- Chemical coupling agent for highly filled PP compounds.
- Coupling agent for continuous glass fiber filled PP compounds.
- Processing Conditions
- A slight pungent odor is normal during processing of OPTIM® P-425 IC.
- During processing, the compounding parameters that can lead to optimized performance include extruder type, screw design, barrel temperature, screw speed, throughput, residence time and material feeding sequence.
- Maximum processing temperature should not exceed 280°C.
Properties
- Physical Form
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Hardness
Value | Units | Test Method / Conditions | |
Tensile Strength | 29 | MPa | ASTM D638/2010 |
Percentage Elongation | 6 | % | ASTM D638/2010 |
Tensile Modulus | 830 | MPa | ASTM D638/2010 |
Flexural Modulus | 1850 | MPa | ASTM D790/2010 |
Flexural Strength | 50 | MPa | ASTM D790/2010 |
Value | Units | Test Method / Conditions | |
MFI (at 190°C/2.16 Kg) | 150 | g/10min | ASTM D1238 |
Density | 0.908 | g/cm³ | ASTM D792 |
Bulk Density | 0.51 | g/ml | PLUSS® method |
Bonded Maleic Anhydride | High | — | PLUSS® method |
Value | Units | Test Method / Conditions | |
Melting Temperature | 161 | °C | DSC |
Vicat Softening Temperature | 150 | °C | ASTM 1525/2010 |
Value | Units | Test Method / Conditions | |
Durometer Hardness | 78 | Shore D | ASTM D2240/2004 |
Packaging & Availability
- Packaging Type
- Packaging Information
- OPTIM® specialty polymers are supplied in pre-dried form in 25 Kg (55 lbs) PE lined, HD woven sack-laminated paper bags and 750 Kg (1650 lbs) FIBC’s.
- They should be stored in cool and dry place.
Storage & Handling
- Storage and Handling Procedures
- OPTIM® P-425 IC is mildly hygroscopic and should be stored in a dry and cool area.
- It is recommended that prior to processing, the requisite quantity of material to be used should be dried in a hopper dryer or air circulating oven, at 80-95°C, for about 2 hours for obtaining best results.