Features & Benefits
- Labeling Claims
- CASE Ingredients Features
- Product Characteristcs
- Permanent, non-leaching flame retardancy
- Contains no co-solvent
- Excellent cost/performance ratio
- Soft, tough, flexible, dry film
- Excellent low temperature flex crack resistance
Applications & Uses
- Markets
- Applications
- Compatible Substrates & Surfaces
- Coating Type
- Suggested Uses
HD-2313 was designed for use as a coating or finish for synthetic textile fabrics that must have permanent flame retardancy. This unique urethane dispersion is manufactured at high solids and without the use of solvent. Low add-on levels of HD-2313 will enable synthetic fabrics to pass various FR tests including NFPA-701, MVSS-302, & others. HD-2313 is well suited for use in textile coatings, such as automotive upholstery, that require outstanding strength and fire retardancy without the use of antimony-oxide/decabrome chemistry. Using HD-2313, a coating can be formulated to pass MVSS-302 and maintain required strength properties at a much lower coating weight than conventional coatings. This results in a much softer hand and possible cost savings. The high solids and solvent-free nature of HD-2313 make it a very cost effective urethane.
- Product Application
HD-2313 may be sprayed or pad applied as supplied. It may be thickened for alternative application methods.
- Curing
This product displays excellent strength properties as supplied, although melamine-formaldehyde (3-6 phr) may be added to enhance performance..
Properties
- Physical Form
- Physical Properties
- Impact Properties
Value | Units | Test Method / Conditions | |
Solid Content | 44 - 46 | % | — |
Viscocity | 50 - 500 * | cPs | — |
pH | 6.5 - 9.5 | — | — |
Density | 8.8 | lbs/gal | — |
Softening Point | 320.0 | °F | — |
Volatile Organic Compounds | 0.8 | %/wt | — |
Value | Units | Test Method / Conditions | |
Elongation (at 20 inch/min) | 560.0 | % | — |
Tensile Strength (at 20 inch/min) | min. 3500 | psi | — |
100% Modulus (at 20 inch/min) | 560.0 | psi | — |
200% Modulus (at 20 inch/min) | 720.0 | psi | — |
300% Modulus (at 20 inch/min) | 880.0 | psi | — |