Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Flame Rating
- UL 94 HB
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Processing Information (Injection Molding)
Value | Units | Test Method / Conditions | |
Tensile Modulus (23°C/50% Relative Humidity, 5 mm/min) | 363000 | psi | ASTM D 638 |
Tensile Modulus (23°C/50% Relative Humidity, 1 mm/min) | 2500 | MPa | ISO 527-1,2 |
Tensile Creep Modulus (23°C/50% Relative Humidity, 1 h) | 2200 | MPa | ISSO 899-1 |
Tensile Creep Modulus (23°C/50% Relative Humidity, 1000 h) | 1500 | MPa | ISSO 899-1 |
Yield Stress (23°C/50% Relative Humidity, 5 mm/min) | 41 | MPa | ASTM D 638 |
Yield Stress (23°C/50% Relative Humidity, 50 mm/min) | 44 | MPa | ISO 527-1,2 |
Yield Strain (23°C/50% Relative Humidity, 50 mm/min) | 2.1 | % | ISO 527-1, -2 |
Tensile Strain at Break (23°C/50% Relative Humidity, 5 mm/min) | min. 15 | % | ASTM D 638 |
Tensile Strain at Break (23°C/50% Relative Humidity, 50 mm/min) | min. 15 | % | ISO 527-1,2 |
Flexural Strength (23°C/50% Relative Humidity, 2 mm/min) | 70 | MPa | ISO 178 |
Flexural Modulus (23°C/50% Relative Humidity, 1.3 mm/min) | 348000 | psi | ASTM D 790 |
Flexural Modulus (23°C/50% Relative Humidity, 2 mm/min) | 2400 | MPa | ISO 178 |
Charpy Notched Impact Strength (23°C (73°F), 50% Relative Humidity) | 16 | kJ/m2 | ISO 179-1eA |
Charpy Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity) | 7 | kJ/m2 | ISO 179-1eA |
Charpy Impact Strength (23°C (73°F), 50% Relative Humidity) | 100 | kJ/m2 | ISO 179-1eU |
Charpy Impact Strength (-30°C (-22°F), 50% Relative Humidity) | 80 | kJ/m2 | ISO 179-1eU |
Izod Notched Impact Strength (-22°F (-30°C), 50% Relative Humidity, 3.2mm, 1/8”) | 105 | J/m | ASTM D 256 |
Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 6.4mm,1/4”) | 205 | J/m | ASTM D 256 |
Izod Notched Impact Strength (23°C (73°F), 50% Relative Humidity) | 16 | kJ/m2 | ISO 180-1A |
Izod Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity) | 7 | kJ/m2 | ISO 180-1A |
Ball Indentation Hardness (23°C/50% Relative Humidity) | 110 | N/mm2 | ISO 2039-1 |
Value | Units | Test Method / Conditions | |
Melt Flow Rate - MFR (230°C, 3.8Kg) | 12 | g/min | ASTM D1238 |
Melt Volume Flow Rate - MVFR (220°C, 10Kg) | 37 | cm3/10min | ISO 1133 |
Molding Shrinkage - Normal (60X60X2 mm) | 0.4-0.6 | % | ISO 294-4 |
Molding Shrinkage - Parallel (60X60X2 mm) | 0.4-0.6 | % | ISO 294-4 |
Density (25°C) | 1.05 | g/cm3 | ISO 1183-1 |
Value | Units | Test Method / Conditions | |
Coefficient Of Linear Thermal Expansion - Parallel (23 to 55°C) | 0.9 | 10-4/K | ISO 11359 -1,2 |
Deflection Temperature Under Load (0.45 Mpa) | 97 | °C | ISO 75-1,2 |
Deflection Temperature Under Load (1.80 Mpa) | 93 | °C | ISO 75-1,2 |
Vicat Softening Temperature (50N, 50°C/h) | 208 | ºF | ASTM D 1525 |
Vicat Softening Temperature (B50, 50°C/h) | 98 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Relative Permittivity (23°C/50 % Relative Humidity, 1 MHz) | 2.9 | — | IEC 60250 |
Relative Permittivity (23°C/50 % Relative Humidity, 100 Hz) | 3.0 | — | IEC 60250 |
Dissipation Factor (23°C/50 % Relative Humidity, 100 Hz) | 55 | 10-4 | IEC 60250 |
Volume Resistivity (23°C/50 % Relative Humidity) | 1E13 | Ohm·m | IEC 60093 |
Surface Resistivity (23°C/50 % Relative Humidity) | 1E15 | Ohm | IEC 60093 |
Comparative Tracking Index - CTI (23°C/50 % Relative Humidity, Solution A) | 600 | Rating | IEC 60112 |
Electric Strength (23°C/50 % Relative Humidity, 1 mm) | 34 | kV/mm | IEC 60243-1 |
Value | Units | Test Method / Conditions | |
Burning Rate (US-FMVSS, 200X105X2mm) | 60 | mm/min | ISO 3795 |
Burning Behavior (1.6 mm) | HB Class | — | UL 94 |
Burning Behavior (1.6 mm) | HB | Class | UL 94 |
Glow Wire Test - GWFI (2.0 mm) | 700 | °C | IEC 60695-2-12 |
Value | Units | Test Method / Conditions | |
Mold Temperature | 70 | °C | ISO 294 |
Injection Velocity | 240 | mm/s | ISO 294 |
Melt Temperature | 240 | °C | ISO 294 |