Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Injection Molding
- Additive
Flame Retardant
- Filler and Reinforcement
- Filler : Glass/Mineral
- Reinforcement : 40% Filler by Weight
Features & Benefits
- Labeling Claims
- Materials Features
- Features
- Bromine Free
- Chlorine Free
- Flame Retardant
- Medium Heat Resistance
- Self Extinguishing
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Processing Information (Injection Molding)
- Impact Properties
- Hardness
Value | Units | Test Method / Conditions | |
Density | 1.43 | — | ASTM D792 |
Melt Mass Flow Rate (at 250°C, 11.6 kg) | 1.0 - 9.0 | g/10 min | ASTM D1238 |
Molding Shrinkage (at 0.125 in, Flow) | 1.0E-3 to 3.0E-3 | in/in | ASTM D955 |
Molding Shrinkage (at 0.125 in, Across Flow) | 1.0E-3 to 3.0E-3 | in/in | ASTM D955 |
Specific Gravity | 1.43 | — | ASTM D792 |
Value | Units | Test Method / Conditions | |
Tensile Strength (at Yield, 0.125 in) | 18300 | psi | ASTM D638 |
Tensile Strength (at Break, 0.125 in) | 18300 | psi | ASTM D638 |
Tensile Elongation (at Yield, 0.125 in) | 1.5 | % | ASTM D638 |
Flexural Modulus (at 0.125 in) | 1400000 | psi | ASTM D790 |
Flexural Strength (at Break, 0.125 in) | 23000 | psi | ASTM D790 |
Value | Units | Test Method / Conditions | |
Deflection Temperature Under Load (at 264 psi, 0.125 in, Unannealed) | 250 | °F | ASTM D648 |
Value | Units | Test Method / Conditions | |
Volume Resistivity | 10000000000000000 | ohms·cm | ASTM D257 |
Value | Units | Test Method / Conditions | |
Drying Temperature | 220 - 230 | °F | — |
Drying Time | 3.0 - 4.0 | hr | — |
Front Temperature | 540 - 600 | °F | — |
Middle Temperature | 520 - 590 | °F | — |
Mold Temperature | 170 - 220 | °F | — |
Maximum Drying Time | 8 | hr | — |
Rear Temperature | 500 - 580 | °F | — |
Processing Temperature (Melt) | 560 - 600 | °F | — |
Value | Units | Test Method / Conditions | |
Impact Strength (at 73°F, 0.125 in, Notched Izod) | 1.3 | ft·lb/in | ASTM D256 |
Value | Units | Test Method / Conditions | |
Rockwell Hardness (M-Scale) | 90 | — | ASTM D785 |