Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Flame Rating
- UL 94 HB
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Flammability
- Other Properties
- Processing Information (Injection Molding)
Value | Units | Test Method / Conditions | |
Elongation at Break (23°C/50% Relative Humidity, 5 mm/min) | 28 | % | ASTM D 638 |
Elongation at Break (23°C/50% Relative Humidity, 50 mm/min) | 28 | % | ISO 527-1,2 |
Tensile Modulus (23°C/50% Relative Humidity, 5 mm/min) | 336500 | psi | ASTM D 638 |
Tensile Modulus (23°C/50% Relative Humidity, 1 mm/min) | 2320 | MPa | ISO 527-1,2 |
Yield Stress (23°C/50% Relative Humidity, 5 mm/min) | 47 | MPa | ASTM D 638 |
Yield Stress (23°C/50% Relative Humidity, 50 mm/min) | 50 | MPa | ISO 527-1,2 |
Flexural Strength (23°C/50% Relative Humidity, 2 mm/min) | 85 | MPa | ISO 178 |
Flexural Modulus (23°C/50% Relative Humidity, 1.3 mm/min) | 336500 | psi | ASTM D 790 |
Flexural Modulus (23°C/50% Relative Humidity, 2 mm/min) | 2320 | MPa | ISO 178 |
Izod Notched Impact Strength (-22°F (-30°C), 50% Relative Humidity, 3.2mm, 1/8”) | 450 | J/m | ASTM D 256 |
Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 6.4mm,1/4”) | 520 | J/m | ASTM D 256 |
Izod Notched Impact Strength (23°C (73°F), 50% Relative Humidity) | 51 | kJ/m2 | ISO 180-1A |
Izod Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity) | 39 | kJ/m2 | ISO 180-1A |
Izod Notched Impact Strength (-40°C (-40°F), 50% Relative Humidity) | 30 | kJ/m2 | ISO 180-1A |
Value | Units | Test Method / Conditions | |
Melt Flow Rate - MFR (230°C, 3.8Kg) | 5 | g/10min | ASTM D1238 |
Melt Volume Flow Rate - MVFR (260°C, 5Kg) | 21 | cm3/10min | ISO 1133 |
Molding Shrinkage - Crosswise (60X60X2 mm) | 0.65-0.75 | % | ISO 294-4 |
Molding Shrinkage - Lengthwise (60X60X2 mm) | 0.65-0.75 | % | ISO 294-4 |
Water Absortion (Equilibrium Value, 23°C, 50 % R.H.) | 0.2 | % | ISO-62 |
Water Absortion (Saturation Value, Water at 23°C) | 0.7 | % | ISO-62 |
Density (25°C) | 1.11 | g/cm3 | ISO 1183-1 |
Value | Units | Test Method / Conditions | |
Coefficient Of Linear Thermal Expansion - Parallel (23 to 55°C) | 0.8 | 10-4/K | ISO 11359 -1,2 |
Coefficient Of Linear Thermal Expansion - Transverse (23 to 55°C) | 0.82 | 10-4/K | ISO 11359 -1,2 |
Deflection Temperature Under Load (0.45 Mpa) | 120 | °C | ISO 75-1,2 |
Deflection Temperature Under Load (1.80 Mpa) | 101 | °C | ISO 75-1,2 |
Vicat Softening Temperature (50N, 50°C/h) | 245 | ºF | ASTM D 1525 |
Vicat Softening Temperature (B120, 120°C/h) | 120 | °C | ISO 306 |
Vicat Softening Temperature (B50, 50°C/h) | 118 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Burning Behavior (1.6 mm) | HB Class | — | UL 94 |
Burning Behavior (1.6 mm) | HB | Class | UL 94 |
Burning Rate (US-FMVSS, 200X105X2mm) | max. 80 | mm/min | ISO 3795 |
Value | Units | Test Method / Conditions | |
VOC Total Emission (23°C) | max. 10 | µg/g | VDA 278 |
Total Carbon Emission (23°C) | max. 15 | µgC/g | VDA 277 |
FOG Total Emission (23°C) | max. 14 | µg/ | VDA 278 |
Value | Units | Test Method / Conditions | |
Mold Temperature | 80 | °C | — |
Injection Velocity | 240 | mm/s | ISO 294 |
Melt Temperature | 260 | °C | — |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability