Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Propionate 384-16 contains an ultra-violet inhibitor(UVI) and has a plasticizer level of 16%. It is resistant to high temperatures.
TENITE™ Propionate 384A4000016 Clear, Trsp
Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Propionate 384-16 contains an ultra-violet inhibitor(UVI) and has a plasticizer level of 16%. It is resistant to high temperatures.
Take Action
Knowde Enhanced TDS
Identification & Functionality
Additives Included
Chemical Family
Polymer Name
Plastics & Elastomers Functions
Technologies
Product Families
Features & Benefits
Applications & Uses
Markets
Plastics & Elastomers End Uses
Recommended Applications
- Color cosmetics packaging
- Consumer housewares-NFC
- Equipment & machinery
- Fragrance packaging
- Ophthalmics
- Personal care & cosmetics packaging
- Profiles
- Sporting equipment
Properties
Physical Form
Mechanical Properties
| Value | Units | Test Method / Conditions | |
| Elongation at Break | 45.0 | % | D 638 |
| Flexural Modulus | 1241 (1.80 x 105) | mPa (psi) | D 790 |
| Flexural Yield Strength | 35.2 (5100) | mPa (psi) | D 790 |
| Izod Impact Strength, Notched at 23°C | min. 533 (min. 10) | j/m (ft·lbf/in.) | D 256 |
| Izod Impact Strength, Notched at -40°C | 123 (2.3) | j/m (ft·lbf/in.) | D 256 |
| Rockwell Hardness, R Scale | 68.0 | - | D 785 |
| Tensile Stress at Break | 30.3 (4400) | mPa (psi) | D 638 |
| Tensile Stress at Yield | 26.9 (3900) | mPa (psi) | D 638 |
Thermal Properties
| Value | Units | Test Method / Conditions | |
| Deflection Temperature at 0.455 MPa (66 psi) | 80 (176) | °C (°F) | D 648 |
| Deflection Temperature at 1.82 MPa (264 psi) | 72 (162) | °C (°F) | D 648 |
| Vicat Softening Temperature | 92 (198) | °C (°F) | D 1525 |
Typical Properties
| Value | Units | Test Method / Conditions | |
| Plasticizer | 16.0 | % | - |
| Specific Gravity | 1.19 | - | D 792 |
Permanence Properties
| Value | Units | Test Method / Conditions | |
| Soluble Matter Loss | 0.1 | % | D 570 |
| Water Absorption, 24 h immersion | 1.4 | % | D 570 |
| Weight Loss on Heating [72 hours at 80°C (176°F)] | 1.3 | % | D 1562 |
Miscellaneous Properties
| Value | Units | Test Method / Conditions | |
| Coefficient of Linear Thermal Expansion(Propinate Properties) | 11-17 x 10-5 (6-9 x 10-5) | mm/mm·°C (in./in.·°F) | D 696 |
| Dielectric Constant 1 MHz(Propinate Properties) | 3.3-3.8 | - | D 150 |
| Dielectric Strength(Propinate Properties) | 11.8-18.7 (300-475) | kV/mm (V/mil) | D 149 |
| Dissipation Factor 1 MHz(Propinate Properties) | 0.01-0.15 | - | D 150 |
| Haze(Propinate Properties) | max. 8.5 | % | D 1003 |
| Light Transmission(Propinate Properties) | min. 90 | % | E 308 |
| Mold Shrinkage(Propinate Properties) | 0.2-0.6 | % | D 955 |
| Refractive Index, nD(Propinate Properties) | 1.46-1.49 | - | D 542 |
| Specific Heat at 23°C (73°F)(Propinate Properties) | 1.26-1.67 (0.301-0.399) | kJ/kg·K (Btu/lb·°F) | DS |
| Thermal Conductivity(Propinate Properties) | 0.17-0.33 (1.2-2.3) | W/m·K (Btu·in./h·ft2·°F) | C 177 |
| Volume Resistivity(Propinate Properties) | 1013-1015 | ohm·cm | D 257 |
Physical Form
Pellets
Appearance
Clear or transparent
Packaging & Availability