
VDA Properties
ValueUnitsTest Method / Conditions
Emission of Organic Compounds5µgC/gVDA 277
Odor3classVDA 270
Fogging (F-Value, Refraction)99/*%ISO 6452
Fogging (G-Value, Condensate)0.1/*mgISO 6452
Processing Information (Injection Molding)
ValueUnitsTest Method / Conditions
Drying Recommendedyes--
Drying Temperature80°C-
Drying Time (Dehumidified Dryer)2 - 4h-
Processing Moisture Contentmax. 0.2%-
Hold Pressure Range50 - 100MPa-
Hold Pressure Time4s/mm-
Ejection Temperature190°C-
Melt Temperature (Optimum)290°C-
Melt Temperature (Minimum)280°C-
Melt Temperature (Maximum)300°C-
Maximum Screw Tangential Speed0.4m/s-
Mold Temperature (Optimum)70°C-
Mold Temperature (Minimum)50°C-
Mold Temperature (Maximum)90°C-
Tribological Properties
ValueUnitsTest Method / Conditions
Coefficient of Static Friction (against Steel)-/0.2-ASTM 1894
Coefficient of Sliding Friction (1H against Steel)-/0.28-ASTM 1894
Rheological Properties
ValueUnitsTest Method / Conditions
Melt Mass Flow Rate (at 275°C/*, 2.16 kg/*)23/*g/10minISO 1133
Viscosity Number ¹150/*cm³/gISO 307, 1157, 1628
Mold Shrinkage (Parallel)1.4/-%ISO 294-4, 2577
Mold Shrinkage (Normal)1.4/-%ISO 294-4, 2577
Note
  • [1]: Sulfuric acid 96%
Chemical Resistance
Chemical Type Chemical Name Resistance
Acids Acetic Acid (5% by mass) (23°C) Probably Resistant
Acids Chromic Acid solution (40% by mass) (23°C) Not Recommended
Acids Citric Acid solution (10% by mass) (23°C) Probably Resistant
Acids Hydrochloric Acid (36% by mass) (23°C) Not Recommended
Acids Lactic Acid (10% by mass) (23°C) Probably Resistant
Acids Nitric Acid (40% by mass) (23°C) Not Recommended
Acids Sulfuric Acid (38% by mass) (23°C) Not Recommended
Acids Sulfuric Acid (5% by mass) (23°C) Not Recommended
Alcohols Ethanol (23°C) Probably Resistant
Alcohols Isopropyl alcohol (23°C) Probably Resistant
Alcohols Methanol (23°C) Probably Resistant
Bases Ammonium Hydroxide solution (10% by mass) (23°C) Probably Resistant
Bases Sodium Hydroxide solution (1% by mass) (23°C) Probably Resistant
Bases Sodium Hydroxide solution (35% by mass) (23°C) Not Recommended
Ethers Diethyl ether (23°C) Probably Resistant
Hydrocarbons iso-Octane (23°C) Probably Resistant
Hydrocarbons n-Hexane (23°C) Probably Resistant
Hydrocarbons Toluene (23°C) Probably Resistant
Ketones Acetone (23°C) Probably Resistant
Mineral oils Insulating Oil (23°C) Probably Resistant
Mineral oils SAE 10W40 multigrade motor oil (130°C) Not Recommended
Mineral oils SAE 10W40 multigrade motor oil (23°C) Probably Resistant
Mineral oils SAE 80/90 hypoid-gear oil (130°C) Not Recommended
Other 1% nonylphenoxy-polyethyleneoxy ethanol in water (23°C) Probably Resistant
Other 50% Oleic acid + 50% Olive Oil (23°C) Probably Resistant
Other DOT No. 4 Brake fluid (130°C) Not Recommended
Other Ethyl Acetate (23°C) Probably Resistant
Other Ethylene Glycol (50% by mass) in water (108°C) Not Recommended
Other Hydrogen peroxide (23°C) Not Recommended
Other Phenol solution (5% by mass) (23°C) Not Recommended
Other Water (23°C) Probably Resistant
Other Water (90°C) Not Recommended
Salt solutions Sodium Carbonate solution (2% by mass) (23°C) Probably Resistant
Salt solutions Sodium Carbonate solution (20% by mass) (23°C) Probably Resistant
Salt solutions Sodium Chloride solution (10% by mass) (23°C) Probably Resistant
Salt solutions Sodium Hypochlorite solution (10% by mass) (23°C) Not Recommended
Salt solutions Zinc Chloride solution (50% by mass) (23°C) Not Recommended
Standard Fuels Diesel fuel (pref. ISO 1817 Liquid F) (>90°C) Not Recommended
Standard Fuels Diesel fuel (pref. ISO 1817 Liquid F) (23°C) Probably Resistant
Standard Fuels Diesel fuel (pref. ISO 1817 Liquid F) (90°C) Not Recommended
Standard Fuels ISO 1817 Liquid 1 - E5 (60°C) Probably Resistant
Standard Fuels ISO 1817 Liquid 2 - M15E4 (60°C) Probably Resistant
Standard Fuels ISO 1817 Liquid 3 - M3E7 (60°C) Probably Resistant
Standard Fuels ISO 1817 Liquid 4 - M15 (60°C) Probably Resistant
Standard Fuels Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23°C) Probably Resistant
Standard Fuels Standard fuel without alcohol (pref. ISO 1817 Liquid C) (23°C) Probably Resistant

Regulatory & Compliance

Technical Details & Test Data

Stress vs Strain (Cond.)

DuPont Zytel 101 NC010 Stress vs Strain (Cond.)

Stress vs Strain (Dry)

DuPont Zytel 101 NC010 Stress vs Strain (Dry)

Secant Modulus vs Strain (Cond.)

DuPont Zytel 101 NC010 Secant Modulus vs Strain (Cond.)

Secant Modulus vs Strain (Dry)

DuPont Zytel 101 NC010 Secant Modulus vs Strain (Dry)

Stress vs Strain (Dry)-new

DuPont Zytel 101 NC010 Stress vs Strain (Dry)-new

Stress vs Strain (Dry)-New

DuPont Zytel 101 NC010 Stress vs Strain (Dry)-New

Secant Modulus vs Strain (Cond.)-New

DuPont Zytel 101 NC010 Secant Modulus vs Strain (Cond.)-New

Stress vs Strain (Cond.)-New

DuPont Zytel 101 NC010 Stress vs Strain (Cond.)-New

Packaging & Availability

Regional Availability

Zytel® 101 NC010
DuPont
Browse
Sample
Request
Search