| Value | Units | Test Method / Conditions | |
| Specific Gravity (Natural or representative color) | 1.09 | - | ISO 1183 |
| Melt Flow Index - MFI (250°C/2.16 kg) | 4 | g/10 min | ASTM D 1238 |
| Melt Flow Index - MFI (250°C/10 kg) | 35 | g/10 min | ASTM D 1238 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.4 - 0.7 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.4 - 0.7 | % | ISO 294-4 |
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (50 mm/min) | 47 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 22 | MPa | ISO 527 |
| Rockwell Hardness | 103 | Scale R | ASTM D785 |
| Tensile Modulus (50 mm/min) | 1870 | MPa | ISO 527 |
| Tensile Strain at Break (50 mm/min) | 22 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 73 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2000 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 47 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 44 | kJ/m2 | ISO 180 1A |
| Unnotched Izod Impact Strength (23°C, 4 mm) | 35 | kJ/m2 | ISO 180 1A |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 93 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Annealed, 4 mm) | 107 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 112 | °C | ISO 75-2 |