Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
Properties
- Filler
- Glass Fiber
- Mechanical Properties
- Physical Properties
- Thermal Properties
Value | Units | Test Method / Conditions | |
Tensile Strength at Break (5 mm/min) | 180 | MPa | ISO 527 |
Tensile Strength at Yield (5 mm/min) | 180 | MPa | ISO 527 |
Rockwell Hardness | 121 | Scale R | ISO 2039-2 |
Tensile Modulus (5 mm/min) | 11400 | MPa | ISO 527 |
Tensile Strain at Break (5 mm/min) | 2.7 | % | ISO 527-2/1A |
Flexural Strength (2 mm/min) | 260 | MPa | ISO 178 |
Flexural Modulus (2 mm/min) | 13400 | MPa | ISO 178 |
Charpy Impact Strength - V-notched (23°C, 4mm) | 13 | kJ/m2 | ISO 179 1eA |
Notched Izod Impact Strength (23°C, 4 mm) | 11 | kJ/m2 | ISO 180 1A |
Value | Units | Test Method / Conditions | |
Specific Gravity (Natural or representative color) | 1.66 | - | ISO 1183 |
Melt Flow Index - MFI (316°C/5 kg) | 83 | g/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 267 | °C | ISO 75-2 |
Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 283 | °C | ISO 75-2 |
Heat Deflection Temperature - HDT (1.8 MPa, Annealed, 4 mm) | 272 | °C | ISO 75-2 |
Regulatory & Compliance
- Certifications & Compliance