Value | Units | Test Method / Conditions | |
Tensile Strength at Break (50 mm/min) | 52 | MPa | ISO 527 |
Tensile Strength at Yield (50 mm/min) | 54 | MPa | ISO 527 |
Rockwell Hardness | 115 | Scale R | ASTM D785 |
Tensile Modulus (50 mm/min) | 2100 | MPa | ASTM D638 |
Tensile Strain at Break (50 mm/min) | 100 | % | ISO 527 |
Flexural Strength (2 mm/min) | 80 | MPa | ISO 178 |
Flexural Modulus (2 mm/min) | 2200 | MPa | ISO 178 |
Charpy Impact Strength - V-notched (23°C, 4mm) | 65 | kJ/m2 | ISO 179 1eA |
Notched Izod Impact Strength (23°C, 4 mm) | 59 | kJ/m2 | ISO 180 1A |
Value | Units | Test Method / Conditions | |
Specific Gravity (Natural or representative color) | 1.2 | - | ISO 1183 |
Melt Flow Index - MFI (260°C/5 kg) | 22 | g/10 min | ASTM D 1238 |
Melt Flow Index - MFI (250°C/10 kg) | 32 | g/10 min | ISO 1133 |
Molding Shrinkage - MD (Flow at 2mm) | 0.5 - 0.8 | % | ISO 294-4 |
Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.5 - 0.8 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 120 | °C | ISO 75-2 |
Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 97 | °C | ISO 75-2 |
Heat Deflection Temperature - HDT (1.8 MPa, Annealed, 4 mm) | 103 | °C | ISO 75-2 |