Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Technologies
- Product Families
Applications & Uses
Properties
- Physical Form
- Typical Properties
Value | Units | Test Method / Conditions | |
MOONEY VISCOSITY ML 1+8 at125°C (257°F) | 40 ± 10 | — | ASTM D 1646 |
MOONEY VISCOSITY Raw Polymer specific Gravity | 0.92 | — | ASTM F 970 |
MOONEY VISCOSITY (% Ash Content) | Max. 2 | wt% | ASTM D 5667-95 |
MOONEY VISCOSITY (Volatile Matter) | Max. 1 | wt% | ASTM D 5668 |
ODR RHEOMETER ML (30 Minutes/3° Arc at 177°C (350°F)) | 2.0 Typical | — | ASTM D 2084 Ts2 |
ODR RHEOMETER MH (30 Minutes/3° Arc at 177°C (350°F)) | 4.0 Typical | — | ASTM D 2084 Tc90 |
Tensile (Cured 40 Min at 150°C(302°F)) | 2400 | psi | ASTM D 412 |
Elongation (Cured 40 Min at 150°C(302°F)) | 575 | % | ASTM D 412 |
300 % Modulus (Cured 40 Min at 150°C(302°F)) | 1200 | psi | ASTM D 412 |
G&E Blended IIR (Internal Mixer Method) | 100 | pts. | ASTM D 3188-06 (2010) |
Zinc Oxide (Internal Mixer Method) | 3 | pts. | ASTM D 3188-06 (2010) |
Sulfur (Internal Mixer Method) | 1.75 | pts. | ASTM D 3188-06 (2010) |
Stearic Acid (Internal Mixer Method) | 1 | pts. | ASTM D 3188-06 (2010) |
IRB 8 Carbon Black (Internal Mixer Method) | 50 | pts. | ASTM D 3188-06 (2010) |
TMTD (Internal Mixer Method) | 1 | pts. | ASTM D 3188-06 (2010) |
Packaging & Availability
- Packaging
Thirty-six, 75 lb. (34 kg.) bales wrapped in low-melt polyethylene film are packaged in Returnable Metal Boxes weighing 2,700 lbs (1.23 MT) each. Corrugated Boxes are available with a weight of 2200 lbs (1 MT)