Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Processing Information (Extrusion)
- Additional Information
Value | Units | Test Method / Conditions | |
Density (23°C) | 1.07 | g/cm3 | ISO 1183 |
Melt Mass Flow Rate - MFR (230°C/2.16kg) | 0.5 | g/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Charpy Notched Impact Strength (-20°C) | 8.5 | kJ/m2 | ISO 179/1eA |
Tensile Modulus (1 mm/min) | 3900 | MPa | ISO 527-1,-2 |
Charpy Notched Impact Strength (23°C) | 18.5 | kJ/m2 | ISO 180/1A |
Tensile Stress at Yield (1A/50) | 62 | MPa | ISO 527-1,-2 |
Tensile Strain at Yield (1A/50) | 5.9 | % | ISO 527-1,-2 |
Tensile Stress at Break (1A/50) | 60 | MPa | ISO 527-1,-2 |
Tensile Strain at Break (1A/50) | 8 | % | ISO 527-1,-2 |
Charpy Unnotched Impact Strength (23°C) | 62.5 | kJ/m2 | ISO 179/1eU |
Charpy Unnotched Impact Strength (-20°C) | 50 | kJ/m2 | ISO 179/1eU |
Flexural Strength (1A/2) | 81.5 | MPa | ISO 178 |
Flexural Modulus (1A/2) | 4100 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature (A120) | 140 | °C | ISO 306 |
Vicat Softening Temperature (B120) | 104 | °C | ISO 306 |
Heat Deflection Temperature - HDT/A (1.8 MPa) | 104 | °C | ISO 75-1,-2 |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 134 | °C | ISO 75-1,-2 |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Extrusion | - | — |
Barrel Temperatures | 180 to 220 | °C | — |
Die Temperature | 190 to 220 | °C | — |
Polymer Melt Temperature | 200 to 220 | °C | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP-R GF25 | - | ISO 1043 |