Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
Applications & Uses
- Applications
- Instruction for Use
To use simply insert the cartridge into the application gun and start the plunger into the cylinders using light pressure on the trigger. Next, remove the cartridge cap and expel a small amount of adhesive to be sure both sides are flowing evenly and freely. If automatic mixing of resin and hardener is desired, attach the mixing nozzle to the end of the cartridge and begin dispensing the adhesive. For hand mixing, expel the desired amount of the adhesive and mix thoroughly. Mix approximately 15 seconds after uniform color is obtained.
- Industrial Usage
Product shall be ideally stored in a cool, dry location in unopened containers at a temperature between 8°C to 28°C (46°F to 82°F) unless otherwise labeled. Optimal storage is at the lower half of this temperature range. To prevent contamination of unused product, do not return any material to its original container. For further specific shelf life information, contact your local Technical Service Center.
Properties
- Color
- Typical Properties
- Typical Cured Properties
| Value | Units | Test Method / Conditions | |
| Polyol | Part B | — | — |
| Isocyanate | PART A | — | — |
| Mix Ratio by Weight (A:B) | 100/200 | — | — |
| Mix Ratio by Volume (Part A /Part B) | 1.2 | — | — |
| Mixed Viscocity (at 25°C) | 200000 | cPs | — |
| Gel Time (at 25°C, 1/8" bead) | 4 - 7 | minutes | — |
| Tack Free Time (at 25°C) | 160 - 180 | minutes | — |
| Recommended Cure (at 25°C) | 24 - 48 | hours | — |
| Value | Units | Test Method / Conditions | |
| Specific Gravity | 1.2 | — | — |
| Hardness | 45 | Shore D | — |
| Lap Shear Strength Aluminum (abraded, cured 5 days at 25°C) | 2100 | — | — |
| Lap Shear Strength Aluminum (anodized, cured 5 days at 25°C) | 750 | — | — |
| Lap Shear Strength of Stainless Steel (cured 5 days at 25°C) | 1000 | — | — |
| Lap Shear Strength of Polycarbonate (cured 5 days at 25°C) | 1900 | — | — |
| Tensile Strength | 1300 | psi | — |
| T-Peel Strength | 14 | pli | — |
| Tensile Elongation | 75 | % | — |
| Water Absorption (7 days immersion at Room Temperature) | 0.14 | % | — |
| Water Absorption (7 days immersion at 100°C) | 0.98 | % | — |
| Glass Transition Temperature (Tg) | 45 | °C | — |
| Dielectric Strength | 400 | Volts/mil | — |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Warning
Adequate ventilation of workplace and ovens is essential.
Packaging & Availability
- Available Packaging
Dual Cartridgs: 50ml, 200ml, 400ml
Storage & Handling
- Shelf Life
- 6 Months