Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Parameters
- Additional Information
Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 900 | MPa | ISO 527 |
Tensile Stress at Yield (50 mm/min) | 19 | MPa | ISO 527-1, -2 |
Tensile Strain at Yield (50 mm/min) | 7.3 | % | ISO 527-1,-2 |
Nominal Tensile Strain at Break | 530 | % | ISO 527-1,-2 |
Izod Impact Strength (23°C) | 83.9 | kJ/m2 | ISO 180/1eU |
Izod Impact Strength (-20°C) | 143.5 | kJ/m2 | ISO 180/1eU |
Charpy Notched Impact Strength (23°C) | 50.8 | kJ/m2 | ISO 180/1eA |
Charpy Notched Impact Strength (-20°C) | 11.9 | kJ/m2 | ISO 180/1eA |
Flexural Modulus (2 mm/min) | 750 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Density (23°C) | 0.91 | g/cm3 | ISO 1183-1 |
Melt Mass Flow Rate - MFR (230°C/2.16kg) | 3.5 | g/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 80 | °C | ISO 75-1,-2 |
Value | Units | Test Method / Conditions | |
Polymer Melt Temperature | 230 to 250 | °C | — |
Mold Temperature | 15 to 50 | °C | — |
Injection Speed | Intermediate | - | — |
Hold Pressure | 50 – 100 % of maximum injection | - | — |
Barrel Temperatures | 210 to 240 | °C | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP/PE KD10 | - | ISO 1043 |