BRALEN+ FC 08-13 is a film grade of low density polyethylene with increased density (MD LDPE). High rigidity, good optical properties and chemical resistance are typical for this grade. It is additives free.

Polymer Name: Low Density Polyethylene (LDPE), Medium Density Polyethylene (MDPE)

Processing Methods: Blow Molding

Technical Data Sheet
  • TypeDocument Name
View All Documents

Knowde Enhanced TDS

Identification & Functionality

Plastics & Elastomers Functions
Technologies

Features & Benefits

Applications & Uses

Plastics & Elastomers Processing Methods
Applications

APPLICATIONS BRALEN+ FC 08-13 is intended for production of bags & pouches, blown films, shrink films and surface protection films. The grade can be used for blow molding products as well. Recommended film thickness is 0.025 to 0.080 mm.

Processing

BRALEN+ FC 08-13 can be used in conventional extrusion machines. Recommended processing temperatures are 170-220 °C.

Recycling

Polyethylene resins are suitable for recycling using modern recycling methods. In-house production waste should be kept clean to facilitate direct recycling.

Properties

Typical Properties
ValueUnitsTest Method / Conditions
Dart Drop (Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.)120gISO 7765-1 method A
Dart drop (Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.)120gISO 7765-1 method A
Density (23°C)929kg/m3ISO 1183-1
Density (23°C)929kg/m³ISO 1183-1
Haze (Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.)5%ASTM D1003
MFR (190°C/2.16 kg)0.8g/10 minISO 1133-1
MFR (190 °C, 2.16 kg)0.8g/10 minISO 1133-1
Hardness49Shore DISO 868
Tensile Strain at Break (MD, Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.)550%ISO 527-1,3
Tensile Strain at Break (TD, Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.)650%ISO 527-1,3
Tensile Strength14MPaISO 527-1,2
Tensile Strength (MD, Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.)28MPaISO 527-1,3
Tensile Strength (TD, Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and a blow up ratio 2.5:1.)26MPaISO 527-1,3
Vicat Softening Temperature103°CISO 306/A 50

Regulatory & Compliance

Certifications & Compliance
Reach Statement

Polymers are exempt of REACH registration. However, their raw materials which mean monomers and relevant additives have been registered. SLOVNAFT, as. is committed to fully respect legislation and will only use REACH compliant raw materials. At this point in time LDPE BRALEN+ does not contain any substances specifically identified as SVHC at levels greater than 0.1%.

Packaging & Availability

Packaging Type

Storage & Handling

Storage and Handling

Pellets are packed in 25 kg PE-LD bags and transported on stretch wrapped pallets at eligible load of polymer 1375 kg. Heat treated pallets are available as well. We use adhesive between the bags in order to avoid their slipping. Pay attention to this fact during the removing of the bags from the pallets. The prefered method is to lift the bag at first without rotation. Transportation in a road silo or rail silo is also available.

Since polyethylene is a combustible substance, the fire safety rules applicable for combustible materials in warehouses and store rooms should be observed.

If polymer is stored in conditions of high humidity and fluctuating temperatures, then atmospheric moisture can condense inside the packing. If it happened, it is recommended the pellets to be dried before use. During the storage polyethylene should not be exposed to UV radiation and temperatures above 40°C. Producer does not take responsibility for any damages caused by adverse storage.