Elix™ ABS HH 3105

1 of 64 products in this brand
High heat resistance ABS. ISO shortname: ISO 2580-1 ABS 1-M, MG, 105-15-16-20. Benefits: Excellent balance of impact strength and flowability; Super low emission grade; Lower mold deposits in injection molding processing applications; Better dimensional under heat. Chemical Composition: Acrylonitrile-butadiene-styrene (ABS) copolymer modified with poly(styrene-co-maleimide) (SMI)

Polymer Name: Acrylonitrile Butadiene Styrene (ABS)

Processing Methods: Injection Molding

Melt Flow Index: 4.0 - 4.0 g/10 min

Similar Products

  • TypeDocument Name
View All Documents

Knowde Enhanced TDS

Identification & Functionality

Plastics & Elastomers Functions
Technologies

Features & Benefits

Applications & Uses

Plastics & Elastomers Processing Methods

Properties

Flame Rating
Physical Form
Flame Rating
UL 94 HB
Mechanical Properties
ValueUnitsTest Method / Conditions
Elongation at Break (23°C/50% Relative Humidity, 5 mm/min)32% ASTM D 638
Elongation at Break (23°C/50% Relative Humidity, 50 mm/min)32% ISO 527-1,2
Tensile Modulus (23°C/50% Relative Humidity, 5 mm/min)312000psi ASTM D 638
Tensile Modulus (23°C/50% Relative Humidity, 1 mm/min)2150MPa ISO 527-1,2
Yield Stress (23°C/50% Relative Humidity, 5 mm/min)39MPa ASTM D 638
Yield Stress (23°C/50% Relative Humidity, 50 mm/min)42 MPa ISO 527-1,2
Flexural Strength (23°C/50% Relative Humidity, 2 mm/min)66MPa ISO 178
Flexural Modulus (23°C/50% Relative Humidity, 1.3 mm/min)328000psi ASTM D 790
Flexural Modulus (23°C/50% Relative Humidity, 2 mm/min)2260MPa ISO 178
Charpy Notched Impact Strength (23°C (73°F), 50% Relative Humidity)19kJ/m2 ISO 179-1eA
Izod Notched Impact Strength (-22°F (-30°C), 50% Relative Humidity, 3.2mm, 1/8”)140J/m ASTM D 256
Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 3.2mm, 1/8”)240J/m ASTM D 256
Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 6.4mm,1/4”)190J/m ASTM D 256
Izod Notched Impact Strength (23°C (73°F), 50% Relative Humidity)18kJ/m2 ISO 180-1A
Izod Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity)11kJ/m2 ISO 180-1A
Ball Indentation Hardness (23°C/50% Relative Humidity)95N/mm2 ISO 2039-1
Physical Properties
ValueUnitsTest Method / Conditions
Melt Flow Rate - MFR (230°C, 3.8Kg) 4g/10minASTM D1238
Melt Volume Flow Rate - MVFR (220°C, 10Kg)16cm3/10min ISO 1133
Molding Shrinkage - Normal (60X60X2 mm)0.6-0.7% ISO 294-4
Molding Shrinkage - Parallel (60X60X2 mm)0.6-0.7% ISO 294-4
Density (25°C)1.03g/cm3ISO 1183-1
Thermal Properties
ValueUnitsTest Method / Conditions
Coefficient Of Linear Thermal Expansion - Parallel (23 to 55°C)0.9910-4/K ISO 11359 -1,2
Deflection Temperature Under Load (0.45 Mpa)104°C ISO 75-1,2
Deflection Temperature Under Load (1.80 Mpa)99°C ISO 75-1,2
Vicat Softening Temperature (50N, 50°C/h)217ºF ASTM D 1525
Vicat Softening Temperature (B120, 120°C/h)105°C ISO 306
Vicat Softening Temperature (B50, 50°C/h)103°C ISO 306
Flammability
ValueUnitsTest Method / Conditions
Burning Behavior (1.6 mm)HB Class UL 94
Burning Behavior (1.6 mm)HBClassUL 94
Burning Rate (US-FMVSS, 200X105X2mm)max. 50mm/minISO 3795
Processing Information (Injection Molding)
ValueUnitsTest Method / Conditions
Mold Temperature70°CISO 294
Injection Velocity240mm/sISO 294
Melt Temperature240°CISO 294