Tarnamid® T- 27 CF10

1 of 108 products in this brand
Tarnamid® T- 27 CF10 is a 10% carbon fiber reinforced polyamide 6 compound, heat stabilized, good conductive and electrostatic properties.

Polymer Name: Polyamide 6 (PA 6)

Processing Methods: Injection Molding

Fillers Included: Carbon Fiber

Additives Included: Heat Stabilizer

Flexural Modulus: 6700.0 - 6700.0 MPa

Similar Products

    Knowde Enhanced TDS

    Identification & Functionality

    Additives Included
    Chemical Family
    Fillers Included
    Polymer Name
    Plastics & Elastomers Functions
    Technologies

    Features & Benefits

    Applications & Uses

    Markets
    Plastics & Elastomers End Uses
    Plastics & Elastomers Processing Methods

    Properties

    Flame Rating
    Physical Form
    Flame Rating
    IEC 60695-11-10 HB
    Mechanical Properties
    ValueUnitsTest Method / Conditions
    Tensile Strength130 / -MPaISO 527
    Tensile Modulus8000 / -MPaISO 527
    Strain at break4.5 / -%ISO 527
    Flexural modulus, 23°6700 / -MPaISO 178
    Charpy notched impact strength (+23°)3 / -kJ/m2ISO 179/1eA
    Charpy impact strength (+23°)42 / -kJ/m2ISO 179/1eU
    Izod notched impact strength, +23°3.5 / -kJ/m2ISO 180/1A
    Ball indentation hardness200 / -MPaISO 2039-1
    Physical Properties
    ValueUnitsTest Method / Conditions
    Melt Volume Flow Rate - MVR (275°C/5.0 kg)60cm3/10minISO 1133
    Melt Volume Flow Rate - MVR (275°C/5 kg)60 / *cm3/10 minISO 1133
    Molding Shrinkage - Paralell (60×60×2 mm)0%ISO 294-4
    Molding Shrinkage - Paralell (60×60×2 mm)9%ISO 294-4
    Molding Shrinkage - Paralell (60×60×2 mm)3/0%ISO 294-4
    Molding shrinkage - parallel0.3 / *%ISO 294-4, 2577
    Molding shrinkage - normal0.9 / *%ISO 294-4, 2577
    Density1160 / -kg/m3ISO 1183
    Thermal Properties
    ValueUnitsTest Method / Conditions
    Delfection Temperature Under Load (1.8 MPa)190°CISO 75-1,-2
    Temperature of deflection under load (1.80 Mpa)190 / *°CISO 75-1/-2
    Melting Point (DSC)221°CISO 11357-1
    Vicat Softening Temperature (50 N)200°CISO 306
    Melting temperature (10°C/min)221 / *°CISO 11357-1/-3
    Thickness tested1.6 / *mm
    Vicat softening temperature200 / *°CISO 306
    Burning Behavior at 1.5 mm nominal thicknessHB / *classIEC 60695-11-10
    Burning Behavior at thicknessHB / *classIEC 60695-11-10
    Electrical Properties
    ValueUnitsTest Method / Conditions
    Surface Resistivity1.00E+07ohmASTM D257
    Volume Resistivity10000000ohm.mASTM D257