Knowde Enhanced TDS
Identification & Functionality
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Compatible Polymers & Resins
- Plastics & Elastomers End Uses
- Applications
- Impact modifier for full range of unfilled polyamides for temperatures as low as -20°C. Level of improvement obtained is a function of the OPTIM® E-131 addition level.
- Impact modifier for mineral & glass filled polyamides
- Adhesion promoter between metal, glass and engineering plastics with polyolefins.
- Processing Conditions
- OPTIM® E-131 can be added to Polyamides to achieve good dispersion of fillers within the polymer matrix thereby obtaining best properties.
- Maximum processing temperature should not generally exceed 290°C.
- At temperatures above 290°C, these specialty polymers can evolve low concentrations of fumes.
- If overheated, more extensive decomposition may occur due to exposure of overheated polymers to atmospheric oxygen.
- Adequate local ventilation should be provided to remove the fumes from the work area.
Properties
- Physical Form
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Hardness
Value | Units | Test Method / Conditions | |
Tensile Strength | 5 | MPa | ASTM D638/2010 |
Percentage Elongation | 825 | % | ASTM D638/2010 |
Tensile Modulus | 2 | MPa | ASTM D638/2010 |
Flexural Modulus | 19 | MPa | ASTM D790/2010 |
Flexural Strength | 1 | MPa | ASTM D790/2010 |
Value | Units | Test Method / Conditions | |
Melting Temperature | 80 | °C | DSC |
Vicat Softening Temperature | 58 | °C | ASTM 1525/2010 |
Value | Units | Test Method / Conditions | |
MFI (at 190°C/2.16 Kg) | 0.6 | g/10min | ASTM D1238 |
Density | 0.874 | g/cm³ | ASTM D792 |
Bulk Density | 0.49 | g/ml | PLUSS® method |
Bonded Maleic Anhydride | High | — | PLUSS® method |
Value | Units | Test Method / Conditions | |
Durometer Hardness | 75 | Shore A | ASTM D2240/2004 |
Durometer Hardness | 19 | Shore D | ASTM D2240/2004 |
Packaging & Availability
- Packaging Type
- Packaging Information
- OPTIM® speciality polymers are supplied in pre-dried form in 25 Kg (55 lbs) PE lined, HD woven sack-laminated paper bags and 750 Kg (1650 lbs) FIBC’s.
- They should be stored in cool and dry place.
Storage & Handling
- Storage and Handling Procedures
- OPTIM® E-131 should be stored in a dry, cool and well-ventilated area.
- It is recommended that prior to processing, the requisite quantity of material to be used should be dried in a hopper dryer or oven at 45-50°C for about 2 hours for obtaining best results.