Zytel® 70G33L NC010

Sold by DuPont
Polymer Name: Polyamide 66 (PA 66)
Processing Methods: Injection Molding
Fillers Included: Glass Fiber
Additives Included: Mold Release Agent, Lubricant (Unspecified)
Flexural Modulus: 9000.0 MPa
Start Order
Secure
Order Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
View

Knowde Enhanced TDS

Expand All

+

Identification & Functionality

Chemical Family
Fillers Included
Plastics & Elastomers Functions
Technologies

Zytel® 70G33L NC010 Features & Benefits

Applications & Uses

Properties

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Modulus10000/8000MPaISO 527-1/-2
Abrasion Resistance10/*mm³ISO 4649
Flexural Modulus9000/6000MPaISO 178
Flexural Strength290/200MPaISO 178
Compressive Strength240/-MPaISO 604
Shear Strength90/-MPaASTM D 732
Stress (at Break)200/140MPaISO 527-1/-2
Strain (at Break)3.5/5%ISO 527-1/-2
Tensile Creep Modulus (1h)*/8000MPaISO 899-1
Tensile Creep Modulus (1000h)*/5500MPaISO 899-1
Charpy Impact Strength (at 23°C)85/100kJ/m²ISO 179/1eU
Charpy Impact Strength (at -30°C)70/75kJ/m²ISO 179/1eU
Notched Charpy Impact Strength (at 23°C)13/17kJ/m²ISO 179/1eA
Notched Charpy Impact Strength (at -30°C)10/10kJ/m²ISO 179/1eA
Notched Charpy Impact Strength (at -40°C)10/10kJ/m²ISO 179/1eA
Poisson's Ratio0.34/0.34--
Notched Izod Impact Strength (at 23°C)12/15kJ/m²ISO 180/1A
Notched Izod Impact Strength (at -30°C)10/10kJ/m²ISO 180/1A
Notched Izod Impact Strength (at -40°C)10/10kJ/m²ISO 180/1A
Izod Impact Strength (at 23°C)80/90kJ/m²ISO 180/1U
Izod Impact Strength (at -30°C)70/70kJ/m²ISO 180/1U
Hardness (Rockwell Scale M)101/--ISO 2039-2
Typical Properties
ValueUnitsTest Method / Conditions
Resin IdentificationPA66-GF33-ISO 1043
ISO DesignationISO 16396-PA66,GF33,M1GNR,S14-100--
Thermal Properties
ValueUnitsTest Method / Conditions
Specific Heat Capacity of Melt2210J/(kg K)-
Melt Temperature (at 10°C/min)262/*°CISO 11357-1/-3
Glass Transition Temperature (at 10°C/min)80/20°CISO 11357-1/-2
Temperature of Deflection Under Load (1.8 Mpa)252/*°CISO 75-1/-2
Temperature of Deflection Under Load (0.45 Mpa)261/*°CISO 75-1/-2
Coefficient of Linear Thermal Expansion (Parallel)18/*E-6/KISO 11359-1/-2
Coefficient of Linear Thermal Expansion (Normal)83/*E-6/KISO 11359-1/-2
Coefficient of Linear Thermal Expansion (Normal, at -40 to 23°C)65/*E-6/KISO 11359-1/-2
Coefficient of Linear Thermal Expansion (Normal, at 55-160°C)140/*E-6/KISO 11359-1/-2
Coefficient of Linear Thermal Expansion (Parallel, at -40 to 23°C)24/*E-6/KISO 11359-1/-2
Coefficient of Linear Thermal Expansion (Parallel, at 55-160°C)13/*E-6/KISO 11359-1/-2
Specific Heat Capacity (Solid, Calculated)1330J/(kg K)-
Relative Thermal Index (Electrical, 0.75mm)130°CUL 746B
Relative Thermal Index (Electrical, 1.5mm)130°CUL 746B
Relative Thermal Index (Electrical, 3mm)130°CUL 746B
Relative Thermal Index (Impact, 0.75mm)120°CUL 746B
Relative Thermal Index (Impact, 1.5mm)120°CUL 746B
Relative Thermal Index (Impact, 3mm)120°CUL 746B
Relative Thermal Index (Strength, 0.75mm)130°CUL 746B
Relative Thermal Index (Strength, 1.5mm)130/*°CUL 746B
Relative Thermal Index (Strength, 3mm)130°CUL 746B
Thermal Conductivity of Melt0.22W/(m K)ISO 22007-2
Electrical Properties
ValueUnitsTest Method / Conditions
Relative Permittivity (at 100Hz)4.2/--IEC 62631-2-1
Relative Permittivity (at 1MHz)4/--IEC 62631-2-1
Dissipation Factor (at 100 Hz)100/-E-4IEC 62631-2-1
Dissipation Factor (at 1 MHz)150/-E-4IEC 62631-2-1
Comparative Tracking Index600/--IEC 60112
Electric Strength (Short Time, 1mm)37/-kV/mmIEC 60243-1
Volume Resistivity1E13/-Ohm.mIEC 62631-3-1
Flammability
ValueUnitsTest Method / Conditions
Oxygen Index24/*%ISO 4589-1/-2
FMVSS ClassSE/B-ISO 3795 (FMVSS 302)
Burning Behavior (at 1.5mm/* Nominal Thickness)UL94 HB/*classIEC 60695-11-10
Burning Behavior (at 0.71mm/* Thickness h)UL94 HB/*classIEC 60695-11-10
Burning Rate (at 1mm Thickness)28mm/minISO 3795 (FMVSS 302)
Other Properties
ValueUnitsTest Method / Conditions
Humidity Absorption (at 2mm)1.8/*%Sim. to ISO 62
Water Absorption (at 2mm)5.7/*%Sim. to ISO 62
Water Absorption (Immersion 24h) ¹1.2/*%Sim. to ISO 62
Density1390/-kg/m³ISO 1183
VDA Properties
ValueUnitsTest Method / Conditions
Emission of Organic Compounds6µgC/gVDA 277
Odor4.5classVDA 270
Fogging (F-Value, Refraction)95/*%ISO 6452
Fogging (G-Value, Condensate)0.3/*mgISO 6452
Processing Information (Injection Molding)
ValueUnitsTest Method / Conditions
Drying Recommendedyes--
Drying Temperature80°C-
Drying Time (Dehumidified Dryer)2 - 4h-
Processing Moisture Contentmax. 0.2%-
Hold Pressure Range50 - 100MPa-
Hold Pressure Time3s/mm-
Ejection Temperature210°C-
Melt Temperature (Optimum)295°C-
Melt Temperature (Minimum)285°C-
Melt Temperature (Maximum)305°C-
Maximum Screw Tangential Speed0.2m/s-
Mold Temperature (Optimum)100°C-
Mold Temperature (Minimum)70°C-
Mold Temperature (Maximum)120°C-
Rheological Properties
ValueUnitsTest Method / Conditions
Viscosity Number157/*cm³/gISO 307, 1157, 1628
Mold Shrinkage (Parallel)0.3/-%ISO 294-4, 2577
Mold Shrinkage (Normal)1.1/-%ISO 294-4, 2577
Note
  • [1]: 2mm thickness
Chemical Resistance
Chemical Type Chemical Name Resistance
Acids Acetic Acid (5% by mass) (23°C) Probably Resistant
Acids Chromic Acid solution (40% by mass) (23°C) Not Recommended
Acids Citric Acid solution (10% by mass) (23°C) Probably Resistant
Acids Hydrochloric Acid (36% by mass) (23°C) Not Recommended
Acids Lactic Acid (10% by mass) (23°C) Probably Resistant
Acids Nitric Acid (40% by mass) (23°C) Not Recommended
Acids Sulfuric Acid (38% by mass) (23°C) Not Recommended
Acids Sulfuric Acid (5% by mass) (23°C) Not Recommended
Alcohols Ethanol (23°C) Probably Resistant
Alcohols Isopropyl alcohol (23°C) Probably Resistant
Alcohols Methanol (23°C) Probably Resistant
Bases Ammonium Hydroxide solution (10% by mass) (23°C) Probably Resistant
Bases Sodium Hydroxide solution (1% by mass) (23°C) Probably Resistant
Bases Sodium Hydroxide solution (35% by mass) (23°C) Not Recommended
Ethers Diethyl ether (23°C) Probably Resistant
Hydrocarbons iso-Octane (23°C) Probably Resistant
Hydrocarbons n-Hexane (23°C) Probably Resistant
Hydrocarbons Toluene (23°C) Probably Resistant
Ketones Acetone (23°C) Probably Resistant
Mineral oils Insulating Oil (23°C) Probably Resistant
Mineral oils SAE 10W40 multigrade motor oil (130°C) Probably Resistant
Mineral oils SAE 10W40 multigrade motor oil (23°C) Probably Resistant
Mineral oils SAE 80/90 hypoid-gear oil (130°C) Probably Resistant
Other 1% nonylphenoxy-polyethyleneoxy ethanol in water (23°C) Probably Resistant
Other 50% Oleic acid + 50% Olive Oil (23°C) Probably Resistant
Other DOT No. 4 Brake fluid (130°C) Probably Resistant
Other Ethyl Acetate (23°C) Probably Resistant
Other Ethylene Glycol (50% by mass) in water (108°C) Probably Resistant
Other Hydrogen peroxide (23°C) Not Recommended
Other Phenol solution (5% by mass) (23°C) Not Recommended
Other Water (23°C) Probably Resistant
Other Water (90°C) Probably Resistant
Salt solutions Sodium Carbonate solution (2% by mass) (23°C) Probably Resistant
Salt solutions Sodium Carbonate solution (20% by mass) (23°C) Probably Resistant
Salt solutions Sodium Chloride solution (10% by mass) (23°C) Probably Resistant
Salt solutions Sodium Hypochlorite solution (10% by mass) (23°C) Not Recommended
Salt solutions Zinc Chloride solution (50% by mass) (23°C) Not Recommended
Standard Fuels Diesel fuel (pref. ISO 1817 Liquid F) (>90°C) Probably Resistant
Standard Fuels Diesel fuel (pref. ISO 1817 Liquid F) (23°C) Probably Resistant
Standard Fuels Diesel fuel (pref. ISO 1817 Liquid F) (90°C) Probably Resistant
Standard Fuels ISO 1817 Liquid 1 - E5 (60°C) Probably Resistant
Standard Fuels ISO 1817 Liquid 2 - M15E4 (60°C) Probably Resistant
Standard Fuels ISO 1817 Liquid 3 - M3E7 (60°C) Probably Resistant
Standard Fuels ISO 1817 Liquid 4 - M15 (60°C) Probably Resistant
Standard Fuels Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23°C) Probably Resistant
Standard Fuels Standard fuel without alcohol (pref. ISO 1817 Liquid C) (23°C) Probably Resistant

Regulatory & Compliance

Technical Details & Test Data

Stress vs Strain (Cond.)

DuPont Zytel 70G33L NC010 Stress vs Strain (Cond.)

Stress vs Strain (Dry)

DuPont Zytel 70G33L NC010 Stress vs Strain (Dry)

Secant Modulus vs Strain (Cond.)

DuPont Zytel 70G33L NC010 Secant Modulus vs Strain (Cond.)

Secant Modulus vs Strain (Dry)

DuPont Zytel 70G33L NC010 Secant Modulus vs Strain (Dry)

Stress vs Strain (Isochronous, 23°C, Cond)

DuPont Zytel 70G33L NC010 Stress vs Strain (Isochronous, 23°C, Cond)

Stress vs Strain (Isochronous, 60°C, Cond.)

DuPont Zytel 70G33L NC010 Stress vs Strain (Isochronous, 60°C, Cond.)

Stress vs Strain (Isochronous, 100°C, Cond.)

DuPont Zytel 70G33L NC010 Stress vs Strain (Isochronous, 100°C, Cond.)

Stress vs Strain (Isochronous, 150°C, Cond)

DuPont Zytel 70G33L NC010 Stress vs Strain (Isochronous, 150°C, Cond)

LTHA Stress at Break (4mm)

DuPont Zytel 70G33L NC010 LTHA Stress at Break (4mm)