Zytel® ST801A NC010A
Sold by DuPont
Zytel® ST801A NC010A is an Unreinforced, Super Toughened, Polyamide 66
Polymer Name: Polyamide 66 (PA 66)
Processing Methods: Film Extrusion, Sheet, Plaques & Profiles Extrusion, Casting, Injection Molding, Coating
Additives Included: Mold Release Agent
Flexural Modulus: 1800.0 MPa
Start Order
SecureOrder Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
Quote required
Similar Products from DuPont NEW
Knowde Enhanced TDS
Identification & Functionality
Additives Included
Chemical Family
Polymer Name
Plastics & Elastomers Functions
Technologies
Product Families
Zytel® ST801A NC010A Features & Benefits
Materials Features
Applications & Uses
Plastics & Elastomers Processing Methods
Properties
Chemical Resistance
Color
Flame Rating
Part Marking Code
Resin ID
Physical Properties
| Value | Units | Test Method / Conditions | |
| Viscosity Number | 130/- | cm3/g | ISO 307, ISO 1157, ISO 1628 |
| Molding Shrinkage - Parallel | 1.8/- | % | ISO 294-4, 2577 |
| Molding Shrinkage - Normal | 1.4/- | % | ISO 294-4, 2577 |
Mechanical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 2000/900 | MPa | ISO 527-1/-2 |
| Stress at 50% Strain | 49/44 | MPa | ISO 527-1/-2 |
| Strain at Break | min. 500/min. 500 | % | ISO 527-1/-2 |
| Flexural Modulus | 1800/700 | MPa | ISO 178 |
| Tensile Creep Modulus (1 h) | -/800 | MPa | ISO 899-1 |
| Tensile Creep Modulus (1000 h) | -/700 | MPa | ISO 899-1 |
| Charpy Impact Strength (23°C) | -/No Break | kJ/m2 | ISO 179-1/1eU |
| Charpy Notched Impact Strength (23°C) | 70/100P | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (-30°C) | 20/20 | kJ/m2 | ISO 179/1eA |
| Izod Notched Impact Strength (23°C) | 80/90 | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (-30°C) | 15/15 | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (-40°C) | 20/17 | kJ/m² | ISO 180/1A |
| Poisson's Ratio | 0.4/0.45 | - | - |
Thermal Properties
| Value | Units | Test Method / Conditions | |
| Melting Temperature (10°C/min) | 262/- | °C | ISO 11357-1/-3 |
| Glass Transition Temperature (10°C/min) | 75/- | °C | ISO 11357-1/-2 |
| Temperature of Deflection Under Load(1.8 MPa) | 63/- | °C | ISO 75-1/-2 |
| Temperature of Deflection Under Load (0.45 MPa) | 157/- | °C | ISO 75-1/-2 |
| Vicat Softening Temperature (50°C/h, 50N) | 205/- | °C | ISO 306 |
| Coefficient of Linear Thermal Expansion - Parallel | 140/- | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion - Normal | 130/- | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion - Normal (23 - 55°C (73 - 130°F)) | 130/- | E-6/K | ASTM E 831 |
| Coefficient of Linear Thermal Expansion - Normal (-40 - 23°C) | 110/- | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion - Normal (55 - 160°C) | 130/- | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion - Parallel (23 - 55°C(73 - 130°F)) | 140/- | E-6/K | ASTM E 831 |
| Coefficient of Linear Thermal Expansion - Parallel (-40 - 23°C) | 110/- | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion - Parallel (55 - 160°C) | 160/- | E-6/K | ISO 11359-1/-2 |
| Relative Temperature Index - Electrical (0.75 mm) | 125 | °C | UL 746B |
| Relative Temperature Index - Electrical (1.5 mm) | 125 | °C | UL 746B |
| Relative Temperature Index - Electrical (3 mm) | 125 | °C | UL 746B |
| Relative Temperature Index - Impact (0.75 mm) | 75 | °C | UL 746B |
| Relative Temperature Index - Impact (1.5 mm) | 75 | °C | UL 746B |
| Relative Temperature Index - Impact (3 mm) | 75 | °C | UL 746B |
| Relative Temperature Index - Strength (0.75 mm) | 85 | °C | UL 746B |
| Relative Temperature Index - Strength (1.5 mm) | 85/- | °C | UL 746B |
| Relative Temperature Index - Strength (3 mm) | 85 | °C | UL 746B |
Electrical Properties
| Value | Units | Test Method / Conditions | |
| Relative Permittivity (100 Hz) | 3.5/5.9 | - | IEC 62631-2-1 |
| Relative Permittivity (1 MHz) | 3.3/3.5 | - | IEC 62631-2-1 |
| Dissipation Factor (100 Hz) | 50/1580 | E-4 | IEC 62631-2-1 |
| Dissipation Factor (1 MHz) | 100/380 | E-4 | IEC 62631-2-1 |
| Surface Resistivity | -/1E12 | ohm | IEC 62631-3-2 |
| Electric Strength | 25/- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index - CTI | 600/- | - | IEC 60112 |
| Electric Strength - Short Time (2 mm) | 25/26 | kV/mm | IEC 60243-1 |
| High Amperage Arc Ignition Resistance (1.5 mm) | 200/-1 | arcs | UL 746A |
| High Amperage Arc Ignition Resistance (3 mm) | 200/-1 | arcs | UL 746A |
| Volume Resistivity | >1E13/8.7E10 | ohm.m | IEC 62631-3-1 |
Flammability
| Value | Units | Test Method / Conditions | |
| Burning Behaviour (1.5 mm, Nominal Thickness) | HB/- | class | IEC 60695-11-10 |
| Burning Behaviour (Thickness h) | HB/- | class | IEC 60695-11-10 |
| Oxygen Index | 20/- | % | ISO 4589-1/-2 |
| FMVSS Class | B | - | ISO 3795 (FMVSS 302) |
| Burning Rate (1 mm, Thickness) | max. 80 | mm/min | ISO 3795 (FMVSS 302) |
| Hot Wire Ignition (1.5 mm) | 15/- | s | UL 746A |
| Hot Wire Ignition (3 mm) | 20/- | s | UL 746A |
| Ul Recognition | Yes/- | - | UL 94 |
| Thickness Tested | 1.5/- | mm | IEC 60695-11-10 |
Other Properties
| Value | Units | Test Method / Conditions | |
| Humidity Absorption (2 mm) | 2/- | % | Sim. to ISO 62 |
| Water Absorption (2 mm) | 6.5/- | % | Sim. to ISO 62 |
| Water Absorption - Immersion (24 h) | 1.1/- | % | Sim. to ISO 62 |
| Density | 1070/- | kg/m³ | ISO 1183 |
Processing Information (Injection Molding)
| Value | Units | Test Method / Conditions | |
| Drying Recommended | Yes | - | - |
| Drying Temperature | 80 | °C | - |
| Drying Time (Dehumidified Dryer) | 2.0 - 4.0 | h | - |
| Processing Moisture Content | ≤0.2 | % | - |
| Melt Temperature Optimum | 290 | °C | - |
| Min. Melt Temperature | 280 | °C | - |
| Max. Melt Temperature | 300 | °C | - |
| Max. Screw Tangential Speed | 0.3/- | m/s | - |
| Mold Temperature Optimum | 80 | °C | - |
| Min. Mold Temperature | 50 | °C | - |
| Max. Mold Temperature | 100 | °C | - |
| Hold Pressure Range | 50 - 100 | MPa | - |
| Hold Pressure Time | 4 | s/mm | - |
| Ejection Temperature | 190 | °C | - |
Chemical Resistance
| Chemical Type | Chemical Name | Resistance |
| Acids | Acetic Acid (5% by mass) (23°C) | Probably Resistant |
| Acids | Chromic Acid solution (40% by mass) (23°C) | Not Recommended |
| Acids | Citric Acid solution (10% by mass) (23°C) | Probably Resistant |
| Acids | Hydrochloric Acid (36% by mass) (23°C) | Not Recommended |
| Acids | Lactic Acid (10% by mass) (23°C) | Probably Resistant |
| Acids | Nitric Acid (40% by mass) (23°C) | Not Recommended |
| Acids | Sulfuric Acid (38% by mass) (23°C) | Not Recommended |
| Acids | Sulfuric Acid (5% by mass) (23°C) | Not Recommended |
| Alcohols | Ethanol (23°C) | Probably Resistant |
| Alcohols | Isopropyl alcohol (23°C) | Probably Resistant |
| Alcohols | Methanol (23°C) | Probably Resistant |
| Bases | Ammonium Hydroxide solution (10% by mass) (23°C) | Probably Resistant |
| Bases | Sodium Hydroxide solution (1% by mass) (23°C) | Probably Resistant |
| Bases | Sodium Hydroxide solution (35% by mass) (23°C) | Not Recommended |
| Ethers | Diethyl ether (23°C) | Probably Resistant |
| Hydrocarbons | iso-Octane (23°C) | Probably Resistant |
| Hydrocarbons | n-Hexane (23°C) | Probably Resistant |
| Hydrocarbons | Toluene (23°C) | Probably Resistant |
| Ketones | Acetone (23°C) | Probably Resistant |
| Mineral oils | Insulating Oil (23°C) | Probably Resistant |
| Mineral oils | SAE 10W40 multigrade motor oil (130°C) | Not Recommended |
| Mineral oils | SAE 10W40 multigrade motor oil (23°C) | Probably Resistant |
| Mineral oils | SAE 80/90 hypoid-gear oil (130°C) | Not Recommended |
| Other | 1% nonylphenoxy-polyethyleneoxy ethanol in water (23°C) | Probably Resistant |
| Other | 50% Oleic acid + 50% Olive Oil (23°C) | Probably Resistant |
| Other | DOT No. 4 Brake fluid (130°C) | Not Recommended |
| Other | Ethyl Acetate (23°C) | Probably Resistant |
| Other | Ethylene Glycol (50% by mass) in water (108°C) | Not Recommended |
| Other | Hydrogen peroxide (23°C) | Not Recommended |
| Other | Phenol solution (5% by mass) (23°C) | Not Recommended |
| Other | Water (23°C) | Probably Resistant |
| Other | Water (90°C) | Probably Resistant |
| Salt solutions | Sodium Carbonate solution (2% by mass) (23°C) | Probably Resistant |
| Salt solutions | Sodium Carbonate solution (20% by mass) (23°C) | Probably Resistant |
| Salt solutions | Sodium Chloride solution (10% by mass) (23°C) | Probably Resistant |
| Salt solutions | Sodium Hypochlorite solution (10% by mass) (23°C) | Not Recommended |
| Salt solutions | Zinc Chloride solution (50% by mass) (23°C) | Not Recommended |
| Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (>90°C) | Not Recommended |
| Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (23°C) | Probably Resistant |
| Standard Fuels | Diesel fuel (pref. ISO 1817 Liquid F) (90°C) | Not Recommended |
| Standard Fuels | ISO 1817 Liquid 1 - E5 (60°C) | Probably Resistant |
| Standard Fuels | ISO 1817 Liquid 2 - M15E4 (60°C) | Probably Resistant |
| Standard Fuels | ISO 1817 Liquid 3 - M3E7 (60°C) | Probably Resistant |
| Standard Fuels | ISO 1817 Liquid 4 - M15 (60°C) | Probably Resistant |
| Standard Fuels | Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23°C) | Probably Resistant |
| Standard Fuels | Standard fuel without alcohol (pref. ISO 1817 Liquid C) (23°C) | Probably Resistant |
Regulatory & Compliance
Certifications & Compliance
OEM Standards
Compliance
Technical Details & Test Data
Viscosity vs Shear Rate
Shear Stress vs Shear Rate
Packaging & Availability
Country Availability
Regional Availability
Zytel® ST801A NC010A
DuPont