Zytel® 8018HS NC010

Sold by DuPont
Polymer Name: Polyamide 66 (PA 66)
Processing Methods: Injection Molding
Fillers Included: Glass Fiber
Additives Included: Mold Release Agent
Flexural Modulus: 3600.0 MPa
Start Order
Secure
Order Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
View
Similar Products from DuPont NEW
TypeDocument Name
Brochure
Technology Profile Laser Welding
Technology Profile Laser Welding
Brochure
Other
Hot Runner Manual for Robust Molding of Semi-crystalline Resins
Hot Runner Manual for Robust Molding of Semi-crystalline Resins
Other
Brochure
Zytel® Plus Nylon
Zytel® Plus Nylon
Brochure
Other
DuPont Zytel® SVHC Statement
DuPont Zytel® SVHC Statement
Other
Other
Next Generation Plastic Metal Hybrids
Next Generation Plastic Metal Hybrids
Other
Other
Failure Analysis using Microscopic Techniques
Failure Analysis using Microscopic Techniques
Other
Other
DuPont™ Zytel® Helps Enable Safe, Long-life Service for Outdoor MV Electrical Switch Equipment
DuPont™ Zytel® Helps Enable Safe, Long-life Service for Outdoor MV Electrical Switch Equipment
Other
Other
Structural and Fatigue Performance
Structural and Fatigue Performance
Other
Brochure
DuPont Performance Polymers - Self Tapping Screws
DuPont Performance Polymers - Self Tapping Screws
Brochure
Other
Minlon® and Zytel® Design Information - Module II
Minlon® and Zytel® Design Information - Module II
Other
Other
Zytel® 8018HS NC010 Injection Molding Guide
Zytel® 8018HS NC010 Injection Molding Guide
Other
Technical Data Sheet
Zytel® 8018HS NC010 Technical Data Sheet
Zytel® 8018HS NC010 Technical Data Sheet
Technical Data Sheet

Knowde Enhanced TDS

Expand All

+

Identification & Functionality

Additives Included
Chemical Family
Fillers Included
Plastics & Elastomers Functions
Technologies

Zytel® 8018HS NC010 Features & Benefits

Applications & Uses

Plastics & Elastomers Processing Methods

Properties

Physical Properties
ValueUnitsTest Method / Conditions
Molding Shrinkage - Parallel0.4/-%ISO 294-4, 2577
Molding Shrinkage - Normal0.8/-%ISO 294-4, 2577
Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Modulus4200/2300MPaISO 527-1/-2
Hardness, Rockwell70Scale MISO 2039-2
Hardness, Rockwell110Scale RISO 2039-2
Stress at Break85/58MPaISO 527-1/-2
Strain at Break6/14%ISO 527-1/-2
Flexural Modulus3600/2000MPaISO 178
Charpy Impact Strength (23°C)80/100kJ/m²ISO 179/1eU
Charpy Impact Strength (-30°C)80/75kJ/m²ISO 179/1eU
Charpy Notched Impact Strength (23°C)14/18kJ/m2ISO 179/1eA
Charpy Notched Impact Strength (-30°C)6/6kJ/m2ISO 179
Charpy Notched Impact Strength (-40°C)4/4kJ/m²ISO 179/1eA
Izod Notched Impact Strength (23°C)13/18kJ/m²ISO 180/1A
Izod Notched Impact Strength (-30°C)10/5kJ/m²ISO 180/1A
Izod Notched Impact Strength (-40°C)7/5kJ/m²ISO 180/1A
Izod Impact Strength (23°C)90/100kJ/m²ISO 180/1U
Izod Impact Strength (-30°C)90/70kJ/m²ISO 180/1U
Poisson's Ratio0.36/0.39--
Thermal Properties
ValueUnitsTest Method / Conditions
Melting Temperature (10°C/min)263/-°CISO 11357-1/-3
Temperature of Deflection Under Load(1.8 MPa)195/-°CISO 75-1/-2
Temperature of Deflection Under Load (0.45 MPa)246/-°CISO 75-1/-2
Coefficient of Linear Thermal Expansion - Parallel50/-E-6/KISO 11359-1/-2
Coefficient of Linear Thermal Expansion - Normal118/-E-6/KISO 11359-1/-2
Relative Temperature Index - Electrical (0.75 mm)120°CUL 746B
Relative Temperature Index - Electrical (1.5 mm)120°CUL 746B
Relative Temperature Index - Electrical (3 mm)120°CUL 746B
Relative Temperature Index - Impact (0.75 mm)65°CUL 746B
Relative Temperature Index - Impact (1.5 mm)95°CUL 746B
Relative Temperature Index - Impact (3 mm)105°CUL 746B
Relative Temperature Index - Strength (0.75 mm)85°CUL 746B
Relative Temperature Index - Strength (1.5 mm)105/-°CUL 746B
Relative Temperature Index - Strength (3 mm)105°CUL 746B
Electrical Properties
ValueUnitsTest Method / Conditions
Comparative Tracking Index - CTI580/--IEC 60112
Flammability
ValueUnitsTest Method / Conditions
Burning Behaviour (1.5 mm, Nominal Thickness)HB/-classIEC 60695-11-10
Burning Behaviour (Thickness h)HB/-classIEC 60695-11-10
Oxygen Index21/-%ISO 4589-1/-2
FMVSS ClassB-ISO 3795 (FMVSS 302)
Burning Rate (1 mm, Thickness)max. 80mm/minISO 3795 (FMVSS 302)
Ul RecognitionYes/--UL 94
Thickness Tested1.5/-mmIEC 60695-11-10
Other Properties
ValueUnitsTest Method / Conditions
Humidity Absorption (2 mm)1.9/-%Sim. to ISO 62
Water Absorption (2 mm)6.3/-%Sim. to ISO 62
Density1190/-kg/m³ISO 1183
Processing Information (Injection Molding)
ValueUnitsTest Method / Conditions
Drying RecommendedYes--
Drying Temperature80°C-
Drying Time (Dehumidified Dryer)2.0 - 4.0h-
Processing Moisture Content≤0.2%-
Melt Temperature Optimum295°C-
Min. Melt Temperature285°C-
Max. Melt Temperature305°C-
Max. Screw Tangential Speed0.2/-m/s-
Mold Temperature Optimum80°C-
Min. Mold Temperature50°C-
Max. Mold Temperature100°C-
Hold Pressure Range50 - 100MPa-
Hold Pressure Time3s/mm-
Ejection Temperature210°C-
Chemical Resistance
Chemical Type Chemical Name Resistance
Acids Acetic Acid (5% by mass) (23°C) Probably Resistant
Acids Chromic Acid solution (40% by mass) (23°C) Not Recommended
Acids Citric Acid solution (10% by mass) (23°C) Probably Resistant
Acids Hydrochloric Acid (36% by mass) (23°C) Not Recommended
Acids Lactic Acid (10% by mass) (23°C) Probably Resistant
Acids Nitric Acid (40% by mass) (23°C) Not Recommended
Acids Sulfuric Acid (38% by mass) (23°C) Not Recommended
Acids Sulfuric Acid (5% by mass) (23°C) Not Recommended
Alcohols Ethanol (23°C) Probably Resistant
Alcohols Isopropyl alcohol (23°C) Probably Resistant
Alcohols Methanol (23°C) Probably Resistant
Bases Ammonium Hydroxide solution (10% by mass) (23°C) Probably Resistant
Bases Sodium Hydroxide solution (1% by mass) (23°C) Probably Resistant
Bases Sodium Hydroxide solution (35% by mass) (23°C) Not Recommended
Ethers Diethyl ether (23°C) Probably Resistant
Hydrocarbons iso-Octane (23°C) Probably Resistant
Hydrocarbons n-Hexane (23°C) Probably Resistant
Hydrocarbons Toluene (23°C) Probably Resistant
Ketones Acetone (23°C) Probably Resistant
Mineral oils Insulating Oil (23°C) Probably Resistant
Mineral oils SAE 10W40 multigrade motor oil (130°C) Probably Resistant
Mineral oils SAE 10W40 multigrade motor oil (23°C) Probably Resistant
Mineral oils SAE 80/90 hypoid-gear oil (130°C) Probably Resistant
Other 1% nonylphenoxy-polyethyleneoxy ethanol in water (23°C) Probably Resistant
Other 50% Oleic acid + 50% Olive Oil (23°C) Probably Resistant
Other DOT No. 4 Brake fluid (130°C) Probably Resistant
Other Ethyl Acetate (23°C) Probably Resistant
Other Ethylene Glycol (50% by mass) in water (108°C) Probably Resistant
Other Hydrogen peroxide (23°C) Not Recommended
Other Phenol solution (5% by mass) (23°C) Not Recommended
Other Water (23°C) Probably Resistant
Other Water (90°C) Not Recommended
Salt solutions Sodium Carbonate solution (2% by mass) (23°C) Probably Resistant
Salt solutions Sodium Carbonate solution (20% by mass) (23°C) Probably Resistant
Salt solutions Sodium Chloride solution (10% by mass) (23°C) Probably Resistant
Salt solutions Sodium Hypochlorite solution (10% by mass) (23°C) Not Recommended
Salt solutions Zinc Chloride solution (50% by mass) (23°C) Not Recommended
Standard Fuels Diesel fuel (pref. ISO 1817 Liquid F) (>90°C) Probably Resistant
Standard Fuels Diesel fuel (pref. ISO 1817 Liquid F) (23°C) Probably Resistant
Standard Fuels Diesel fuel (pref. ISO 1817 Liquid F) (90°C) Probably Resistant
Standard Fuels ISO 1817 Liquid 1 - E5 (60°C) Probably Resistant
Standard Fuels ISO 1817 Liquid 2 - M15E4 (60°C) Probably Resistant
Standard Fuels ISO 1817 Liquid 3 - M3E7 (60°C) Probably Resistant
Standard Fuels ISO 1817 Liquid 4 - M15 (60°C) Probably Resistant
Standard Fuels Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23°C) Probably Resistant
Standard Fuels Standard fuel without alcohol (pref. ISO 1817 Liquid C) (23°C) Probably Resistant

Regulatory & Compliance

Certifications & Compliance
Compliance
UL Flame Rated

Technical Details & Test Data