Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Physical Form
- Flame Rating
- UL 94 HB
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Flammability
- Processing Information (Extrusion)
- Processing Information (Injection Molding)
- Additional Information
Value | Units | Test Method / Conditions | |
Tensile Stress at Yield (50 mm/min) | 25 | MPa | ISO 527-2 |
Charpy Notched Impact Strength (-20°C) | 2 | kJ/m2 | ISO 179/1eA |
Charpy Notched Impact Strength (23°C) | 20 | kJ/m2 | ISO 179/1eA |
Tensile Strain at Yield (50 mm/min) | 12 | % | ISO 527-2/1A |
Charpy Impact Strength (23°C) | No Break | kJ/m2 | ISO 179/1eU |
Charpy Notched Impact Strength (0°C) | 3 | kJ/m3 | ISO 179/1eA |
Tensile Modulus (1 mm/min) | 850 | MPa | ISO 527-1,-2 |
Charpy Impact Strength (0°C) | No Break | kJ/m2 | ISO 179/1eU |
Charpy Impact Strength (-20°C) | 70 | kJ/m2 | ISO 179/1eU |
Value | Units | Test Method / Conditions | |
Density (23°C) | 0.9 | g/cm3 | ASTM D792 |
Melt Mass Flow Rate - MFR (230°C/2.16kg) | 0.3 | g/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 68 | °C | ISO 75-1,-2 |
Value | Units | Test Method / Conditions | |
Burning Behaviour (d=3.2 mm) | HB | Class | UL-94 |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Extrusion | - | — |
Barrel Temperatures | 180 to 220 | °C | — |
Polymer Melt Temperature | 200 to 220 | °C | — |
Die Temperature | 200 to 220 | °C | — |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Injection Molding | - | — |
Hold Pressure | 50 – 100 % of actual injection pressure | - | — |
Barrel Temperatures | 190 to 250 | °C | — |
Mold Temperature | 15 to 50 | °C | — |
Injection Speed | Slow to Intermediate | - | — |
Polymer Melt Temperature | 230 to 260 | °C | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP-R | - | ISO 1043 |
Regulatory & Compliance
- Certifications & Compliance