Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
Properties
- Physical Properties
- Mechanical Properties
- Thermal Properties
| Value | Units | Test Method / Conditions | |
| Specific Gravity (Natural or representative color) | 1.17 | - | ISO 1183 |
| Melt Flow Index - MFI (220°C/10 kg) | 30 | g/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (50 mm/min) | 61 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 48 | MPa | ISO 527 |
| Rockwell Hardness | 118 | Scale R | ASTM D785 |
| Tensile Modulus (50 mm/min) | 2500 | MPa | ASTM D638 |
| Tensile Strain at Break (50 mm/min) | 45 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 89 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2550 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 17 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 14 | kJ/m2 | ISO 180 1A |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 94 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Annealed, 4 mm) | 97 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (0.45 MPa, Annealed, 4 mm) | 102 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 82 | °C | ISO 75-2 |
| Vicat Softening Temperature (B/50) | 100 | °C | ISO 306 |
| Vicat Softening Temperature (B/120) | 103 | °C | ISO 306 |