Stir well the contents of each container every time before removing material. If the contents are hard or lumpy, warm to 80°C and mix thoroughly before removing material.
1. Weigh each 100 grams of EC-1009 to 10 grams of Hardener EH-21.
2. Mix until uniform. Scrape the sides and bottom of container repeatedly during mixing.
3. Apply to clean bonding surfaces and cure as recommended to achieve the desired properties.
4. Typical cured properties were determined using recommended cure schedule. Some difference in properties may occur with the alternate or other cure schedules.- Industrial Usage
Practices of good housekeeping, safety and cleanliness should be followed before, during and after use.
Properties
- Color
- Typical Properties
- Typical Cured Properties
| Value | Units | Test Method / Conditions | |
| Mix Ratio by Weight (Epoxicast/Hardener) | 100/10 | — | — |
| Mixed Viscocity (at 25°C) | 3000 - 5000 | cPs | — |
| Pot Life (at 25°C, 100g) | 3 | hours | — |
| Recommended Cure (at 65°C) | 3 | hours | — |
| Alternate Cure (at 25°C) | 24 - 48 | hours | — |
| Value | Units | Test Method / Conditions | |
| Specific Gravity (24 Hrs at room temp) | 1.9 | — | — |
| Hardness (24 Hrs at room temp) | 86 | Shore D | — |
| Linear Shrinkage (24 Hrs at room temp) | 0.017 | % | — |
| Weight Loss (10 days exposure at 125°C) | 0.22 | % | — |
| Thermal Conductivity (24 Hrs at room temp) | 1.5 | W/m °K | — |
| Glass Transition Temperature (24 Hrs at room temp) | 56 | °C | — |
| Coefficient of Linear Thermal Expansion (at 10°C, Below Tg, 24 Hrs at room temp) | 31 | — | — |
| Flexural Strength (24 Hrs at room temp) | 16250 | psi | — |
| Flexural Modulus (24 Hrs at room temp) | 12x10^5 | psi | — |
| Dielectric Constant (at 1 kHz, 24 Hrs at room temp) | 6.1 | — | — |
| Dissipation Factor (at 1 kHz, 24 Hrs at room temp) | 0.015 | — | — |
| Volume Resistivity (24 Hrs at room temp) | 2x10^5 | Ω-cm | — |
| Service Temperature Range (24 Hrs at room temp) | -55 to 155 | °C | — |
| Hardness (3 Hrs at 65°C) | 89 | Shore D | — |
| Linear Shrinkage (3 Hrs at 65°C) | 0.31 | % | — |
| Water Absorption (24 hr immersion at Room Temperature) | 0.09 | % | — |
| Water Absorption (24 hr immersion at Room Temperature) | 0.18 | % | — |
| Thermal Conductivity (3 Hrs at 65°C) | 1.6 | W/m °K | — |
| Glass Transition Temperature (3 Hrs at 65°C) | 70 | °C | — |
| Coefficient of Linear Thermal Expansion (at 10°C, Below Tg, 3 Hrs at 65°C) | 34 | — | — |
| Flexural Strength (3 Hrs at 65°C) | 18100 | psi | — |
| Flexural Modulus (3 Hrs at 65°C) | 9x10^5 | psi | — |
| Dielectric Constant (at 1 kHz, 3 Hrs at 65°C) | 6.1 | — | — |
| Dissipation Factor (at 1 kHz, 3 Hrs at 65°C) | 0.014 | — | — |
| Volume Resistivity (3 Hrs at 65°C) | 3x 10^15 | Ω-cm | — |
Safety & Health
- Warning
Adequate ventilation of workplace and ovens is essential. These materials may cause injury to the skin following prolonged or repeated contact and dermatitis in susceptible individuals. In case of skin contact, wash thoroughly with soap and water. For eyes, flush immediately with plenty of water for at least 10 minutes and seek medical attention.
Packaging & Availability
- Available Packaging
2 parts Kit - Packaged in Pint, Quart, Gallon, and 5-Gallon size.