Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
• Shopping bag
• Garbage bag
• Industrial liner
- Processing conditions
Typical processing conditions: 180-230 ºC.
Properties
- Thermal Properties
- Film Properties
- Neat Resin Properties
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature at 10N | 126 | ºC | ASTM D1525 |
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield - (MD)(Without Stabilizer) | 35 | MPa | ASTM D882 |
| Tensile Strength at Yield - (TD) (Without Stabilizer) | 30 | MPa | ASTM D882 |
| Tensile Strength at Yield - (MD) (With Stabilizer) | 35 | MPa | ASTM D882 |
| Tensile Strength at Yield - (TD) (With Stabilizer) | 30 | MPa | ASTM D882 |
| Tensile Strength at Break - (MD) (Without Stabilizer) | 70 | MPa | ASTM D882 |
| Tensile Strength at Break - (TD) (Without Stabilizer) | 65 | MPa | ASTM D882 |
| Tensile Strength at Break - (MD) (With Stabilizer) | 75 | MPa | ASTM D882 |
| Tensile Strength at Break - (TD) (With Stabilizer) | 55 | MPa | ASTM D882 |
| Tensile Elongation at Break - (MD) (Without Stabilizer) | 560 | % | ASTM D882 |
| Tensile Elongation at Break - (TD) (Without Stabilizer) | 550 | % | ASTM D882 |
| Tensile Elongation at Break - (MD) (With Stabilizer) | 520 | % | ASTM D882 |
| Tensile Elongation at Break - (TD) (With Stabilizer) | 560 | % | ASTM D882 |
| 1% Secant Modulus-(MD) (Without Stabilizer) | 930 | MPa | ASTM D882 |
| 1% Secant Modulus-(TD) (Without Stabilizer) | 990 | MPa | ASTM D882 |
| 1% Secant Modulus-(MD) (With Stabilizer) | 1030 | MPa | ASTM D882 |
| 1% Secant Modulus-(TD) (With Stabilizer) | 1140 | MPa | ASTM D882 |
| Elmendorf Tear Strength-(MD) (Without Stabilizer) | 17 | gf | ASTM D1922 |
| Elmendorf Tear Strength-(TD) (Without Stabilizer) | 39 | gf | ASTM D1922 |
| Elmendorf Tear Strength-(MD) (With Stabilizer) | 78 | gf | ASTM D1922 |
| Elmendorf Tear Strength-(TD) (With Stabilizer) | 280 | gf | ASTM D1922 |
| Dart Drop Impact (Without Stabilizer) | 340 | g | ASTM D1709 |
| Dart Drop Impact (With Stabilizer) | 280 | g | ASTM D1709 |
| Value | Units | Test Method / Conditions | |
| MFR (190ºC/2.16Kg) | 0.05 | g/10min | ASTM D1238 |
| MFR (190ºC/21.6Kg) | 9.3 | g/10min | ASTM D1238 |
| Density | 0.951 | g/cm3 | ASTM D792 Method A |
Storage & Handling
- Storage and handling
F0554 should be stored in a dry cool place with adequate ventilation and protected from UV-light at temperatures below 50°C. It is advisable to process polyethylene resins within 6 months after delivery.