Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
• Woven sacks
• Carpet packing
• Binding tape
• Monofilament- Processing conditions
- Recommended Extrusion Temperature: 230 – 260 ºC
- Stretching Temperature: 140 – 160 ºC
- Stretching Ratio 4-6.
Properties
- Mechanical Properties
- Thermal Properties
- Neat Resin Properties
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield | 34 | MPa | ASTM D638 |
| Tensile Elongation at Yield | 9 | % | ASTM D638 |
| Tensile Strength at Break | 19 | MPa | ASTM D638 |
| Tensile Elongation at Break | 165 | % | ASTM D638 |
| Flexural Modulus | 1300 | MPa | ASTM D790 |
| Flexural Strength | 35 | MPa | ASTM D790 |
| Izod Impact, Notched 23ºC | 3 | kJ/m2 | ASTM D256 |
| Rockwell Hardness | 98 | — | ASTM D785 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature at 10N | 152 | ºC | ASTM D1525 |
| Value | Units | Test Method / Conditions | |
| MFR (230ºC/2.16Kg) | 3 | g/10min | ASTM D1238 |
| Density | 0.9 | g/cm3 | ASTM D792 Method A |
Storage & Handling
- Storage and handling
FY3011E should be stored in a dry cool place with adequate ventilation and protected from UV-light at temperature below 50 ºC. It is advisable to process polypropylene resins within 6 months after delivery.