Polyethylene composition Grade F2030M is intended for further processing by blown-extrusion method into films of various thicknesses for packing purposes, storage and transportation of goods (articles), for manufacture of bags to be operated under severe conditions. Films manufactured from polyethylene Grade F2030M feature high tensile strength and high anti-puncture resistance.
Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Density at 20°C | 918 - 922 | kg/m3 | — |
Melt Flow Index at 190 °С and Load of 2.16 kg | 2.6 - 3.4 | g/10 min | — |
Melt Flow Index Spread within a Batch | max. 10 | % | — |
Number of Inclusions | max. 8 | pieces | — |
Tensile Yield Strength | min. 9 | MPa | — |
Rupture Strength | min. 27 | MPa | — |
Elongation at Break | min. 600 | % | — |
Packaging & Availability
- Packaging Type
- Packing
Product is packed in polyethylene bags (one bag net weight 25.00±0.25kg) and stacked on flat pallets with shrink film. Maximum gross weight of a bundle is 2 tons.
- Transportation
By all modes of transport.
Storage & Handling
- Storage
Polyethylene shall be stored in enclosed dry space preventing from direct sunlight on shelves or pallets at least 5 cm from the floor and at least 1 m from heaters, at temperature max 30°C, relative humidity max 80 %. Prior to processing bags with polymer shall be kept in production area for at least 12 hrs.