G&E Blended Chlorobutyl

1 of 15 products in this brand
G&E Blended Chlorobutyl is produced by carefully combining selected feedstocks for uniform viscosity and rheology. G&E Blended Chlorobutyl is excellent for cost reduction in applications such as innerliners and most mechanical goods when blended with prime Chlorobutyl.

Polymer Name: Chlorobutyl Rubber

Technical Data Sheet
  • TypeDocument Name
View All Documents

Knowde Enhanced TDS

Identification & Functionality

Polymer Name
Technologies

Applications & Uses

Markets

Properties

Physical Form
Typical Properties
ValueUnitsTest Method / Conditions
MOONEY VISCOSITY ML 1+8 at125°C (257°F)35 ± 10ASTM D 1646
MOONEY VISCOSITY Raw Polymer specific Gravity0.93ASTM F 970
MOONEY VISCOSITY (XRF Bromine Content)1.40-2.60%(G&E Method)
MOONEY VISCOSITY ( % Ash Content)Max. 2wt%ASTM D 5667 -95
MOONEY VISCOSITY (Volatile Matter, % weight)Max. 1wt%ASTM D 5668
ODR RHEOMETER ML (30 Minutes/3° Arc at 177°C (350°F)) (14 lbr)2minsASTM D 2084 Ts2
ODR RHEOMETER MH (30 Minutes/3° Arc at 177°C (350°F)) (37 lbr)9minsASTM D 2084 Tc90
Tensile (Cured 40 Min at 150°C(302°F))1500 minASTM D 412
Elongation (Cured 40 Min at 150°C(302°F))375 minASTM D 412
300 % Modulus (Cured 40 Min at 150°C(302°F))800 minASTM D 412
G&E Blended IIR (Internal Mixer Method)100ASTM D 3958-06
Zinc Oxide (Internal Mixer Method)5ASTM D 3958-06
Stearic Acid (Internal Mixer Method)1ASTM D 3958-06
IRB 8 Carbon Black (Internal Mixer Method)40ASTM D 3958-06

Packaging & Availability

Packaging Type
Packaging

Thirty-six, 75 lb. (34 kg.) bales wrapped in low-melt polyethylene film are packaged in Returnable Metal Boxes weighing 2,700 lbs (1.23 MT) each.